Search

Abstract: Ageing treatment at 200°C and 225°C for various periods of time was introduced to the Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt.%) alloy, the age-hardening behaviour and phase transformation were analysed systematically. The alloy aged at 225°C exhibits accelerated ageing progress compared with that aged at 200°C. The precipitation sequences of the alloy aged at both 200°C and 225°C are supersaturated solid solution (SSSS)→β′′ (D019)→β′ (bco). Stacking faults and 14H LPSO phase formed in the alloy over-aged at 200°C and 225°C, respectively. The equilibrium β phase precipitated at the grain boundaries with the formation of precipitate free zone (PFZ) at the peak-aged stage, after further ageing treatment, the β phase got coarsened, which was accompanied with the widening of the PFZ. [Copyright &y& Elsevier]

Abstract: The extruded Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt%) alloy were subjected to large-strain hot rolling with different final rolling temperatures. The microstructural evolution and mechanical properties of the sheets were investigated. The microstructure became homogeneous after hot rolling process and long period stacking ordered (LPSO) phase distributed at grain boundaries along rolling direction. The sheet rolled at 300°C was composed of deformed grains, substructures and excessive dislocations. With increasing final rolling temperatures from 300°C to 400°C, the volume fraction of recrystallized grains with relatively random orientations increased significantly. The strength of the rolled sheets was improved while the ductility was deteriorated with decreasing final rolling temperatures. The tensile yield strength and ultimate tensile strength of the sheet rolled at 300°C reached 320MPa and 416MPa, respectively with the elongation to failure of 5.3%. The mechanical anisotropy of the rolling sheet became unity when rolled at higher temperature of 400°C due to the formation of weaker basal texture. [Copyright &y& Elsevier]

Abstract: Different cooling processes, such as quenching in warm water and cooling in furnace, were introduced to homogenize Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt%) alloy. Microstructure evolution and mechanical properties of the homogenized alloy were investigated. The as-quenched sample was comprised of α-Mg matrix, Mg5RE phase and 18R LPSO phase distributed at the grain boundaries and a few of RE-rich particles distributed randomly. During the process of cooling in furnace, Mg5RE and 18R LPSO phases were transformed into block-shaped 14H LPSO phase and lamellar-shaped 14H LPSO phase, respectively, due to the diffusion of solute atoms into the α-Mg matrix. Furthermore, the lamellar-shaped 14H LPSO phase grew and ran through the whole grains. The as-quenched sample exhibits tensile yield strength of 130MPa, ultimate tensile strength of 206MPa and elongation to failure of 5.5%, while the sample cooled in the furnace exhibits higher tensile yield strength but lower ultimate tensile strength and ductility due to the coarse grains and formation of block-shaped 14H LPSO phase. [Copyright &y& Elsevier]

Abstract: The Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt.%) alloy was hot rolled with different final rolling reductions at 400°C. The microstructure evolution and texture of the sheets were analyzed, and their effect on the mechanical properties was discussed. All of the rolled sheets consist of fine dynamically recrystallized grains with almost random orientation, large deformed grains with strong basal texture. In addition, bent lamellar-shaped long period stacking ordered (LPSO) phases due to kink deformation were observed in the deformed grains. The volume fraction of the dynamic recrystallization increased with increasing final rolling reduction and the basal texture weakened gradually. The strength of the alloy sheets changed a little with increasing final rolling reduction, while the yield anisotropy and the ductility were significantly improved. The sheet final-rolled with thickness reduction of 60% exhibits tensile yield strength of 306MPa, ultimate tensile strength of 393MPa and elongation to failure of 14.6% at ambient temperature, and tensile yield strength of 264MPa, ultimate tensile strength of 345MPa and elongation to failure of 19.4% at 250°C. [Copyright &y& Elsevier]

Abstract: Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy ingot with diameter of 280mm and length of 2940mm was successfully fabricated by semi-continuous casting. The microstructure and mechanical properties of the large ingot at different locations were investigated. The concentration of the RE and Zn elements distributed almost homogeneously through the whole alloy ingot. The average grain size decreased from the center to the surface of the alloy ingot, while the strength and ductility were improved gradually. The main eutectic compounds located at the grain boundaries were (Mg,Zn)3(Gd,Y) phase, adjacent to these eutectic compounds the 14H-type long period stacking ordered (LPSO) phase formed. Furthermore, some block-shaped Mg24(Gd,Y)5 phase and isolated Zr cores can be recognized in the interior of the grains. [Copyright &y& Elsevier]

Abstract: Ultra high-strength Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy sheet was prepared by large-strain hot rolling and subsequent ageing process. The sheet exhibits excellent tensile properties at ambient temperature with ultimate tensile strength of 517MPa, 0.2% proof stress of 426MPa and elongation to failure of 4.5%. The notable improvement in strength is attributed to the dense distribution of the fine precipitates inside the grains, scattered precipitates at the grain boundaries, bimodal grain size distribution with fine recrystallized grains and large deformed grains with intense basal texture. [Copyright &y& Elsevier]