Abstract: The Mg/Al laminated composite was fabricated by the accumulative roll bonding (ARB) using the pure magnesium and Al5052 alloy at 400°C. Tensile properties along rolling direction and the transverse direction and the microhardness were evaluated at the ambient temperature. The tensile strength of the laminated Mg/Al composite along both directions increased gradually till two ARB cycles, but then decreased after the third ARB cycles. Optical microscopy and scanning electron microscopy (SEM) were utilized to reveal the microstructure evolution and the failure mechanism. Grain refinement of Mg layers was not obvious during the ARB process due to the high temperature and interval reheating. The obvious crack at the coarse intermetallic compounds and rupture of the Al layer after the third cycle led to the premature failure of the sample along the rolling direction during the tensile test. [Copyright &y& Elsevier]

In this study, both AZ91 alloy and nano-SiCp/AZ91 composite were subjected to multi-pass forging under varying passes and temperatures. The microstructure and mechanical properties of the alloy were compared with its composite. After six passes of multi-pass forging at a constant temperature of 400 ℃, complete recrystallization occurred in both the AZ91 alloy and composite. The decrease of temperature and the increase of passes for the multi-pass forging led to further refinement of dynamic recrystallized grains and dynamic precipitation of second phases. The grain size of the nano-SiCp/AZ91 composite was smaller than that of the AZ91 alloy under the same multi-pass forging condition, which indicated that the addition of SiC nanoparticles were beneficial to grain refinement by pinning the grain boundaries. The texture intensity for the 12 passes of multi-pass forging with varying temperatures was increased compared with that after nine passes. The ultimate tensile strength is slightly decreased while the yield strength was increased unobviously for the AZ91 alloy with the decrease of temperature and the increase of the passes for the multi-pass forging. Under the same condition of multi-pass forging, the yield strength of the composite was higher than that of the AZ91 alloy due to the Orowan strengthening effect and grain refinement strengthening resulting from externally applied SiC nanoparticles and internally precipitated second phases. By comparing the microstructure and mechanical properties between the AZ91 alloy and nano-SiCp/AZ91 composite, the strength-toughness properties of the composites at room temperature were affected by the matrix grain size, texture evolution, SiC nanoparticles distribution and the precipitated second phases. [ABSTRACT FROM AUTHOR]

Mg-10Zn-6Y-0.5Zr (wt%) alloy and Mg-10Zn-3Y-3Gd-0.5Zr (wt%) alloy with medium RE content have been fabricated by conventional casting and indirect extrusion. The as-extruded Mg-10Zn-6Y-0.5Zr (wt%) alloy shows a bimodal microstructure containing dynamic recrystallized (DRXed) grains with average grain size of 2 μm and deformed regions. In addition to the fragmented W phase particle bands distributing along the extrusion direction, large amount of nano W phase and small amount of nano β 2 ′ phase are precipitated in the matrix. While the as-extruded Mg-10Zn-3Y-3Gd-0.5Zr (wt%) alloy exhibits completely dynamic recrystallized microstructure with average grain size of 3 μm. The broken W phase particles are distributed homogeneously in the matrix. Icosahedral quasicrystal phase layer is observed at the surface of some W phase particles in the as-extruded Mg-10Zn-3Y-3Gd-0.5Zr alloy. The as-extruded Mg-10Zn-6Y-0.5Zr (wt%) alloy exhibits yield strength of 341 MPa, ultimate tensile strength of 368 MPa and elongation to failure of 6.8%. While the as-extruded Mg-10Zn-3Y-3Gd-0.5Zr (wt%) alloy shows lower yield strength of 247 MPa, ultimate tensile strength of 330 MPa and higher elongation to failure of 19.8%. The higher strength in the as-extruded Mg-10Zn-6Y-0.5Zr (wt%) alloy is mainly attributed to higher area fraction of unDRXed regions with strong texture and the precipitation of nano W and β 2 ′ phase. The fully recrystallized microstructure with weak texture and the formation of icosahedral quasicrystal phases with good coherent bond with α-Mg contribute to the good ductility of the as-extruded Mg-10Zn-3Y-3Gd-0.5Zr alloy. [ABSTRACT FROM AUTHOR]

In this study, low volume fraction SiCp/AZ91 magnesium matrix nanocomposites billets intended for structural applications were synthesized using semisolid stirring assisted ultrasonic vibration, leading to the dispersion of SiC nanoparticles. Both the AZ91 alloy and nanocomposite billets were then subjected to isothermal multidirectional forging (IMDF). Micrographic observations illustrated that the mean grain size of the developed nanocomposite showed an initial increase after 3 IMDF passes, followed by a decrease after 6 IMDF passes compared to the AZ91 alloy. This indicated that the effect of dispersed SiC nanoparticles on the inhibition of the dynamic recrystallization grains growth was impaired due to the present high IMDF temperature. The improved yield strength of the nanocomposite could be attributed to Orowan strengthening effect related to the dispersed SiC nanoparticles as well as the second phases precipitated far from the dynamic recrystallization grains. [ABSTRACT FROM AUTHOR]

AZ91 alloy was subjected to multidirectional forging (MDF) and the relationship between microstructures and mechanical properties generated by MDF were investigated. The results showed that after 1 MDF pass grain size of the alloy decreased compared with as-cast alloy, and the amount of recrystallization grains increased when the MDF temperature increased from 250 °C to 400 °C. With increasing the MDF passes at 350 °C, grains of the alloy were gradually refined. A typical basal texture was obtained after 1 MDF pass, and then the basal pole scattered with the increase of MDF passes. Mg 17 Al 12 phases were precipitated along grain boundaries during MDF, which could hinder the growth of recrystallization grains. Both tensile strength and elongation to failure of the alloy were significantly enhanced till 3 MDF passes with increasing the MDF passes. [ABSTRACT FROM AUTHOR]

