Neutron and x‐ray diffraction measurements have been performed on CaO–MgO–Al2O3–SiO2 (CMAS) glasses doped with NiO–FeXO at room temperature, along with x‐ray measurements on aerodynamically levitated liquids at ≥2000 K. The disordered structures have been modeled using empirical potential structure refinement to investigate the relation between the aluminosilicate network and the modifying cations. The SiO4 and AlO4 tetrahedra are found to have wider Si–O and Al–O bond distance distributions in the glass, and the first Ca–On coordination shell is highly distorted, redistributing different populations of long and short bonds between the liquid and the glass. The addition of Fe and Ni at low aluminosilicate content increases the number of free oxygens not bonded to AlO4 or SiO4. Mg–O and Fe–O are both found to be predominantly fourfold and fivefold in the liquid and glassy states. Despite these low coordination numbers, their bond angle distributions indicate that they are predominantly in nontetrahedral‐type geometries, with ferrous and ferric iron possessing similar coordination environments. The Ca–O and Mg–O average coordination numbers and enthalpies of solution are consistent with their higher reactivity within relatively acidic aluminosilicate melts. [ABSTRACT FROM AUTHOR]

Rare-earth titanates form very fragile liquids that can be made into glasses with useful optical properties. We investigate the atomic structure of 83TiO2-17Nd2O3 glass using pair distribution function (PDF) analysis of X-ray and neutron diffraction with double isotope substitutions for both Ti and Nd. Six total structure factors are analyzed (5 neutron + 1 X-ray) to obtain complementary sensitivities to O and Ti/Nd scattering, and an empirical potential structure refinement (EPSR) provides a structural model consistent with the experimental measurements. Glass density is estimated as 4.72(13) g cm−3, consistent with direct measurements. The EPSR model indicates nearest neighbor interactions for Ti-O at r ¯ TiO = 1.984(11) Å with coordination of n TiO = 5.72(6) and for Nd-O at r ¯ NdO = 2.598(22) Å with coordination of n NdO = 7.70(26), in reasonable agreement with neutron first order difference functions for Ti and Nd. The titanate glass network comprises a mixture of distorted Ti-O5 and Ti-O6 polyhedra connected via 71% corner-sharing and 23% edge-sharing. The O-Ti coordination environments include 15% nonbridging O-Ti1, 51% bridging O-Ti2, and 32% tricluster O-Ti3. This structure is highly unusual for oxide glasses melt-quenched at ambient pressure, as it consists of Ti-Ox predominantly in octahedral (with nearly no tetrahedral) coordination. [ABSTRACT FROM AUTHOR]