Solid Oxide Fuel Cells (SOFCs) are a promising technology that can provide efficient and clean energy production. The general barriers hindering their market entry are durability, i.e. resistance to aging, and costs. In parallel to the deeper insight into the different degradation sources and improved understanding of ageing factors and their interactions, work towards higher accuracy for the assessment and monitoring of real-world fuel cell ageing in necessary. The requirements for operational stability formulate the parameter “degradation rate” (DR). Most often long term durability tests are performed at constant current load and the decrease of the voltage is used for its definition. In this work a new approach based on analysis of the volt-ampere characteristics, named Differential Resistance Analysis (DRA), is presented. It operates with the differential resistance, i.e. with the derivative of the voltage in respect to the current (dU/dI = Rd) which is more sensitive to small deviations and thus increases the sensitivity of the analysis. Two performance indicators are derived (Rd, min and ∆U*) with differing selectivity: ∆U* is more sensitive to activation losses and Rd, min - to transport hindrances. The application of the DRA is demonstrated on examples from measurements in fuel cell and in reverse (fuel cell/electrolyzer) mode, as well as on modeling data. The results show that the method is at least 10 times more sensitive to DR evaluation in comparison with the classical approach.

International audience; This study aims at understanding the structural changes occurring in the carbonaceous matrix of wood-based chars during their thermal conversion. Although chars are routinely characterized by porosity measurements or scanning electron microscopy, the composition and structure of the carbonaceous matrix is often not investigated. Here, advanced characterization using X-ray synchrotron microtomography, transmission electron microscopy, Raman spectroscopy and X-ray diffraction provided a precise description of the char properties, allowing for an accurate discussion of their catalytic properties. Two chars were produced by slow pyrolysis of wood waste (400 and 700 °C) and a third one was fabricated by activation under steam at 850 °C of the char obtained at 700 °C. The results show that the pyrolysis temperature and the activation performed did not affect the macrostructure of the chars and that the pores were interconnected at the macroscopic scale. However, at 700 °C, the micro- and nanostructures were modified: short-range organized graphene fringes were observed. The activated char showed a homogeneous microstructure similar to that of its precursor. Besides, the ratio of graphene-like structures, the local organization of graphene sheets, and the imperfections in graphene-like sheets were clearly improved by the post-treatment. To our knowledge, this is the first time that such an approach, combining various tools, is applied for the study of pyrolysis chars.

Steam electrolysis by means of reversible Fuel Cells is a promising concept for compensating the intermittency of renewable energy sources. Several tests on SOFC stacks operated in reverse mode (SOEC) reported faster degradation than in power production mode. Although not completely clarified, the degradation mechanisms appear partly related to the higher steam concentration at the electrode compartments. This work introduces a novel type of cell with dual anionic-protonic conductivity, which allows the separation of the steam compartment from the electrodes compartments. The concept is presented together with a set of experimental results pointing out the potential advantages of this approach. © The Electrochemical Society.

International audience; Novel ionic conductors were prepared by substituting Ca2+ and Sr2+ for Gd3+ in Gd3GaO6. A microwave-assisted combustion technique was used to synthesize these compounds at 900 °C. SEM observations showed that both substituents promote grain growth during sintering. XRD proved that the Gd3-x(Ca,Sr)xGaO6-x/2 solid solutions are formed up to x = 0.10. Below 600 °C, the level of conductivity under wet Ar is higher than that of measured under dry atmospheres, thereby demonstrating the contribution of proton defects to the overall conductivity. The highest level of proton conduction, i.e. σ600°C = 1 × 10−3 S cm−1, was measured for Gd2.9Sr0.1GaO5.95 at 600 °C in wet Ar. At higher temperatures, only oxygen ions contribute to the conductivity. At 800 °C, a total oxide-ion conductivity of σ800°C = 1 × 10−2 S cm−1 was measured for the highest substitution level, i.e. x = 0.10. In both temperature ranges, activation energy associated with ionic transport decreases with the Me content as a result of an increase in grain size. Stability tests were successfully achieved as the structure of materials remains unchanged after different treatment under severe conditions. Conductivity measurements under varying oxygen partial pressures demonstrated that materials are purely oxide-ion conductors up to pO2 = 1 × 10−5 atm. At higher pO2, a p-type contribution appears.

