Abstract: By using different dual-template combinations, four types of mesoporous silica materials with different morphologies were successfully synthesized. A solid-sphere mesoporous (SSM) silica was obtained using a combination of tri-block copolymer (F127) and 1,12-diaminododecane (DADD), but when F127 was substituted with poly(vinylpyrrolidone) (PVP), a leaf-shaped mesoporous (LSM) silica was obtained. In addition, a hollow-sphere mesoporous (HSM) silica was obtained by using a combination of PVP and dodecylamine (DDA), but a cotton-like mesoporous (CLM) silica was obtained using F127 instead of PVP. All four types of synthesized materials were characterized by SEM, TEM, XRD, and N2 adsorption–desorption isotherms, and the results showed that all of them exhibited high surface area, large pore volume, worm-like pore structure, and beautiful shapes. The results of storage experiments revealed that the HSM and CLM showed good adsorption and storage properties. The HSM (the largest pore volume) seemed to have the larger storage capacity when compared to the CLM, albeit CLM had the highest surface area among all. [Copyright &y& Elsevier]

Abstract: A hollow sphere neodymium embedded mesoporous silica material (NEMS) has been synthesized successfully by using neutral 1,12-diaminododecane as template and embedding Nd into the framework simultaneously. It is interesting that a lamellar structured material with MSU-V structure was obtained if only DADD was used as template without embedding of Nd. The synthesized materials were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), BET method, thermal gravimetry/differential thermal analysis (TG/DTA), and X-ray photoelectron spectroscopy (XPS). The hollow sphere morphology was observed by TEM images and clearly revealed the structure of NEMS molecular sieves. Both XRD and XPS results confirmed that the Nd atoms were incorporated into the framework of mesoporous materials. The TG/DTA results verified the good thermal stability of the synthesized NEMS material. The surface area of samples with Si/Nd molar ratio from 10 to 60 reached from 543 to 1103m2 g−1, respectively. It also found that the Nd embedded mesoporous silica material showed good catalytic activity and selectivity towards the oxidation of styrene, proportional to the neodymium content in the catalysts. [Copyright &y& Elsevier]

Highlights: [•] Mesoporous silica supported Pd-promoted gold catalyst was prepared. [•] Low Pd/Au atomic ratio of 0.05/1 can effectively decrease the gold particles size. [•] Pd0.2Au shows 8 and 3 times higher activity than the Au/MSN and Pd/MSN respectively. [•] Catalysts were characterized by XRD, N2 sorption, DRUV-vis, TPR, XPS and TEM. [Copyright &y& Elsevier]