The present study dealt with the AZ91 alloy subjected to multidirectional forging (MDF) under decreasing temperature conditions with emphasizing on relationship between microstructures and mechanical properties generated by MDF. The obtained results showed that grains of the alloy were gradually refined while the amount of the second phase precipitated along the grain boundaries was increased with increasing the MDF passes and decreasing the MDF temperature. Compared with the as-cast alloy, yield strength, ultimate tensile strength and elongation of the AZ91 alloy after MDF under decreasing temperature conditions were simultaneously increased. As the numbers of MDF passes were gradually increased and the MDF temperature was gradually decreased, the yield strength was gradually decreased, suggesting that texture softening may overwhelm the strengthening due to the grain refinement as well as the homogeneous distribution of precipitates. [ABSTRACT FROM AUTHOR]

The hardness, tensile ductility and fatigue lifetime of nanostructured (NC) Cu-Zr alloyed thin films have been systematically measured at different Zr additions (0, 0.5, 2.0, 4.0, 8.0at.%). Experimental results showed that the Cu-0.5at.% Zr film exhibited the highest hardness, largest ductility and longest fatigue lifetime, which are increased by 120%, 80%, and above an order of magnitude, respectively, in comparison with its pure Cu counterpart. The simultaneous improvements of mechanical properties are rationalized with respect to microstructural evolutions related to Zr segregation at grain boundaries (GBs). Besides refinement in NC grains and enhancement in nanotwins, grain orientation was apparently modified by the GB Zr segregation. (110) grains were promoted and layer-like microstructure was formed with coexistence of three orientation of grains at the upper layer, facilitating Cu grain growth at room temperature. GB doping strengthening worked as an additional strengthening mechanism and mechanically driven grain growth became the predominant deformation mechanism and fatigue mechanism, which accounted for the optimal combination of mechanical properties achieved in the Cu-0.5at.% Zr film. When the Zr content was >2.0at.%, however, amorphous phases were formed at the GBs due to locally increased Zr concentration. The GB doping strengthening effect was concomitantly weakened and strength was gradually decreased. In addition, stress/strain localization occurred readily at the amorphous phase regions, triggering intergranular fracture and reducing ductility. During cyclic testing in the low stress range, GB amorphous phases strengthened rather impaired the GBs, which gave the Cu-Zr films a fatigue lifetime greater than that of the pure NC Cu film. The present results clearly indicate that, once solute content is suitably explored, the solute segregation at GBs in NC metals can not only retain NC grains in loading-free conditions, but also impart enhanced mechanical properties when exposed to applied stress. [ABSTRACT FROM AUTHOR]

Highlights: [•] The solidification rates significantly affect the CNTs distribution. [•] Uniform CNTs distribution was achieved in the composites. [•] The tensile properties of the composites follow the Kelly–Tyson formula well. [Copyright &y& Elsevier]

Highlights: [•] Bimodal size SiCp/AZ31B composites were fabricated. [•] The influence of bimodal size SiCp for matrix alloy was determined. [•] Mechanical properties of bimodal size SiCp/AZ31B composite were enhanced significantly. [ABSTRACT FROM AUTHOR]

The Mg–4.50Zn–1.13Ca (wt%) alloy was subjected to double extrusion, and the microstructure and mechanical properties of the extruded alloys were investigated. Double extrusion refined the microstructure significantly, resulting in the enhancement of mechanical properties of the double-extruded alloys compared with the single-extruded alloy. The yield strength of the single-extruded alloy was 173MPa, while the value was increased to 320MPa and 370MPa after subsequent second extrusion at 300°C and 250°C, respectively. The second extrusion ratio had little effect on the microstructure and mechanical properties of the double-extruded alloys, while grain size was decreased and strength was increased with the decrease of double extrusion temperature. The double-extruded Mg–Zn–Ca alloy exhibited superior elevated temperature mechanical properties, which was attributed to the fine stable Ca2Mg6Zn3 intermetallic compound particles dispersed in the alloy. [ABSTRACT FROM AUTHOR]

Abstract: Ultra high-strength Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy sheet was prepared by large-strain hot rolling and subsequent ageing process. The sheet exhibits excellent tensile properties at ambient temperature with ultimate tensile strength of 517MPa, 0.2% proof stress of 426MPa and elongation to failure of 4.5%. The notable improvement in strength is attributed to the dense distribution of the fine precipitates inside the grains, scattered precipitates at the grain boundaries, bimodal grain size distribution with fine recrystallized grains and large deformed grains with intense basal texture. [Copyright &y& Elsevier]

Abstract: Plasma sprayed hydroxyapatite (HA) coatings on titanium alloy substrate have been used extensively due to their excellent biocompatibility and osteoconductivity. However, the influence of the high temperature process on substrates can not to be ignored, especially for metastable β type titanium alloy substrates. In this paper, martensitic transformation and recrystallization occurred in near surface of the low-modulus Ti-24Nb-4Zr-7.9Sn alloy substrate after application of a HA coating. Various analyses revealed that the martensitic transformation and recrystallization were mainly related to the high temperature and cooling process. The different microstructures can be attributed to inhomogeneous temperature and cooling rate distributions in the substrate. Corresponding to the microstructure, the Young''s modulus and micro-hardness of the near surface of the alloy showed a similar graded distribution along the direction perpendicular to the coating/substrate interface. In addition, the martensitic transformation and recrystallization caused remarkable changes of the entire alloy. [Copyright &y& Elsevier]