International audience; Images of a hematite-based epoxy coating are obtained by scanning electron microscopy (SEM). At the scale of a few micrometers, they show aggregates of hematite nano-particles organized along thin curved channels. We first segment the images and analyze them using mathematical morphology. The heterogeneous dispersion of particles is quantified using the correlation function and the granulometry of the embedding (epoxy) phase. Second, a two-scales, 3D random microstructure model with exclusion zones is proposed to simulate the spatial distribution of particles. This simple model is parametrized by four geometrical parameters related to the exclusion zones solely. The microstructure is numerically optimized, in the space of morphological parameters, on the granulometry of the embedding epoxy phase and on the microstructure correlation function, by standard gradient-descent methods. Excellent agreement is found between the SEM images and our optimized model. Finally, the size of the representative volume element associated to the optimized microstructure model is compared with that of the SEM images.

In the high current density regime, the performance of SOFCs is limited by concentration overpotentials, which are particularly significant at the anode side where a competition occurs between incoming hydrogen and outgoing water. In standard SOFCs where the anode is made of YSZ and Ni, this becomes crucial when the demand for reactants exceeds the capacity of the porous cermet anode to supply them by gas diffusion mechanisms. A delicate compromise should be found between maintaining a high level of activation in the anode, i.e. high density of triple phase boundaries (TPB), favored by a distribution of small interconnected pores with high tortuosity and small grains size, and high gas permeability, favored by a distribution of large interconnected pores with low tortuosity, while the percolation of both electronic and anionic conductivity phases is maintained. The present work aims at determining experimentally anodes gas permeability as a function of the experimentally determined percolation, tortuosity and volume fraction of the pores, assuming that the diffusion of gases is described by the Darcy Law. Anodes with varying porosity ensured by different quantities of the pore former were obtained by cold pressing and sintering. SEM image analysis, mercury intrusion porosimetry and permeability measurements for different gases were performed. The obtained results show that permeability increases with the volume fraction of the pore former. However, non-linearity as a function of the gases molecular weight is observed and discussed as a function of the mean free path and thus of possible mixed Darcy and Knudsen diffusion.

The route for the increase in SOFC performances is many-fold: i/ in the low current density domain, through the enhancement of the catalytic properties of the electrodes, i.e. via a higher Triple Phase Boundary (TPB) density, hence a higher exchange current and a lower activation overpotential, ii/ in the ohmic loss region, through lower resistance, i.e. via thickness reduction, materials with a higher conductivity, iii/ in the high current density region, via the optimization of the electrodes microstructure, i.e. the control of the porosity, of the tortuosity and percolation of phases. Taking ideas from the batteries community, where the conceptual design of electrodes is much more mature, the present work proposes to explore how the corrugation of electrode/electrolyte interfaces impacts the performances. This approach was applied to the anode/electrolyte interface of a SOFC based on standard compositions, YSZ (or YDC) for the electrolyte, and YSZ (or YDC) + nickel for the anode. The corrugation of surfaces was obtained through the patterning of this interface with different geometries (flat, pyramids, shallow and deep ellipsoids) at the 10-100 µm scale by cold pressing, templating or serigraphy. Thin electrolyte layers have been deposited on top of these architectures by Atomic Layer Deposition (ALD). In parallel, an electrochemical model was carried out and implemented by considering masses and charges conservation, gas transport and electrochemical reaction kinetics throughout the interface in FEM (finite element method) with COMSOL Multiphysics. The results showed a 25 % increase in the total current density for a certain ellipsoid geometry.

International audience; The oxide-ion and proton conduction properties of RE3NbO7 (RE = La, Gd, Y, Yb, Lu) compounds were investigated. For the bigger rare-earth cation, i.e. La3+, the compound crystallises in a weberite-type structure and the oxide-ion conductivity is low owing to the lack of intrinsic oxygen vacancies. Consequently, the resultant proton incorporation and conductivity in La3NbO7 are also low. For small rare-earth cations, i.e. from Gd3+ to Lu3+ and for RE = Y, materials adopt a fluorite-like structure confirmed from X-ray powder diffraction. In this latter case, materials include intrinsic oxygen vacancies leading to a higher oxygen conductivity. For these compounds, a proton incorporation takes place at low temperature under wet conditions giving rise to proton conductivity. Nevertheless, both oxygen and proton conductivities are low in these materials, which can be explained by the ordering of oxygen vacancies observed by Transmission Electron Microscopy.

