Search

The biofouling propensity and cleaning effectiveness were evaluated for a new generation of polyamide thin-film composite (PA-TFC) membranes that are surface nano-structured (SNS) with terminally anchored hydrophilic polymer chains. The SNS-PA-TFC membranes were formed via surface graft polymerization onto the surface of polyamide base membranes previously activated via surface treatment with atmospheric pressure plasma. Poly(methacrylic acid) (PMMA) and polyacrylamide (PAAm) SNS-PA-TFC membranes were synthesized and evaluated with respect to their biofouling resistance using secondary wastewater from a municipal wastewater treatment (MWT) plant. Biofouling resistance and cleaning effectiveness were quantified via flux decline measurements in addition to imaging of the biofouled membranes before and after DI water and chemical (Na 2 ·EDTA) cleaning. Increased biofouling resistance was highest for the PMAA-SNS-PA-TFC membrane being a factor of 4.2 greater than for the commercial membrane of about the same salt rejection used in the MWT plant. Moreover, permeability recovery for the PMAA-SNS-PA-TFC membrane was higher by factors of up to ~1.2 relative to the reference commercial membrane upon cleaning with DI water and more aggressive chemical cleaning at high pressure. The present evaluation of the SNS-PA-TFC membranes suggests that biofouling resistance and cleaning effectiveness of RO membranes can be enhanced via hydrophilic brush layers.

The influence of a pre-existing biofilm on RO membrane mineral scaling was evaluated using gypsum as a model scalant. The biofilm was established using microfiltered secondary treated wastewater effluent on-site in a wastewater treatment facility. Mineral scaling was then monitored via direct visual observation of crystal growth on the membrane surface in a transparent plate-and-frame RO cell. SEM imaging of the membrane surface and sectioned biofilm revealed gypsum crystals within the biofilm matrix, including the protrusion of crystal rods from within the biofilm. Both mineral scale surface coverage and crystal number density were greater in the presence of the biofilm. Moreover, individual mineral crystal growth rate within the biofilm was significantly higher relative to growth in the absence of a biofilm. Analyses of crystal growth and nucleation rates, within the biofilm and in its absence, suggest concentration polarization enhancement within the biofilm. The present study suggests that mineral scaling may not be restricted to tail elements in RO plants, but could also occur in lead elements where biofilms can enhance concentration polarization. Therefore, understanding of the coupling of biofouling and mineral scaling may be of particular significance to the operation and design of RO plants in water reuse applications.

The mineral scaling propensity of aromatic polyamide membrane surfaces was evaluated for surfaces ranging in roughness from about 1 to 94 nm, surface feature heights ranging from a few nanometers to as high as 400–450 nm and average peak separation of ∼140 nm to 2 μm. The polyamide surfaces were interfacially polymerized onto quartz crystal microbalance (QCM) sensors and silicon wafer substrates which were previously structured with a polyelectrolyte film formed by a layer-by-layer self-assembly method. Mineral scaling was quantified via QCM measurements of the time evolution of surface crystallization along with SEM and AFM surface characterization. Crystal surface mass density and rate of surface crystallization increased with increasing surface roughness. However, surface scaling propensity was also significantly impacted by the details of surface topography revealing fewer but larger crystals on rough surfaces that possessed large features with large separation distances. It is hypothesized that the separation distance between features and feature heights (dictating the geometry of surface “valleys”), for a given surface roughness, could affect the availability of surface nucleation sites as well as constrain growth of crystals within surface valleys.

Surface nano-structuring of polyamide desalination membrane with a hydrophilic poly(methacrylic acid) was shown to reduce the membrane mineral scaling propensity as demonstrated with calcium sulfate dihydrate (gypsum). A two-step approach was employed, whereby the active polyamide (PA) layer of a thin-film composite (TFC) synthesized membrane was activated with impinging atmospheric plasma, followed by a solution free-radical graft polymerization (FRGP) of a water soluble methacrylic acid (MAA) monomer, at 60 °C and initial monomer concentration of 5–20% (v/v), onto the surface of the PA-TFC membrane. The approach of creating a layer of end-grafted poly(methacrylic acid) (PMAA) surface chains was first developed and evaluated using a surrogate polyamide membrane layer interfacially polymerized onto a thin poly(ethyleneimine) (PEI) film coated onto a silicon wafer. The resulting PMAA–PA-PEI–Si surrogate membrane surface was hydrophilic with a water contact angle range of 10–17°. Structuring of the PA-TFC membrane at equivalent FRGP reaction conditions resulted in membranes of higher permeability (by a factor of 1.3–2.26) relative to a commercial RO membrane of a similar surface roughness (∼70 nm) and salt rejection. Flux tests of membrane mineral scaling demonstrated that membrane mineral scaling propensity can be measurably reduced, relative to commercial membrane of the same salt rejection, while yielding equivalent or higher water permeability. The onset time for gypsum scaling for the optimal membrane surface (prepared at 10% (v/v) initial MAA concentration) was retarded by a factor of 2–5 relative to the commercial RO membrane. Current work is ongoing to further optimize the surface structure in order to increasing scaling resistance and assess the impact of surface structuring on nucleation of mineral salt crystals.