The intercritical annealing and isothermal bainitic processing response was studied for three Nb and V microalloyed Transformation-Induced Plasticity (TRIP)-assisted 980 MPa grade steels. Their mechanical and microstructural properties were compared to industrially produced TRIP 800 steel. Depending on the isothermal holding temperature and microalloying, the experimental steels reached properties comparable to the reference steel. The retained austenite content did not show direct correlation to elongation properties. Niobium was found to be more effective microalloying element than vanadium in increasing the elongation properties, which were investigated by measuring true fracture strain from tensile test specimens. [ABSTRACT FROM AUTHOR]

The quenching and partitioning response following intercritical annealing was investigated for three lean TRIP-type high-Al steel compositions. Depending on the intercritical austenite fraction following annealing, the steels assumed either a ferrite/martensite/retained austenite microstructure or a multiphase structure with ferritic, bainitic and martensitic constituents along with retained austenite. The amount of retained austenite was found to correlate with the initial quench temperature and, depending on the intercritical annealing condition prior to initial quenching, with the uniform and ultimate elongations measured in tensile testing. [ABSTRACT FROM AUTHOR]