International audience; Recently a new design of solid oxide fuel cell (SOFC) named dual membrane fuel cell (dmFC) has been introduced and proved. It is based on the introduction of three independent compartments for hydrogen, oxygen and water, which eliminate the dilution of the fuel or the oxidizer respectively in the SOFC construction or in its proton conducting (pSOFC) modification. Due to the registered sufficient mixed ionic conductivity of BaCe0.85Y0.15O2.925 (BCY15), a simplified modification in respect to shaping technology and construction is introduced. It's performance is better than the one of pSOFC cell produced with the same material and shaping procedure: 76 mW/cm2 (dmFC thickness 1.1 mm) against 71 mW/cm2 (pSOFC thickness 0.66 mm) at 700 °C. Impedance measurements carried out down to 1 mHz ensure information about the water formation and behaviour in the separate central membrane compartment of the dmFC design, which brings to performance improvements, registered also in electrolyser mode of operation.

International audience; In-substituted BaSnO 3 (BaSn 1Àx In x O 3Àδ , x ¼ 0:125, 0.25 and 0.50) compounds were prepared by a gel polymerization method. Their microstructure, hydration energy and electrical properties were investigated. Single phases were confirmed by X-ray dif-fraction analysis over the whole range of substitution, and were identified as cubic perovskite-like structure. The grain size and conductivities of samples measured under dry and wet atmospheres increase significantly with indium content as such, 1À2 μm for BaSn 0:875 In 0:125 O 3Àδ (x ¼ 0:125) and 20 μm for BaSn 0:50 In 0:50 O 3Àδ (x ¼ 0.50). The highest proton conductivity at 600 ○ C, ¼ 9:5 Â 10 À4 SÁcm À1 , is obtained for BaSn 0:5 In 0:5 O 2:75 (x ¼ 0:50). Barium stannates with chemical formula derived from BaSnO 3 has recently been proposed as protonic conductors with potential applications in fuel cells. 1À6 It was shown that Y-substituted BaSnO 3 materials exhibit high proton conductivity in wet atmospheres. 5,6 Nevertheless, barium stannate based compounds exhibit a strong aversion against densification, i.e. the relative density reaches only about 90% with difficulty although sintered at 1600 ○ C for 12 h. 5,6 Such a high sintering temperature possibly results in barium volatilization leading to the decrease of proton conductivity, and also makes this oxide difficult to integrate electrochemical devices. 7,8 In the literature, the In element has received much less attention than the rare earth elements as a substituant for proton-conducting perovskites. 9À21 Matsumoto et al. 22 reported that electrical performances of BaCe 0:90 In 0:10 O 3Àδ are much more lower than those of the counterparts substituted with other trivalent dopants (Y, Tm, Yb and Sc). Zhang et al. 20 pointed out that the proton concentration and electrical properties of BaCe 0:80Àx Sm 0:20 In x O 3Àδ decrease when the indium content increases. However, Giannici et al. 21 reported that a high content of vacancies can be created by the substitution of Sn 4þ for In 3þ in BaSnO 3. Shober et al. 2 also point out that BaSn 0:5 In 0:5 O 2:75 (x ¼ 0:50) go along with high proton defects, then exhibits a high level of grain conductivity, nevertheless it is relatively unstable in severe reducing atmospheres. The literature showed that in substitution in BaCeO 3 plays a beneficial role on the stability and sinterability of proton-conducting perovskites in CO 2 atmosphere. 9,20 Moreover, indium as a second substituent improve the sinterability of BaZr 0:9 Y 0:1 O 3Àδ while yttrium enhance the proton conductivity. 18 In this paper, the effect of the substitution of Sn 4þ for In 3þ in BaSnO 3 on the micro-structure, water hydration and electrical properties has been investigated. BaSn 1Àx In x O 3Àδ (denoted x ¼ 0:125, 0.25 and 0.50 as BSIn125, BSIn25 and BSIn50 in the following) powders have been synthesized by a gel polymerization route from an aqueous solution containing cation salts. 5,6,23 The resultant precursors were heat-treated at 1200 ○ C for 4 h to obtain §

