Search

Cross‐sectional transmission electron microscopy has been widely used to investigate organic–inorganic hybrid halide perovskite‐based optoelectronic devices. Electron‐transparent specimens (lamellae) used in such studies are often prepared using focused ion beam (FIB) milling. However, the gallium ions used in FIB milling may severely degrade the structure and composition of halide perovskites in the lamellae, potentially invalidating studies performed on them. In this work, the close relationship between perovskite structure and luminescence is exploited to examine the structural quality of perovskite solar cell lamellae prepared by FIB milling. Through hyperspectral cathodoluminescence (CL) mapping, the perovskite layer was found to remain optically active with a slightly blue‐shifted luminescence. This finding indicates that the perovskite structure is largely preserved upon the lamella fabrication process although some surface amorphisation occurred. Further changes in CL due to electron beam irradiation were also recorded, confirming that electron dose management is essential in electron microscopy studies of carefully prepared halide perovskite‐based device lamellae. Research Highlights: Cathodoluminescence is used to study the emission of focused ion beam milled perovskite solar cell lamellae.The perovskite remained optically active with a slightly blue‐shifted luminescence, indicating that the perovskite structure is mostly preserved. [ABSTRACT FROM AUTHOR]

Metal‐halide perovskite solar cells (PSCs) have had a transformative impact on the renewable energy landscape since they were first demonstrated just over a decade ago. Outstanding improvements in performance have been demonstrated through structural, compositional, and morphological control of devices, with commercialization now being a reality. Here the authors present an aerosol assisted solvent treatment as a universal method to obtain performance and stability enhancements in PSCs, demonstrating their methodology as a convenient, scalable, and reproducible post‐deposition treatment for PSCs. Their results identify improvements in crystallinity and grain size, accompanied by a narrowing in grain size distribution as the underlying physical changes that drive reductions of electronic and ionic defects. These changes lead to prolonged charge‐carrier lifetimes and ultimately increased device efficiencies. The versatility of the process is demonstrated for PSCs with thick (>1 µm) active layers, large‐areas (>1 cm2) and a variety of device architectures and active layer compositions. This simple post‐deposition process is widely transferable across the field of perovskites, thereby improving the future design principles of these materials to develop large‐area, stable, and efficient PSCs. [ABSTRACT FROM AUTHOR]

Halide perovskites have attracted substantial interest for their potential as disruptive display and lighting technologies. However, perovskite light‐emitting diodes (PeLEDs) are still hindered by poor operational stability. A fundamental understanding of the degradation processes is lacking but will be key to mitigating these pathways. Here, a combination of in operando and ex situ measurements to monitor the performance degradation of (Cs0.06FA0.79MA0.15)Pb(I0.85Br0.15)3 PeLEDs over time is used. Through device, nanoscale cross‐sectional chemical mapping, and optical spectroscopy measurements, it is revealed that the degraded performance arises from an irreversible accumulation of bromide content at one interface, which leads to barriers to injection of charge carriers and thus increased nonradiative recombination. This ionic segregation is impeded by passivating the perovskite films with potassium halides, which immobilizes the excess halide species. The passivated PeLEDs show enhanced external quantum efficiency (EQE) from 0.5% to 4.5% and, importantly, show significantly enhanced stability, with minimal performance roll‐off even at high current densities (>200 mA cm−2). The decay half‐life for the devices under continuous operation at peak EQE increases from <1 to ≈15 h through passivation, and ≈200 h under pulsed operation. The results provide generalized insight into degradation pathways in PeLEDs and highlight routes to overcome these challenges. [ABSTRACT FROM AUTHOR]

The upscaling of perovskite solar cells is one of the challenges that must be addressed to pave the way toward the commercial development of this technology. As for other thin-film photovoltaic technologies, upscaling requires the fabrication of modules composed of series-connected cells. In this work we demonstrate for the first time the interconnection of inverted modules with NiOx using a UV ns laser, obtaining a 10.2 cm2 minimodule with a 15.9% efficiency on the active area, the highest for a NiOx based perovskite module. We use optical microscopy, energy-dispersive X-ray spectroscopy, and transfer length measurement to optimize the interconnection. The results are implemented in a complete electrical simulation of the cell-to-module losses to evaluate the experimental results and to provide an outlook on further development of single junction and multijunction perovskite modules. [ABSTRACT FROM AUTHOR]