In this study, it is aimed to produce wood plastic composite material with eggshell additives and to investigate the mechanical properties of these materials. Mechanical properties such as tensile strength and modulus of elasticity, elongation at break, flexural strength and modulus of elasticity and impact resistance of new materials produced by adding eggshell to wood plastic composite at different rates were investigated. It was determined that tensile strength values gradually decreased due to the increase in the amount of eggshell in the composites produced. The modulus of elasticity of the composite material in tensile strength increases with the increase in the amount of eggshell in the mixture. With the increase of the eggshell ratio used, the elongation values of the plastic composite at break are reduced. The eggshell material used in wood plastic composite reduces the bending strength of the material. The eggshell reduces the modulus of elasticity of the composite material in bending. The eggshell composite material did not cause a significant change in impact resistance. [ABSTRACT FROM AUTHOR]

The use of different mineral material types and contents in medium density fiberboard (MDF) production was investigated. Three different minerals (sepiolite, dolomite, and perlite) and five different ratios (3%, 6%, 9%, 12%, and 15%) were used according to the oven-dry wood fiber weight. These minerals were homogeneously added as powder between the wood fibers. Some physical, mechanical, limit oxygen index (LOI), and thermogravimetric analysis (TGA) tests of the boards were conducted. The mineral fillers negatively affected the physical properties such as water absorption (WA), thickness swelling (ThS), and mechanical properties such as modulus of rupture (MOR), modulus of elasticity (MOE), and internal bond (IB). However, LOI and TGA test results showed a positive effect on combustion resistance depending on the type and rate of mineral fillers. [ABSTRACT FROM AUTHOR]

Textile (cotton) dust, which is harmful to humans and the environment, is one of the largest wastes in the textile industry. The aim of this study was to investigate the potential use of this waste in high value-added materials. Physical and mechanical properties and formaldehyde emissions of the three-layered particleboards with textile (cotton) dust in the middle layer were investigated in this study. A phenol formaldehyde resin was used as the binder in particleboard production. Four different amounts of textile dust (10%, 20%, 30%, and 40%) based on the oven-dried weight of the wood were obtained from a commercial textile manufacturer as industrial waste. The density, thickness swelling, modulus of rupture, modulus of elasticity, internal bond, and formaldehyde emissions of the produced panels were determined. The physical and mechanical properties and formaldehyde emissions of the particleboards were negatively affected, which decreased with the addition of a high amount of textile powder. At low rates, the use of textile dust in the middle layer did not significantly decrease the particleboard properties. Textile dust can be a partial solution for the raw material demand of the wood-based panel industry. [ABSTRACT FROM AUTHOR]