In this study, the synthesis, structural and electrical properties of BaSn 0.75 M 0.25 O 3− δ (M = Fe, Sc, In, Y, Gd, Sm, Nd and La) compounds have been investigated. Single phase powders of these materials were successfully synthesized by a gel polymerization route and sintered to obtain dense pellets. X-ray diffraction reveals that all compounds crystallise in a cubic perovskite like-structure (space group: Pm 3 ¯ m ) at room temperature. However, cell parameters of the substituted compounds do not evolve in accordance with the substituent radius, i.e. an abnormal drop was observed for elements with a large radius, i.e. Sm, Nd and La. A possible interpretation could be the partial incorporation of substituents into the Ba-site. The site incorporation selectivity of substituents into the Ba- and Sn-sites was investigated based on the study of lattice parameters and empirical defect models. Experiments show that the thermal expansion coefficients and electrical properties have no specific correlation with the nature of the substituent.

International audience; The effects of ZnO additive on the phase formation, microstructure and electrical conduction of Y-doped BaSnO3 have been investigated. The single-phase and dense BaSn0.75Y0.25O3−δ compound with 4 mol% ZnO additive was successfully prepared after sintering at 1300 °C, which significantly reduces the sintering temperature. The conductivities measured under dry and wet air atmospheres reveal that the bulk conductivity of BaSn0.71Y0.25Zn0.04O3−δ is much lower than that of BaSn0.75Y0.25O3−δ. However, ZnO as a sintering aid does not affect the bulk conductivity. The total conductivity of BaSn0.75Y0.25O3−δ with ZnO as the sintering aid is slightly higher than that of unmodified BaSn0.75Y0.25O3−δ, and reaches 2.4 × 10−3 S cm−1 at 621 °C. Therefore, this material can be used as a proton-conducting electrolyte for intermediate temperature solid oxide fuel cells.

This paper presents results for the conductivity of BaCe0.85Y0.15O2-δ (BCY15) measured by electrochemical impedance spectroscopy in wet hydrogen and in Air, as well as test results from the application of the material in a new dual membrane fuel cell configuration (“IDEAL Cell”), in which the water is produced and evacuated through a separate chamber. The conductivity of dense BCY15 in wet hydrogen atmosphere at 700 °C is 2.0 10-2 S/cm. The measured values in air are of the same order. Preliminary tests of the material in the new cell design, where the three types of conductivity (protonic, oxide ion and mixed) are used in different cell compartments, are successfully performed.

International audience; Ba2SnYO5.5 nanopowders were synthesized by a gel polymerization method. In this process, a gel containing Ba, Sn and Y cations has been obtained by the polymerization of acrylic acid using N,N′-methylene bis-acrylamide as a cross-linking reagent and hydrogen peroxide as an igniting reagent. The gel was calcined at 1200 °C, giving rise to the Ba2SnYO5.5 single-phase nanopowders with the grain size ranging from 50 nm to 70 nm. Nanopowders were sintered at 1150 °C by spark plasma sintering (SPS) to obtain dense nanostructure materials (> 95%) containing grains whose size ranges between 70 nm and 100 nm. Nanostructured Ba2SnYO5.5 shows a good chemical stability in wet atmosphere. However, its protonic conductivity decreases compared with that of microcrystallin Ba2SnYO5.5 ceramics.

IDEAL-Cell is a new concept of a high temperature fuel cell operating in the range 600-700 °C. It is based on the junction between the anode part of a PCFC and the cathode part of a SOFC through a mixed H+ and O2- conducting porous ceramic membrane. This concept, extensively described in the present paper, aims at avoiding all the severe pitfalls connected with the presence of water at the electrodes in both SOFC and PCFC concepts. Spark Plasma Sintering samples were designed specifically for proving the IDEAL-Cell concept. The first electrochemical results obtained at 600 °C under hydrogen on millimeter thick samples show that IDEAL-Cell behaves like a high temperature fuel cell. It is estimated that the overall efficiency of this new concept should greatly surpass that of standard SOFCs and PCFCs and that the material constraints, especially in the case of interconnect materials, should significantly decrease.

