Search

This study aims to determine the effect of the mold casting duct variations on shrinkage, porosity defects, density, hardness, and chemical composition of materials. The primary raw material uses melting secondary aluminium through a small-scale smelting furnace. Research study about three kinds of ducts: triangular duct, rectangular duct, and circular duct. The testing chemical composition uses an emission spectrometer. Research founds defects by comparing the dimensions of the original object with the specimen results of each duct variation. The density value calculates porosity defects. ASTM E10 standard Brinell test measures the hardness. Besides, ASTM E3 standard test quantifies the microstructure of the product. The highest average shrinkage is the triangular ducts at 3.68%. The least significant numbers of porosity were in rectangular ducts of 2.964 gr/ml. Higher the density value, the denser the material, and the more negligible the porosity. The density of the material affects the hardness material obtained from the results of the Brinell test. The hardness of the Brinell test brought that the rectangular duct with 102.5 BHN was the most enormous. In addition, the results showed that the chemical composition mainly contained mostly chemical elements (Al) 87.1% as the main chemical ingredient and (Si) 9.51%.

Gray cast iron has graphite flakes which makes it relatively weak and brittle. The addition of magnesium to gray cast iron resulted in nodular cast iron which has spherical graphite. The aim of this research was to investigate the changes in the microstructure and strength due to the addition of magnesium to gray cast iron. Microstructure observations were made by metallographic testing using Scanning Electron Microscopy and Energy Dispersive Spectroscopy. Tensile testing was carried out to measure the yield strength, tensile strength, and modulus of elasticity. The addition of magnesium to gray cast iron was observed to increase the yield strength by 179%, tensile strength by 238%, and decrease the modulus of elasticity by 94%.

This study presents the investigation of friction coefficient effect on stress-strain distribution of ceramic coated aeroengine specific material substrate using explicit finite element method. Half-cylinder-on-flat contact configuration subjected to normal and tangential loading is examined. Elastic ceramic coated elastic-plastic Ti-6Al-4V and Super CMV substrates are assigned to study the influence of different friction coefficient on contact pressure, von Mises stress, tangential stress and equivalent plastic strain distribution. The outcome of present research is quite revealing that stress-strain distribution response is remarkable for sliding step which experiencing significant traction compared to normal loading step. Higher possibilities of coated substrate equivalent plastic strain (plastic deformation) are registered under higher friction coefficient cases due to substantial resistance to overcome relative to tangential motion of contacting bodies.

One of the techniques to increase the hardness of aluminum alloy is by aging process. The aging process includes natural aging and artificial aging processes. This study aims to investigate the effect of artificial aging on the hardness of aluminum silicon alloys. Artificial aging is carried out at two temperature variations, namely 150 and 200 °C. Metallographic test using optical microscopy and scanning electron microscopy were performed to observe the microstructure and deposits of silicon. Investigation of the constituent elements of aluminum silicon was carried out using the Energy Dispersive X-Ray Spectroscopy technique. The mechanical properties of aluminum silicon alloys examined were hardness before aging and hardness after artificial aging at temperatures of 150 and 200 °C. Hardness testing is conducted by Rockwell B hardness testing. The hardness test results showed that the hardness before the aging process was 61.1 HRB, the hardness after artificial aging at 150 °C was 69.11 HRB and the hardness after artificial aging at 200 °C was 80.36 HRB. There was an increase in hardness after the artificial aging process was carried out.

Nodular cast iron is a type of cast iron with spheroid graphite surrounded by ferrite matrix and / or pearlite. The size of the graphite and its matrix affects the mechanical properties of the cast iron. This research was conducted to investigate the effect of Magnesium composition on strength, stiffness and toughness of nodular cast iron. Magnesium addition is performed by adding FeSiMg alloys. After that, the composition of magnesium was investigated by using spectrometry. Then tensile test was conducted to obtain the yield strength, tensile strength and modulus of elasticity. Further, impact test was performed to determine the impact energy needed to break the material. The result showed an increase of yield strength, tensile strength and stiffness and a decrease of toughness.

The purpose of this research is to investigate the corrosion resistance of 5052 aluminum alloy to increasing salinity in sea water. Salt spray chamber was used to measure and compare the corrosion rate of 5052 aluminum alloy with weight reduction method. The experiment was conducted by varying the three concentrations of NaCl solution to compare the corrosion rate of the metal. The test specimens used were aluminum alloy 5052 with length of 6 cm, width of 4 cm and thickness of 0.7 cm. The tests were carried out for 48 hours, aggressive NaCl solutions with concentrations of 3.5%, 4% and 5% were used as an artificial sea water corrosion medium and the temperature in the test chamber was maintained at 35 °C. Corrosion rate for 3.5% NaCl solution, 4% NaCl solution and 5% NaCl solution were 0.197 mm/year, 0.541 mm/year and 0.558 mm/year, respectively. The higher concentration leads to greater corrosion rate.