Search

A Cu-based methanol synthesis catalyst was obtained from a phase pure Cu,Zn,Al hydrotalcite-like precursor, which was prepared by co-precipitation. This sample was intrinsically more active than a conventionally prepared Cu/ZnO/Al2O3 catalyst. Upon thermal decomposition in air, the [(Cu0.5Zn0.17Al0.33)(OH)2(CO3)0.17] ⋅ mH2O precursor is transferred into a carbonate-modified, amorphous mixed oxide. The calcined catalyst can be described as well-dispersed 'CuO' within ZnAl2O4 still containing stabilizing carbonate with a strong interaction of Cu2+ ions with the Zn-Al matrix. The reduction of this material was carefully analyzed by complementary temperature-programmed reduction (TPR) and near-edge X-ray absorption fine structure (NEXAFS) measurements. The results fully describe the reduction mechanism with a kinetic model that can be used to predict the oxidation state of Cu at given reduction conditions. The reaction proceeds in two steps through a kinetically stabilized CuI intermediate. With reduction, a nanostructured catalyst evolves with metallic Cu particles dispersed in a ZnAl2O4 spinel-like matrix. Due to the strong interaction of Cu and the oxide matrix, the small Cu particles (7 nm) of this catalyst are partially embedded leading to lower absolute activity in comparison with a catalyst comprised of less-embedded particles. Interestingly, the exposed Cu surface area exhibits a superior intrinsic activity, which is related to a positive effect of the interface contact of Cu and its surroundings. [ABSTRACT FROM AUTHOR]

The application of different methods for a microstructural analysis of functional catalysts is reported for the example of different Cu/ZnO-based methanol synthesis catalysts. Transmission electron microscopy and diffraction were used as complementary techniques to extract information on the size and the defect concentration of the Cu nano-crystallites. The results, strengths and limitations of the two techniques and of different evaluation methods for line profile analysis of diffraction data including Rietveld-refinement, Scherrer- and (modified) Williamson-Hall-analyses, single peak deconvolution and whole powder pattern modeling are compared and critically discussed. It was found that in comparison with a macrocrystalline pure Cu sample, the catalysts were not only characterized by a smaller crystallite size, but also by a high concentration of lattice defects, in particular stacking faults. Neutron diffraction was introduced as a valuable tool for such analysis, because of the larger number of higher-order diffraction peaks that can be detected with this method. An attempt is reported to quantify the different types of defects for a selected catalyst. [ABSTRACT FROM AUTHOR]

Formal kinetic analysis of reduction process of the Cu-based layered double hydroxide -- LDH catalyst precursor for methanol synthesys was implemented. The process was studied by means of thermogravimetry (TG) and Differential scanning calorimetry (DSC) with respect to changes taking place in gas phase, which was analyzed by Massspectrometry (MS). The kinetic parameters of the non-isothermal reduction were determined and the rate limiting step was found. [ABSTRACT FROM AUTHOR]

One of the main stumbling blocks in developing rational design strategies for heterogeneous catalysis is that the complexity of the catalysts impairs efforts to characterize their active sites. We show how to identify the crucial atomic structure motif for the industrial Cu/ZnO/Al2O3 methanol synthesis catalyst by using a combination of experimental evidence from bulk, surface-sensitive, and imaging methods collected on real high-performance catalytic systems in combination with density functional theory calculations. The active site consists of Cu steps decorated with Zn atoms, all stabilized by a series of well-defined bulk defects and surface species that need to be present jointly for the system to work. [ABSTRACT FROM AUTHOR]