Search

The present study deals with preparing a polymer-based material with incorporated ceramics and monitoring changes in properties after in vitro natural degradation. The developed material is a mixture of polymers of polylactic acid and polyhydroxybutyrate in a ratio of 85:15. Ceramic was incorporated into the prepared material, namely 10% hydroxyapatite and 10% tricalcium phosphate of the total volume. The material was processed into a filament form, and types of solid and porous samples were prepared using additive technology. These samples were immersed in three different solutions: physiological solution, phosphate-buffered saline, and Hanks' solution. Under constant laboratory conditions, changes in solution pH, material absorption, weight loss, changes in mechanical properties, and surface morphology were monitored for 170 days. The average value of the absorption of the solid sample was 7.07%, and the absorption of the porous samples was recorded at 8.33%, which means a difference of 1.26%. The least change in pH from the reference value of 7.4 was noted with the phosphate-buffered saline solution. Computed tomography was used to determine the cross-section of the samples. The obtained data were used to calculate the mechanical properties of materials after degradation. The elasticity modulus for both the full and porous samples degraded in Hanks' solution (524.53 ± 13.4 MPa) has the smallest deviation from the non-degraded reference sample (536.21 ± 22.69 MPa). [ABSTRACT FROM AUTHOR]

The paper deals with the separation of the third cervical vertebra using the software VGStudio MAX, Mimics, and inVesalius. During the separation, various parameters of the threshold were used to determine the effect. The comparison of models from Mimics and inVesalius to VGStudio MAX showed that the cumulative variance distribution for 95% surface coverage is less than 0.935 mm. When comparing medically oriented software, Mimics and inVesalius, the deviation was less than 0.356 mm. The model was made of polylactic acid (PLA) material on a low-cost 3D printer, Prusa i3 MK2.5 MMU1. The printed model was scanned by four scanners: Artec Eva, 3Shape D700, Steinbichler Comet L3D, and Creaform EXAscan. The outputs from the scanners were compared to the reference model (standard tessellation language (STL) model for 3D printing) as well as to the scanner with the best accuracy (3Shape). Compared to the publications below, the analysis of deviations was evaluated on the entire surface of the model and not on selected dimensions. The cumulative variance distribution for comparing the output from the 3D scanner with the reference model, as well as comparing the scanners, shows that the deviation for 95% of the surface coverage is at the level of 0.300 mm. Since the model of the vertebra is planned for education and training, the used software and technologies are suitable for use in the design and the production process. [ABSTRACT FROM AUTHOR]

Highlights • The initial testing of a new PLA/PHB material mixture. • The drying of the material PLA/PHB significantly affects its degradation properties. • Determination of viscoelastic properties of PLA/PHB blend comparing dried and non-dried material. • Metrological verification of cubic and tubular samples printed on 3D Bioplotter Enviontec. Abstract Additive manufacturing has a great potential for creating hard tissue substitutes, such as bone and cartilage, or soft tissues, such as vascular and skin grafts. This study is a pilot study for 3D printing of a new material mixture potentially used as a tubular substitute for urethra replacement. This new mixture is a blend of polylactic acid (PLA) and polyhydroxybutyrate (PHB). The basic aspect that affects the 3D printing process is correct material preparation and setting of 3D printer parameters. Selection of material and printing parameters depend on printing technology. The printing technology affects material behavior during printing process. The goal of preprocessing and 3D printing process is to provide stabile conditions during manufacturing to obtain usable printed samples. The study deals with preparation of material before 3D printing – material drying. Moisture in material affects material degradation and viscosity during printing. According to this, it is necessary to verify recommended drying parameters. Verification was performed by printing strand samples from dried and non-dried material and also by calculating and comparing respective viscosities that change in time. Printed strand clearly show that non-dried material degrades in less than 10 min, what leads to inappropriate application in short-time printing. Dried material shows significant stability and degrades slightly during selected time span. For metrological verification of material stability two sample types were designed and manufactured – a cubic sample which represents basic scaffold structures and a tubular one that serves as urethra substitution. Obtained results showed appropriate usability of selected technology and printing parameters for PLA / PHB material blend. [ABSTRACT FROM AUTHOR]