Search

Conventional free radical polymerization and post-alkylation of 4-diphenylphosphino styrene (DPPS) generate a new class of high-molecular-weight phosphonium-containing homopolymers with tunable thermal, viscoelastic, and wetting properties. Post-alkylation and subsequent anion exchange provide an effective method for tuning Tg values and thermal stability as a function of alkyl chain length and counteranion selection (X(-) , BF4 (-) , TfO(-) , and Tf2 N(-) ). Rheological characterization facilitates the generation of time-temperature-superposition (TTS) pseudomaster curves and subsequent analysis of frequency sweeps at various temperatures reveals two relaxation modes corresponding to long-range segmental motion and the onset of viscous flow. Contact angle measurements reveal the influence of counteranion selection on wetting properties, revealing increased contact angles for homopolymers containing nucleophilic counteranions. These investigations provide fundamental insight into phosphonium-containing polymers, aiming to guide future research and applications involving electro-active polymeric devices., (© 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.)

We demonstrate that increasing the hydrophobic environment around the charge center of a polyelectrolyte (PE) not only decreases the water content of an adsorbed PE layer but can even dewater up to ~50% of an initially hydrated substrate. The results of this work are expected to yield new stratagies to dewater PE systems and have potential applications in mineral recovery, paper manufacturing, and biomedical materials. Adsorption of a series of cationically derivatized dextran polyelectrolytes onto sulfated nanocrystalline cellulose (SNC) has been studied using quartz crystal microbalance with dissipation monitoring (QCM-D) and surface plasmon resonance (SPR). Synthesized samples of (N,N-dimethylamino)ethyldextran (DMAE-Dex), (N,N-diethylamino)ethyldextran (DEAE-Dex), and (N,N-diisopropylamino)ethyldextran (DIAE-Dex) had degrees of substitution (DS) ranging from 0.05 to 0.82. DMAE-Dex, DEAE-Dex, and DIAE-Dex all showed decreasing adsorption onto SNC and decreasing water content of the adsorbed film with increasing DS. Additionally, DEAE-Dex and DIAE-Dex films adsorbed onto SNC contained less water than DMAE-Dex films with the same DS. Interestingly, QCM-D results for high DS DIAE-Dex adsorbed onto SNC revealed mass loss, whereas SPR results clearly showed DIAE-Dex adsorbed. These observations were consistent with dehydration of the SNC substrate. This study indicates that the water content of the substrate could be tailored by controlling the DS and hydrophobic character of the adsorbed polyelectrolytes.

Phase separation in thin film blends of poly(tert-butyl acrylate) (PtBA) and a polyhedral oligomeric silsesquioxane (POSS), trisilanolphenyl-POSS (TPP), is studied as functions of annealing temperature and time, using reflected light optical microscopy, atomic force microscopy, and X-ray photoelectron spectroscopy. The results demonstrate that the PtBA/TPP blend system confined to thin films ( approximately 90 nm) exhibits lower critical solution temperature (LCST) behavior with a critical temperature of approximately 70 degrees C and a critical composition of 60 wt % PtBA with insignificant dewetting at the phase boundary. Off-critical spinodal behavior is observed for 58 and 62 wt % PtBA blend films. Phase separation by nucleation and growth is observed for all compositions outside the window between 58 and 62 wt % PtBA. The temporal evolution of spinodal decomposition in 60 wt % PtBA blend films is explored at annealing temperatures of 75, 85, 95, and 105 degrees C. The morphological evolution in 60 wt % PtBA blend films is similar for all experimental temperatures (75, 85, 95, and 105 degrees C) with the expected shorter time scales for phase evolution at higher annealing temperatures. Fast Fourier transforms of optical micrographs reveal that these blend films immediately undergo phase separation by spinodal decomposition during temperature jump experiments. Power law scaling for the characteristic wavevector with time (q approximately t(n) with n approximately -1/4 to -1/3) for domain growth during the early stages of phase separation yields to domain pinning at the later stages for 60 wt % PtBA blend films annealed at 75, 85, and 95 degrees C. In contrast, domain growth is pinned over the entire experimental time scale for 60 wt % PtBA blend films annealed at 105 degrees C.