Search

The Kurtz-Perry powder technique (KPPT) is widely utilized for the rapid characterization of newly grown nonlinear optical (NLO) materials available in pristine powder form. It assesses the effective nonlinear susceptibility of randomly oriented powder in comparison with a reference material. This technique becomes especially versatile when equipped with a broad wavelength range and intensity tunability because it provides key NLO properties of the materials under investigation, such as the frequency dispersion of the NLO susceptibility, phase-matching (PM) range, and laser-induced damage threshold (LIDT) as a guideline. In this study, wavelength-dependent NLO experiments (λ = 1100 – 3700 nm) were conducted on polycrystalline LiInSe 2 , prepared by high-temperature, solid-state synthesis. Our LiInSe 2 was found to be phase-matchable for λ > 2500 nm and the effective NLO susceptibility was estimated as 20.0 ± 1.9 pm/V, assessed at the static limit using commercial-grade single crystals of AgGaS 2 and AgGaSe 2 that were ground to powders. Alternatively, the effective NLO susceptibility was determined to be twice as large, ~40 pm/V, when utilizing a homemade, microcrystalline AgGaSe 2 reference at the static limit. This severe overestimation of the NLO susceptibility that can occur while working with a homemade standard underscores the importance of using a commercial-grade reference with the KPPT. Furthermore, this study also discusses the LIDT of LiInSe 2 based on intensity-dependent SHG at 1064 nm with picosecond pulses, and compares with those of the commercial-grade AgGaS 2 and AgGaSe 2 , determined under identical conditions. As defect levels can cause widely varying apparent color, thus optical bandgap, in LiInSe 2 , this study stresses the importance of using a high-quality standard when exploiting the KPPT for NLO materials characterization. The role of defects is discussed in terms of χ 2 , phase matching onset and LIDT, parameters that predominantly affect the evaluation of new NLO materials. [Display omitted] • A high-quality NLO reference is necessary for the Kurtz-Perry powder technique. • Broadband measurements best characterize the behavior of candidate NLO materials. • The laser-induced damage threshold of LiInSe 2 is 1.0 GW/cm2 (λ = 1064 nm, τ = 30 ps). • LiInSe 2 has a χ(2) value of ~20 pm/V and is phase matchable for λ > 2500 nm. [ABSTRACT FROM AUTHOR]

Two new lithium-containing diamond-like semiconductors, Li2ZnGeSe4 and Li2ZnSnSe4, have been prepared by high-temperature, solid-state synthesis. Single crystal X-ray diffraction reveals that both compounds adopt the wurtz–kesterite structure type, crystallizing in the noncentrosymmetric space group Pn. X-ray powder diffraction coupled with Rietveld refinement indicates the high degree of phase purity in which the materials are prepared. Both compounds display optical bandgaps around 1.8 eV, wide optical transparency windows from 0.7 to 25 μm and type-I phase matched second harmonic generation starting at 2500 nm and persisting deeper into the infrared. Using the Kurtz powder method, the second-order nonlinear optical coefficient, χ(2), was estimated to be 19 and 23 pm V−1 for Li2ZnGeSe4 and Li2ZnSnSe4, respectively. Using a 1064 nm incident laser beam with a pulse width (τ) of 30 ps both compounds exhibit a laser damage threshold of 0.3 GW cm−2, which is higher than that of the AgGaSe2 reference material measured under identical conditions. Differential thermal analysis shows that the title compounds are stable up to 684 and 736 °C, respectively. These properties collectively demonstrate that Li2ZnGeSe4 and Li2ZnSnSe4 have great potential for applications in tunable laser systems, especially in the infrared and even up to the terahertz regime. Electronic structure calculations using a plane-wave pseudopotential method within density functional theory provide insight regarding the nature of the bandgap and bonding. [ABSTRACT FROM AUTHOR]

Two new lithium-containing diamond-like semiconductors, Li2ZnGeSe4 and Li2ZnSnSe4, have been prepared by high-temperature, solid-state synthesis. Single crystal X-ray diffraction reveals that both compounds adopt the wurtz–kesterite structure type, crystallizing in the noncentrosymmetric space group Pn. X-ray powder diffraction coupled with Rietveld refinement indicates the high degree of phase purity in which the materials are prepared. Both compounds display optical bandgaps around 1.8 eV, wide optical transparency windows from 0.7 to 25 μm and type-I phase matched second harmonic generation starting at 2500 nm and persisting deeper into the infrared. Using the Kurtz powder method, the second-order nonlinear optical coefficient, χ(2), was estimated to be 19 and 23 pm V−1 for Li2ZnGeSe4 and Li2ZnSnSe4, respectively. Using a 1064 nm incident laser beam with a pulse width (τ) of 30 ps both compounds exhibit a laser damage threshold of 0.3 GW cm−2, which is higher than that of the AgGaSe2 reference material measured under identical conditions. Differential thermal analysis shows that the title compounds are stable up to 684 and 736 °C, respectively. These properties collectively demonstrate that Li2ZnGeSe4 and Li2ZnSnSe4 have great potential for applications in tunable laser systems, especially in the infrared and even up to the terahertz regime. Electronic structure calculations using a plane-wave pseudopotential method within density functional theory provide insight regarding the nature of the bandgap and bonding. [ABSTRACT FROM AUTHOR]