International audience; Atomistic simulations have been used to investigate energetic aspects of defects in pure and doped BaSnO3, in close comparison with experimental data. Semiempirical potentials were used to determine the solution energies of trivalent cation on either A or B site of the perovskite structure. Density functional theory calculations were also performed to gain further insight into the redox properties of this material. Both approaches give a complete view of the way doping atoms will be inserted inside the BaSnO3 structure. For instance, we calculated with good precision the evolution of cell parameters with dopant nature and concentration. Then, by taking into account dopant vacancy interactions, we also show that the oxygen vacancy preferentially locates close to the dopant in the case of small size dopant while stays at the second neighbor position in the case of bigger dopant. These calculations also show that In and Y are the dopants giving the most homogeneous energetic map for oxygen vacancy movements and might thus be anticipated as the best acceptor-like dopants for enhanced anion conduction properties. Finally, we calculated an oxygen ion migration activation energy of 0.65 eV.

International audience; This work explores experimental procedures for tape-cast proton conducting ceramic fuel cells (PCFC) based on Yttrium-doped Barium Cerate (BCY10). The work is based on several years experience on aqueous tape-casting applied to the shaping of YSZ-based SOFC: however, water-based tape casting of BCY10 appeared to be impracticable for reasons associated with the high basicity of this material that results in rapid hydrolysis when in contact with water. Organic tape casting was therefore developed for BCY10, but only on Electrolyte (BCY10)/Anode (BCY10 + NiO) half cells since up to now no cathode material is available. Planar 20 mm diameter circular half-cells were obtained with the aid of a small load on top of the bi-layer to counterbalance the inevitable warping of the samples. Back-scattered SEM and X-Ray computer-controlled microtomography showed sedimentation of some large grains in the green tapes which are believed to have formed by a mechanism associated with a porosity gradient. The deformation occurring during sintering was modelled taking into account the elastic, thermal, viscoplastic and sintering components of the total deformation. 2D and 3D Finite Element numerical simulations showed that the driving force for deformation is associated with this porosity gradient.

Oxy-apatite materials La 9.33 + x Si 6 O 26 + 3 x /2 are thought as zirconia-substitutes in Solid Oxide Fuel Cells due to their fast ionic conduction. However, the well-known difficulties related to their densification prevent them from being used as such. This paper presents strategies to obtain oxy-apatite dense materials. First, freeze-drying has been optimized to obtain ultrafine and very homogeneous La 9.33 + x Si 6 O 26 + 3 x /2 (0 ≤ x ≤ 0.67) nanopowders. From these powders, conventional and Spark Plasma Sintering (SPS) have been used leading to very dense samples obtained at temperatures rather lower than those previously reported. For instance, SPS has allowed to prepare fully dense and transparent ceramics from 1200 °C under 100 MPa. The microstructure and transport properties of such samples have been then evaluated as a function of sintering conditions and lanthanum content. It will be show that for lanthanum content higher than 9.60 per unit formula, the parasitic phase La 2 SiO 5 appears leading to a degradation of conduction properties. We also show that grain boundaries and porosity (for conventionally-sintered materials) seem to have blocking effects on oxygen transport. The highest overall conductivity values at 700 °C, i.e. σ 700 °C = 7.33.10 − 3 S cm − 1 , were measured for La 9.33 Si 6 O 26 material conventionally-sintered at 1500 °C which contains bigger grains' size by comparison with σ 700 °C = 4.77.10 − 3 S cm − 1 for SPS-sintered materials at the same temperature but for few minutes. These values are associated with activation energies close to 0.83–0.91 eV, regardless of sintering condition, which are commonly encountered for anionic conductivity into such materials.

Lanthanum silicate oxyapatites, ion-conducting materials presenting a strong aversion against densification, have been obtained in the form of dense transparent ceramics, by combining the beneficial use of freeze-drying and spark plasma sintering methods.

