Search

LMA (Large Mode Area) optical fibers are presently under active investigation to explore their potential for generating laser action or broadband emission directly within the optical fiber structure. Additionally, a wide mode profile significantly reduces the power distribution density in the fiber cross-section, minimizing the power density, photodegradation, or thermal damage. Multi-stage deposition in the MCVD-CDT system was used to obtain the structural doping profile of the LMA fiber multi-ring core doped with Tm3+ and Tm3+/Ho3+ layer profiles. The low alumina content (Al2O3: 0.03wt%) results in low refractive index modification. The maximum concentrations of the lanthanide oxides were Tm2O3: 0.18wt % and Ho2O3: 0.15wt%. The double-clad construction of optical fiber with emission spectra in the eye-safe spectral range of (1.55–2.10 µm). The calculated LP01 Mode Field Diameter (MFD) was 69.7 µm (@ 2000 nm, and 1/e of maximum intensity), which confirms LMA fundamental mode guiding conditions. The FWHM and λmax vs. fiber length are presented and analyzed as a luminescence profile modification. The proposed structured optical fiber with a ring core can be used in new broadband optical radiation source designs. [ABSTRACT FROM AUTHOR]

Double-clad optical fiber with a multi-ring core profile doped with thulium and holmium fabricated by Modified Chemical Vapor Deposition Chelate Doping Technology (MCVD-CDT) is presented. The measured Tm2O3 and Ho2O3 complexes' weight concentrations were 0.5% and 0.2% respectively. Numerical analyses show weakly guiding conditions and 42.2 µm of MFD LP01 at 2000 nm. The low NA numerical aperture (NA = 0.054) was obtained for the 20/250 µm core/cladding ratio optical fiber construction. The emission spectra in the range of 1.6–2.1 µm vs. the fiber length are presented. The full width at half maximum (FWHM) decreases from 318 to 270 nm for fiber lengths from 2 to 10 m. The presented fiber design is of interest for the development of new construction of optical fibers operating in the eye-safe spectral range. [ABSTRACT FROM AUTHOR]

An investigation of fluoroindate glass and fiber co-doped with Yb3+/Er3+ ions as a potential temperature sensor was assessed using the fluorescence intensity ratio (FIR) technique. Analysis of thermally coupled levels (TCLs—2H11/2 and 4S3/2), non-thermally coupled levels (non-TCLs—4F7/2 and 4F9/2), and their combination were examined. Additionally, the luminescent stability of the samples under constant NIR excitation using different density power at three different temperatures was carried out. The obtained values of absolute sensitivity (0.003 K−1—glass, 0.0019 K−1—glass fiber 2H11/2 → 4S3/2 transition) and relative sensitivity (2.05% K−1—glass, 1.64% K−1—glass fiber 4F7/2 → 4F9/2 transition), as well as high repeatability of the signal, indicate that this material could be used in temperature sensing applications. [ABSTRACT FROM AUTHOR]

This study presented an analysis of the TeO2/GeO2 molar ratio in an oxide glass system. A family of melt-quenched glasses with the range of 0–35 mol% of GeO2 has been characterized by using DSC, Raman, MIR, refractive index, PLE, PL spectra, and time-resolved spectral measurements. The increase in the content of germanium oxide caused an increase in the transition temperature but a decrease in the refractive index. The photoluminescence spectra of europium ions were examined under the excitation of 465 nm, corresponding to 7F0 → 5D2 transition. The PSB (phonon sidebands) analysis was carried out to determine the phonon energy of the glass hosts. It was reported that the red (5D0 → 7F2) to orange (5D0 → 7F1) fluorescence intensity ratio for Eu3+ ions decreased from 4.49 (Te0Ge) to 3.33 (Te15Ge) and showed a constant increase from 4.58 (Te20Ge) to 4.88 (Te35Ge). These optical features were explained in structural studies, especially changes in the coordination of [4]Ge to [6]Ge. The most extended lifetime was reported for the Eu3+ doped glass with the highest content of GeO2. This glass was successfully used for the drawing of optical fiber. [ABSTRACT FROM AUTHOR]

The method of the analysis of luminous flux diffusion on the lateral surface of an optical fiber as a basis for designing and manufacturing of side-hole optical fibers is presented. The idea of the controllable emission of the luminous flux by formation of the fiber lateral surface is described. The presented method was verified by manufacturing an optical fiber with controllable emission from the shaped lateral surface. [ABSTRACT FROM AUTHOR]

