In this study, the aging process of a surface-functional titanium dioxide nanosheet (f-TNS) composited room-temperature-vulcanized silicone rubber (RTV) composite coating was simulated in a NO2 generation device, and then the electrochemical impedance spectroscopy (EIS) of the aged composite coating was tested in a 3.5% NaCl solution. The water permeation process was analyzed by the changes in the impedance modulus, porosity, and breakpoint frequency of the composite coating. The experimental results show that the water permeability of aged RTV decreases first and then increases with the increase in the composite proportion of f-TNS. When the composite proportion of TNS was 0.3 wt.%, the composite sample had the minimum water permeability and the best resistance to NO2 corrosion. The effect of TNS on the NO2 aging resistance of RTV composites and its mechanism were studied by SEM, FT-IR, and XPS. The impedance modulus and porosity of the aged 0.3% f-TNS/RTV, respectively, were 1.82 × 107 Ω cm2 and 0.91 × 10−4%, which increased by 2.23 times and decreased by 0.37 times, respectively, compared with the values of aged pure RTV sample. In addition, the breakpoint frequency of the aged 0.3% f-TNS/RTV also significantly reduced to 11.3 Hz, whereas it was 35 Hz in aged pure RTV. [ABSTRACT FROM AUTHOR]

In this study, functional graphene oxide (f-GO) nanosheets were prepared to enhance the NO2 resistibility of room-temperature-vulcanized (RTV) silicone rubber. A nitrogen dioxide (NO2) accelerated aging experiment was designed to simulate the aging process of nitrogen oxide produced by corona discharge on a silicone rubber composite coating, and then electrochemical impedance spectroscopy (EIS) was used to test the process of conductive medium penetration into silicone rubber. After exposure to the same concentration (115 mg·L−1) of NO2 for 24 h, at an optimal filler content of 0.3 wt.%, the impedance modulus of the composite silicone rubber sample was 1.8 × 107 Ω·cm2, which is an order of magnitude higher than that of pure RTV. In addition, with an increase in filler content, the porosity of the coating decreases. When the content of the nanosheet increases to 0.3 wt.%; the porosity reaches a minimum value 0.97 × 10−4%, which is 1/4 of the porosity of the pure RTV coating, indicating that this composite silicone rubber sample has the best resistance to NO2 aging. [ABSTRACT FROM AUTHOR]