Nanoscale, 9 (38), ISSN:2040-3364, ISSN:2040-3372

We extend the commonly used synthesis strategies for responsive microgels to the design of novel multiresponsive and multifunctional nanoparticles that combine inorganic magnetic, metallic/catalytic and thermoresponsive organic moieties. Magnetic responsiveness is implemented through the integration of silica-coated maghemite nanoparticles into fluorescently labeled crosslinked poly(N-isopropylmethacrylamide) microgels. These particles are then employed as templates for the in situ reduction of catalytically active gold nanoparticles. In order to tune the reactivity of the catalyst through a thermally controlled barrier, an additional layer of crosslinked poly(N-isopropylacrylamide) is added in the final step. We subsequently demonstrate that these particles can be employed as smart catalysts. We show that the thermoresponsive nature of the outer particle shell not only provides control over the catalytic activity, but when combined with a magnetic core allows for very efficient removal of the catalytic system through temperature-controlled reversible coagulation and subsequent magnetophoresis in an applied magnetic field gradient. We finally discuss the use of this design principle for the synthesis of complex hybrid particles for various applications that would all profit from their multiresponsive and multifunctional nature.

The synthesis via in situ polymerization and characterization of nanocomposites (NCs) made from silica (SiO(2)) nanoparticles in a methyl methacrylate (MMA) monomer matrix is reported. We first investigate the transfer of well-defined spherical silica nanoparticles (NPs) (average radius R = 24.2 ± 3.2 nm) into the monomer solvent. We study the influence of two transfer methods and different surface chemistries on the resulting colloidal stability. The first transfer method consists of drying the silica particles into powder before dispersing them via ultrasonication in the MMA matrix. The second is based on repetitive centrifugations to exchange NPs from their synthetic milieu to pure MMA, avoiding the dried powder state. These transfer methods are compared for two kinds of NP surface chemistry, natural silanol (Si-OH) groups of the silica NPs and an additional silane coupling agent, namely 3-(trimethoxysilyl)propyl methacrylate (TPM), which mimics the monomeric group of the MMA dispersing milieu. We then characterize the morphology of the resulting nanocomposites prepared via in situ polymerization at a fixed amount of dispersed NPs (2.2 wt%; 1 vol%) using a combination of transmission electron microscopy (TEM) from ultramicrotomed nanocomposite films, thermogravimetry (TGA) and small angle X-ray scattering (SAXS).