An investigation of the structural and luminescent properties of the transparent germanate glass-ceramics co-doped with Ni2+/Er3+ for near-infrared optical fiber applications was presented. Modification of germanate glasses with 10–20 ZnO (mol.%) was focused to propose the additional heat treatment process controlled at 650 °C to obtain transparent glass-ceramics. The formation of 11 nm ZnGa2O4 nanocrystals was confirmed by the X-ray diffraction (XRD) method. It followed the glass network changes analyzed in detail (MIR—Mid Infrared spectroscopy) with an increasing heating time of precursor glass. The broadband 1000–1650 nm luminescence (λexc = 808 nm) was obtained as a result of Ni2+: 3T2(3F) → 3A2(3F) octahedral Ni2+ ions and Er3+: 4I13/2 → 4I15/2 radiative transitions and energy transfer from Ni2+ to Er3+ with the efficiency of 19%. Elaborated glass–nanocrystalline material is a very promising candidate for use as a core of broadband luminescence optical fibers. [ABSTRACT FROM AUTHOR]

In this paper, we report on fabricating optical fibers with a controlled process of crystallization core during the drawing process. The research and synthesis of the core material of silica-germanium-antimony oxide glass were discussed. We also investigated the optical and luminescence properties were in relation to concentrating Eu 2 O 3 and P 2 O 5. Based on this investigation, we selected the most promising material for optical fiber core. In the next step, we drew optical fibers using a well-known rod-in-tube method. After drawing, we examine the optical fibers for luminescence shape changes. We observed a promising similarity between optical fibers and heat-treated samples with confirmed nanocrystals. Finally, XRD and TEM measurements confirm EuPO 4 nanocrystals at the core of the optical fiber. Highlighting the successful control of crystallization in the one-step method used to draw optical fibers. [ABSTRACT FROM AUTHOR]

In this study, a comprehensive analysis of emission in erbium-doped and erbium and ytterbium co-doped fluoroindate glasses has been presented. The luminescence of the erbium transitions and the effect of ytterbium co-doping under 488, 808 and 976 nm laser excitation have been discussed. Optimization of rare-earth (RE) ions doping concentration and the energy transfer processes related to the sensibilization effect in Er3+/Yb3+ co-doped fluoroindate glasses focusing on the reciprocal distribution of radiative transitions, energy transfer parameters, and lifetimes have been analyzed. The luminescence consists of several bands in the visible (525, 546 and 660 nm) and the infrared (1550 and 2700 nm) spectral regions that correspond to characteristic radiative energy transitions within the erbium ions. In glasses co-doped with the Er3+/Yb3+ system, an augmentation in the emission intensity was observed in the visible and at 1550 nm, while a decrease was observed in the 2700 nm infrared band. The increase of the Yb3+: 2F 5/2 lifetime under 488, 808 and 976 nm excitation showed significant Er3+: 4I 11/2 → Yb3+: 2F 5/2 back energy transfer. Based on the analysis of the available literature, it can be concluded that energy transfer upconversion and cooperative energy upconversion play a significant role in modulating luminescence intensity values within the examined emission bands. This effect is likely enhanced due to the incorporation in a low phonon energy glass matrix. As a result of the above optimization, a glass optical fiber co-doped with 0.8 YbF 3 /1.4 ErF 3 (in mol%) was drawn and characterized, showing a strong emission at 2.77 μm. The optimized Er3+/Yb3+ co-doped fluoroindate glass and glass optical fiber confirmed their ability to be used in the visible and near-infrared spectral regions as efficient optical fiber sources. [ABSTRACT FROM AUTHOR]

This work presents an analysis of the spectroscopic properties of glass and glass ceramics co-doped with Ni2+ and Er3+ ions. Spectroscopic analysis showed the embedding of nickel ions in the gamma-gallium oxide nanocrystals as a result of heat treatment of the glass samples. Analysis of the luminescence properties of the obtained samples under 940 nm and 980 nm pump excitation allowed the selection of a proper Er3+ ions concentration for further optical fiber fabrication. Measured lifetime results of glass-ceramics samples confirm energy transfer from nickel ions to erbium. In the process of drawing the optical fiber, it was possible to create a transparent nanocrystalline glass-ceramic core, as confirmed by XRD results. The produced glass-ceramic optical fiber was characterized by broadband emission in the range from 1100 nm to 1650 nm corresponding to the 3T 2 (3F) →3A 2 (3F) (Ni2+) and 4I 13/2 → 4I 15/2 (Er3+) transitions for 940 nm and 980 nm pump excitation. The Er3+ to Ni2+ ions emission intensity ratio of the fabricated glass-ceramic fiber was estimated to be 0.84 and 7.14 for 940 nm and 980 nm optical pumps, respectively. [ABSTRACT FROM AUTHOR]