During operation, cables of overhead power lines (OPLs) are exposed to the impact that differs in separate parts of the OPL span due to the different responses of cables near the clamps and far from them. This paper presents the results of a study of aluminum and steel wires cut from such separate parts of ACSR cables before and after exploitation. Structural, microstructural, and elastic–microplastic properties of wires and their changes during operation were studied through optical microscopy, energy-dispersive X-ray microanalysis, electron backscattering diffraction, X-ray diffraction, densitometry, and acoustic measurements. The characteristics of the properties of the wires along the span were found to change in a coordinated manner. Numerical estimates of the influence of the steel core on aging the ACSR cable were obtained. Changes in the properties of the wires, as well as oxidization and corrosion of their near-surface layers, were studied in detail. Quantitative values of the characteristics of properties, the most distant from those observed in the new wires, were revealed for samples of aluminum and steel wires cut from the cable at 1/4 span and near clamps. It is assumed that these cable parts should be the most crucial for cable durability. [ABSTRACT FROM AUTHOR]

Single Al wires from unused AAAC (A50) cables were studied after laboratory fatigue testing, which simulated processes arising in these wires during their operation in the cables of overhead power lines (OPLs) and are valuable for predicting the lifespan of cables of OPLs. These wires, which were either fractured during testing (maximum loads—149.4–155.9 MPa; number of cycles till rupture—83,656–280,863) or remained intact, were examined by X-ray diffraction, electron backscatter diffraction, densitometry, and acoustic methods. An analysis of the structural, microstructural, and elastic-microplastic properties of the wires revealed common characteristics inherent in the samples after operation in OPLs and after fatigue tests, namely a decrease in the integral and near-surface layer (NSL) densities of the wires, a decrease in their Young's modulus and microplastic stress, and an increase in the decrement. However, the tests did not fully reproduce the environmental influence, since in contrast to the natural conditions, no aluminum-oxide crystallites were formed in NSLs in tests and the microstructure was different. A comparison of the characteristics of the broken and unbroken wires allows us to suggest that the fastening locations of the wires are crucial for their possible failure. [ABSTRACT FROM AUTHOR]