Search

Growing concerns regarding plastic waste have prompted various attempts to replace plastic packaging films with biodegradable alternatives such as poly(lactic acid) (PLA). However, their low hydrolysis resistance owing to the presence of aliphatic polyesters limits the shelf life of biodegradable polymers. Hydrolysis leads to the deterioration of mechanical performance, which is a key disadvantage of biodegradable plastics. In this study, a layer-by-layer (LBL) assembly method was used for the dip-coating of biorenewable, biodegradable nanocellulose/nanochitin on the PLA surface. Additional crosslinking and compression of the coated nanofibers, each containing carboxylic acid and amine groups, respectively, were induced through electromagnetic microwave irradiation to protect the PLA film by improving hydrolysis resistance. The coatings were examined by morphological observations and water contact angle measurements. The LBL coatings of differently charged nanofibers of 10.6 μm were reduced to 40 % after microwave treatment, and the thickness does not vary after the hydrolysis experiment. Microwave irradiation increased the water contact angle owing to amide linkage formation, thereby preventing the peeling off of coating layers. Improved hydrolysis resistance inhibited the reduction in molecular weight and tensile strength. These findings could be used to develop sustainable and biodegradable plastic packaging films with a prolonged shelf life., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2023. Published by Elsevier B.V.)

Among plastic items, single‐use straws are particularly detrimental to marine ecosystems because such straws, including those made of poly(lactic acid) (PLA), are sharp and extremely slowly degradable in the ocean. While paper straws are promising alternatives, they exhibit hydration‐induced swelling even when coated with a non‐degradable plastic coating and promote effervescence (fizzing) in soft drinks owing to their surface heterogeneities. In this study, upgraded paper straw is coated with poly(butylene succinate) cellulose nanocrystal (PBS/CNC) composites. CNC increases adhesion to paper owing to their similar chemical structures, optimizes crystalline PBS spherulites through effective nucleation, and reinforces the matrix through its anisotropic and rigid features. The straws are not only anti‐fizzing when used with soft drinks owing to their homogeneous and seamless surface coatings, but also highly water‐resistant and tough owing to their watertight surfaces. All degradable components effectively decompose under aerobic composting and in the marine environment. This technology contributes to United Nations Sustainable Development Goal 14 (Life Below Water). [ABSTRACT FROM AUTHOR]

Biodegradable polyesters, such as poly(butylene adipate-co-terephthalate) (PBAT), can trigger the hydrolysis of esters in a natural environment. However, biodegradability does not guarantee its eco-friendliness due to the concerns associated with terephthalic acid. Substitution by biomass-based counterparts no longer ensures "truly" eco-friendly biodegradable polyesters. In this study, we have used poly(butylene adipate-co-furanoate) (PBAF), which utilizes a biomass-derived substituent, furan-2,5-dicarboxylic acid (FDCA), and have proven that this is superior from the perspective of both mechanical performance and enzymatic degradation. Compared to its terephthalate counterpart, PBAF exhibits remarkable elasticity upon stretching: when released beyond 800% extension, PBAT almost malfunctioned, whereas PBAF exhibited instant elastic recovery. This results in PBAT and PBAF having a similar tensile strength in the range of 50–70 MPa at the ring fraction of 50 to 80 mol%. During the enzymatic degradation using lipase from Thermomyces lanuginosus, PBAF with a ring fraction of 50 mol% solely undergoes hydrolysis due to enzyme specificity. Ex situ spectroscopic analysis confirms that the participation of FDCA ester groups in the early stages of degradation triggered the successive hydrolytic reaction. Thus, understanding the structural characteristics of FDCA would open new opportunities in the field of sustainable plastic industries. [ABSTRACT FROM AUTHOR]

• Explains the importance of biomass-derived plastic materials and introduces 2,5-furandicarboxylic acid (FDCA) as a promising material. • Presents research cases of plastics synthesized using FDCA as a raw material and summarizes their properties. • Evaluates the biodegradability of FDCA-based plastics and considers the environmental impact they have. As environmental regulations stemming from the use of plastics are implemented around the world, bioplastics are gaining traction to replace petroleum-based materials. 2,5-furandicarboxylic acid (FDCA), which can be converted from biomass, is a typical bio-based material used in the synthesis of bioplastics, whose structural properties can impart unique properties to polymers, such as high T g and low gas and water permeability. In this review, we aim to investigate the properties of FDCA and how they vary with the chain length of the diol monomer and the type of co-monomer used to synthesize polyester based on it. In addition, the biodegradation behavior of the synthesized polyester is discussed, and the potential applications of FDCA-based polyester are suggested. [ABSTRACT FROM AUTHOR]