Abstract: Borogermanates are a class of very important compounds in materials chemistry. In this paper, the syntheses, structures, and properties of metal borogermanates are reviewed. Organically templated borogermanates with zeolite-like open-frameworks show potential applications as microporous materials. Many compounds in alkali or alkaline-earth borogermanate systems are structurally acentric or polar, some of which exhibit excellent Second Harmonic Generation (SHG) coefficients, wide transparency regions, and high optical-damage thresholds as well as excellent thermal stability. Most of the lanthanide borogermanates are structurally centrosymmetric and not SHG active; however, they are able to emit strong luminescence in visible or near-IR region. In the B-rich compounds, BO3 and BO4 groups can be polymerized into a variety of discrete polynuclear anionic cluster units or extended architectures via B–O–B bridges; whereas in the Ge-rich compounds, GeO4 and GeO6 polyhedra can also be polymerized. The combinations of borate and germinate afforded rich structural and topological types. [Copyright &y& Elsevier]

• Cu 4 ZnGe 2 Se 7 is a new diamond-like semiconductor with the Cu 4 NiSi 2 S 7 structure type. • CZGSe and Cu 4 ZnGe 2 Se 7 possess optical bandgaps of 1.38 and 0.91 eV, respectively. • CZGSe and Cu 4 ZnGe 2 Se 7 are air stable and have wide windows of optical transparency. • CZGSe exhibits a strong second harmonic generation response at λ = 2900 nm. • CZGSe is an excellent candidate for low-powered infrared nonlinear optical devices. [Display omitted] In this study, two quaternary diamond-like semiconductors (DLSs) in the Cu-Zn-Ge-Se system, the known Cu 2 ZnGeSe 4 (also referred to as CZGSe) and the new Cu 4 ZnGe 2 Se 7 , are compared in terms of their crystal structures, electronic structures and physicochemical properties. Both compounds were prepared by high-temperature, solid-state synthesis at 800 °C. Single crystal X-ray diffraction was used to determine the structure of Cu 4 ZnGe 2 Se 7. The structures of both Cu 2 ZnGeSe 4 and Cu 4 ZnGe 2 Se 7 can be considered as derivatives of cubic diamond. Cu 4 ZnGe 2 Se 7 , with a reduced symmetry due to the cation ordering pattern, adopts the Cu 4 NiSi 2 S 7 structure type, with space group C 2. The corner-sharing tetrahedra in Cu 4 ZnGe 2 Se 7 are slightly distorted because the charge for some of the S2- anions is not compensated by the first-nearest-neighbor cations. Rietveld refinements using synchrotron X-ray powder diffraction data were used to assess the phase purity of the samples and confirm the bulk structural behavior. Diffuse reflectance UV/Vis/NIR spectroscopy shows that Cu 2 ZnGeSe 4 and Cu 4 ZnGe 2 Se 7 have direct optical bandgaps of 1.38 and 0.91 eV, respectively. Electronic structure calculations implementing density functional theory confirm the direct bandgap for Cu 4 ZnGe 2 Se 7 , with a calculated value of 0.62 eV. Both compounds are air stable, thermally stable up to relatively high temperatures, undergo phase transitions and have wide windows of optical clarity. The Kurtz-Perry powder technique was used to determine the second harmonic generation (SHG) responses using a commercial AgGaSe 2 standard. While Cu 4 ZnGe 2 Se 7 displays a weak SHG response, Cu 2 ZnGeSe 4 exhibits a response that is greater than several benchmark materials, with a large SHG coefficient, χ (2) , of 43 ± 6 pm/V at λ = 2900 nm. [ABSTRACT FROM AUTHOR]

A new alkali-metal borogermanate with noncentrosymmetric structure, namely, Cs2GeB409, has been discovered, and a large crystal with dimensions of 20 × 16 × 8 mm(3) has been grown by a high-temperature top-seeded solution method using Cs2O-B2O2 as a flux. The compound crystallizes in the tetragonal space group I4 with a = b = 6.8063(2) Å, c = 9.9523(7) Å, V = 461.05(4) Å3, and Z = 2. It features a three-dimensional anionic open framework based on GeO4 tetrahedra and B4O9 clusters that are interconnected via corner-sharing, forming one-dimensional channels of nine-/ten-membered rings along the a and b axes, which are occupied by Cs+ cations. Cs2GeB409 exhibits a very high thermal stability with a melting point of 849 °C, and it possesses a short-wavelength absorption edge onset at 198 nm determined by UV-vis transmission spectroscopy measurements on a slab of polished crystal. Powder second-harmonic generation (SHG) measurement on sieved crystals reveals that Cs2GeB409 is a type I phase-matchable material with a strong SHG response of about 2.8 × KH2PO4. The preliminary investigation indicates that Cs2GeB409 is a new promising second-order nonlinear-optical crystalline material. [ABSTRACT FROM AUTHOR]

A new nonlinear optical crystal, Na3VO2B6O11, has been grown by the top-seeded solution growth method using a Na2CO3−V2O5flux. The structure of the compound was determined by single-crystal X-ray diffraction. It crystallizes in the noncentrosymmetric orthorhombic system, space group P212121, with cell parameters a= 7.7359(9) Å, b= 10.1884(12) Å, c= 12.5697(15) Å, V= 990.7(2) Å3, and Z= 4. Na3VO2B6O11has a three-dimensional structure consisting of hexaborate groups connected by VO4tetrahedra with the sodium atoms distributed in channels through out the three-dimensional network. The refractive indices have been measured by the minimum deviation technique and fit to the Sellmeier equations. Nonlinear optical measurements on the compound demonstrate that the material has second harmonic generation properties, with an efficiency approximately the same as that of KH2PO4. [ABSTRACT FROM AUTHOR]