This article presents the influence of severe plastic deformation by hydrostatic extrusion (HE) on the thermal and structural properties of polyamide 6 (PA6). During the hydrostatic extrusion process, a fibrous structure oriented along the extrusion direction is formed, which was visualized during microscopic observations. The degree of crystallinity was analyzed by differential scanning calorimetry (DSC). Wide-angle X-ray scattering diffraction (WAXS) analysis was used to partially characterize the PA6 structure after the HE process. The contents of various forms of the crystalline phase in PA6 samples before and after the HE process were analyzed in fragments of spectroscopy in infrared (FTIR). The favorable properties of PA6 after the HE process were obtained after deformation under conditions generating an adiabatic temperature higher than the glass transition temperature and lower than the temperature of the onset of melting of the crystalline phase. Thermal analysis using DSC allowed us to conclude that in the PA6 after the HE process generating deformations in the range of 0.68–1.56, the proportion of the crystalline phase α increases in PA6. As the deformation increases in the HE process, the crystalline phase proportion increases by 12% compared to the initial material (before HE). The glass transition temperature of PA6 is ca. 50.6 °C, reduced for the sample after the HE process at a small deformation of 0.68 (PA6_0.68) to ca. 44.2 °C. For other samples, Tg is ca. 53.2–53.5 °C. As a result of the analysis of WAXS diffractograms of PA6 samples after various deformations in the HE process, the presence of typical peaks of phases α1 and α2 and γ was observed. The results of the FTIR spectroscopic analysis confirm these observations that as the deformation increases, the proportion of the crystalline phase α increases. [ABSTRACT FROM AUTHOR]

This paper presents the effect of severe plastic deformation obtained using the cold hydrostatic extrusion (HE) method on the mechanical and structural properties of polyamide 6 (PA6). As a result of the plastic strain, a significant increase in ultimate tensile strength and tensile modulus were observed. Tensile strength rose by almost 500%, up to the level of 508 MPa, whereas the tensile modulus rose by about 65%. Flexural modulus increase was also observed to 3230 MPa, i.e., by approx. 160%. As a result of high plastic deformation, the structure of the polyamide 6 changed significantly, as evidenced by its fibrous nature as presented in the results of the scanning electron microscopy inspection (SEM). The surface quality of products investigated was tested using profilometry. [ABSTRACT FROM AUTHOR]