Search

The aim of this work is to determine paraquat adsorption capacity of zeolite NaX and Al-MCM-41. All adsorbents were synthesized by hydrothermal method using rice husk silica. For Al-MCM-41, aluminum (Al) was added to the synthesis gel of MCM-41 with Al content of 10, 15, 20 and 25 wt%. The faujasite framework type of NaX and mesoporous characteristic of Al-MCM-41 were confirmed by X-ray diffraction. Surface area of all adsorbents determined by N2 adsorption-desorption analysis was higher than 650 m2/g. Al content and geometry were determined by X-ray fluorescence and 27Al nuclear magnetic resonance, respectively. Morphology of Al-MCM-41 were studied by transmission electron microscopy; macropores and defects were observed. The paraquat adsorption experiments were conducted using a concentration range of 80-720 mg/L for NaX and 80-560 mg/L for Al-MCM-41. The paraquat adsorption isotherms from all adsorbents fit well with the Langmuir model. The adsorption capacity of NaX was 120 mg/g-adsorbent. Regarding Al-MCM-41, the 10% Al-MCM-41 exhibited the lowest capacity of 52 mg/g-adsorbent while the other samples had adsorption capacity of 66 mg/g-adsorbent.

The goal of this work was to utilize rice husk silica (RHS) and porous materials synthesized with RHS, including mesoporous material (MCM-41) and microporous materials (zeolite NaY and NaBEA), for adsorption of herbicide paraquat. The adsorption occurred although cation exchange and the capacity decreased in the following order: NaY > NaBEA > MCM-41 > RHS, consistent with the amount of Al. The adsorption on all adsorbents fitted well with the Langmuir model and the maximum adsorption capacity of 185.2 mg/g-adsorbent was obtained on NaY. In addition, blue dye in commercial grade paraquat did not interfere with paraquat adsorption. Although MCM-41 was the most efficient adsorbent for the blue dye, RHS was favorable in terms of production cost. A mixture of NaY and RHS is recommended for simultaneous adsorption of paraquat and blue dye.

Zeolite NaY synthesized from a typical procedure could suffer from agglomeration. Adding non-refluxed cogon grass (NG) to the synthesis gel could produce NaY with good dispersion and uniform crystal size. Small molecules produced from cogon grass in alkaline conditions could prevent agglomeration. The obtained zeolite (Y-NG) has a crystallinity and surface area comparable to the synthesis without grass (Y-WG). Y-NG demonstrated similar paraquat adsorption capacity to Y-WG at high initial concentrations. On the other hand, the zeolite from the addition of acid-refluxed grass (Y-RG) has the lowest crystallinity, smallest surface area, and poorest paraquat adsorption capacity. The effect of grass amount on the zeolite structure was studied. One gram of cogon grass was the optimum amount to add to the synthesis gel. [ABSTRACT FROM AUTHOR]

An optical sensor based on pyranine immobilized on aminopropyl-modified mesoporous silica films was developed for paraquat detection in aqueous solutions. An electrochemically assisted self-assembly method was used to deposit mesoporous silica film on fluorine-doped tin oxide glass. The obtained films were modified with various concentrations of 3-aminopropyl triethoxysilane (APTES) before the immobilization of pyranine. Cyclic voltammetry, scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, and fluorescence spectroscopy were used to characterize the films. Pyranine-immobilized films gave an emission at 506 nm with an excitation at 450 nm. The fluorescence signal was quenched in the presence of paraquat. The films modified with 3% APTES provided the optimum response to paraquat. The developed films had a linear response to paraquat in the concentration range of 1 to 10 ppm at the optimum conditions, with a detection limit of 0.80 ppm. The developed method was used to quantify paraquat in sugarcane peel and tap water samples with satisfactory results. [ABSTRACT FROM AUTHOR]

The nature of paraquat adsorption is compared between zeolite NaX and NaY which have the same faujasite structure but different Si/Al ratio, namely 1.2 and 2.2, respectively. The adsorption was proposed to occur via ion exchange and expected to increase with Al content. However, NaX had a lower paraquat adsorption capacity than NaY. The bare and paraquat-containing zeolites (PQX and PQY) were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, N2 adsorption–desorption analysis, magic-angle spinning nuclear magnetic resonance (MAS) NMR, and X-ray photoelectron spectroscopy. The presence of adsorbed paraquat was confirmed by Fourier transform infrared spectroscopy. Paraquat adsorbed in supercages of the zeolites resulting in a decrease of surface area and displacement of sodium cations. Results from 23Na MAS NMR and X-ray photoelectron spectroscopy indicated that interaction of sodium ions in the cavity of NaX was stronger than that in NaY, making it less exchangeable with paraquat. [ABSTRACT FROM AUTHOR]

Adsorption of paraquat and pirimiphos-methyl in water was performed on four adsorbents including montmorillonite (Mt), organoclay (TDA-Mt) from intercalation of Mt with tetradecylammonium chloride, and mesoporous Mt from intragallery templating method (with and without Ti addition). The adsorbents were characterized by X-ray diffraction, N2 adsorption-desorption, and transmission electron microscopy. Paraquat adsorption isotherms followed Langmuir model and the adsorption capacity was as follows: TDA-Mt>Mt>mesoporous Ti-Mt>mesoporous Mt. The adsorption mechanism on TDA-Mt and Mt might be via ion exchange. The adsorption on mesoporous samples was on the external surface with negative charge. The presence of Ti enhanced the adsorption capacity. Pirimiphos-methyl adsorbed on negative charge of the external surface of Mt samples. The adsorbed amount increased with the initial concentration due to a strong intermolecular interaction. [ABSTRACT FROM AUTHOR]

NaY was synthesized from fumed silica and further modified to form a composite with SBA-15. Textural properties and basicity of the composite NaY-SBA-15 were between those of the parent materials. Paraquat adsorption on NaY was 204.1 mg/g, higher than that on NaY synthesized with rice husk silica from the previous work. SBA-15 was a poor adsorbent for paraquat. Based on the weight of NaY, the adsorption capacity of analytical-grade paraquat on the NaY-SBA-15 composite was 241.5 mg/g-NaY. Moreover, the composite adsorbed blue dye from a commercial grade paraquat. Interaction between the NaY-SBA-15 and paraquat could be from C and N atoms in paraquat with oxygen atom on NaY-SBA-15. [ABSTRACT FROM AUTHOR]

Photocatalysts were prepared by using TiO2 at 10 and 30 wt% grafted on rice husk silica (RHS) and zeolite NaY. The photocatalysts were characterized by X-ray diffraction and N2 adsorption-desorption analysis. The TiO2 in the anatase phase was well dispersed on the external surface area of the supports. Paraquat adsorption on the catalysts (determined before the photocatalytic testing) mainly occurred on the supports. The adsorption on the TiO2/NaY was much higher than that on the TiO2/RHS. In photocatalytic testing, both the 10 and 30% TiO2/NaY catalysts were not active probably due to high adsorption of the paraquat on the supports. In contrast, both of the TiO2/RHS catalysts were active and the best photocatalyst was the 30% TiO2/RHS. The supported catalyst showed a higher activity than the bare TiO2 indicating the enhancement from the dispersion of the RHS. Moreover, the photocatalytic degradation of paraquat on the 30% TiO2/RHS was similar to commercial TiO2 (P25) with the same TiO2 content. [ABSTRACT FROM AUTHOR]