The EVOLVE cell, named after a running FP7 project, is an innovative SOFC concept that integrates advanced materials, providing multiple functionalities (electrochemical activity, ion or/and electron conduction, gas diffusion…), and an inventive anode current collector made of a NiCrAl preoxidized foam impregnated with a conductive perovskite. Therefore, this anode combines the beneficial characteristics of MSC and ASC technologies, and strong improvements in terms of reliability and durability (inter-diffusion, Ni coarsening and agglomeration, sulphur tolerance, mechanical robustness and chemical stability under redox cycling in temperature) are expected. In order to enhance the electrode efficiency, the 3D microstructure needs to be precisely described at the microscopic scale by a morphology model. An optimized microstructure (controlled pores size, morphology and connectivity, grains size distribution, 3D tortuosity and 3D percolation of phases, volume fraction of phases, final thickness of components …) is closely related to the starting parameters (nature and quantity of starting powder, binder, shaping aids…) and to the control of the shaping process parameters (sintering treatment and atmosphere). It should meet the best compromise between a good electrocatalytic activity and a low ohmic resistivity while ensuring a stisfactory long term thermomechanical stability on the life time of the device. Based on a mathematical morphology approach applied on symmetrical LST/CGO anode layers, the present work aims at showing how a morphology model can be establised and 3D microstructural data relevant for shaping and performances can be derived from back-scattered electrons (BSE) SEM observations. For each sample, a series of images were used as input information for the microstructural modelling. All the original images were first filtered to remove the noise, thresholded and finally a series of morphological operators (openings, surface openings, closings and reconstruction with markers) were applied to remove artefacts. A 3D pluri-Gaussian model has been generated from 2D images, and then computed to predict volume fraction of the 3 phases, 3D tortuosity, gas permeation and ionic conductivities. These results were used for the optimization of the shaping process that includes the integration of the metal foam.

7 pages; International audience; New oxygen ion conductors have been prepared by substituting Ga3+ for Ge4+ in Nd4GeO8, Zn2+ and Mg2+ for Ga3+ in Nd3GaO6, and Ca2+ and Sr2+ for Nd3+ in Nd3GaO6. A combustion technique using ethylenediamine tetraacetic acid has been developed to synthesize these materials at ~900 C, leading to powders with spherical particles of about 100-200 nm. The green pellets obtained through the combustion-synthesized powders could be sintered to ~98% at 1250 C. It was found that Nd4Ge1-xGaxO8-x/2 are formed up to x = 0.10, Nd3Ga1-xMxO6-x/2 (M = Zn, Mg) up to x = 0.03, and Nd3(1-x)M'3xGaO6-3x/2 up to x = 0.03 and 0.015 for M' = Ca and Sr, respectively. These relatively small substitution rates induce a significant increase in oxygen ion conductivity (800C = 0.2 × 10-2 S cm-1 for Nd4Ge0.9Ga0.1O7.95; 800C = 0.5 × 10-2 and 0.4 × 10-2 S cm-1 for Nd3Ga0.97M0.03O5.985 with M = Zn and Mg, respectively, and 800C = 0.6 × 10-2 and 0.7 × 10-2 S cm-1 for Nd2.91Ca0.09GaO5.955 and Nd2.955Sr0.045GaO5.9775, respectively) with respect to pure Nd4GeO8 (800C = 2.8 × 10-4 S cm-1) and pure Nd3GaO6 (800C = 2.7 × 10-4 S cm-1).

The structural, dynamical and dielectric properties of the cubic phase of perovskite barium stannate BaSnO3, a potential candidate as protonic conductor for solid oxide fuel cells, have been investigated by the means of first-principles density functional calculations, and the structural and electrical properties have been explored at low temperature. From density functional perturbative calculations, the phonon modes, the Born effective charges and the dielectric tensor are derived and analyzed, at zero pressure. The phonon band-structure of the cubic phase does not exhibit unstable modes, in good agreement with x-ray diffraction, which shows that BaSnO3 remains perfectly cubic down to 10 K. The dielectric response in BaSnO3 as measured and calculated is lower than in titanate and zirconate perovskites.

This work is dedicated to the development of a numerical model to optimize the anodeelectrolyte interface geometry for improving the electrochemical performance of a SOFC cell in a 3- Dimensional SOFC simulation process. A SOFC repeated unit composed of anode, electrolyte and cathode is taken as a modeling target. The model is implemented by considering electron and ions conservation, gas transport and electrochemical reaction kinetics in FEM (finite element method) software COMSOL Multiphysics. Four different interface geometries—flat, pyramid, ellipsoid and cube, which are predicted to show better electrochemical performance due to increased TPBs and less activation resistance, are investigated to find the best morphology according to their simulated performance. Results reveal that the cubic interface case achieves the highest current density at fixed 0.7V cell operating voltage, 63.55% higher than the flat reference interface. Distribution of different electrochemical variables is also obtained in each condition, giving valuable information for further optimization.