Magnetic anisotropy strongly influences the performance of the magnetocaloric effect. We investigated the magnetocaloric properties of the NdAlGe single crystal with I41md structure. The temperature-dependent magnetization revealed significant anisotropic properties; stable antiferromagnetic transition at TN = 6 K for H//a and meta-magnetic spin reorientation at low temperature (T ≤ 5 K) within an intermediate field (H = 2 T) for H//c. During the metamagnetic spin reorientation, the abrupt change of the magnetic entropy leads to a significant magnetocaloric effect with negative magnetic entropy change (∆SM) by −13.80 J kg−1 K−1 at TC = 5.5 K for H = 5 T along the H//c axis. In addition, the antiferromagnetic state for H//a shows the inverse magnetocaloric effect(I-MCE) by positive entropy change ∆SM = 2.64 J kg−1 K−1 at TN = 6 K for H = 5 T. This giant MCE accompanied by the metamagnetic transition resulted in a significantly large relative cooling power (158 J/kg at H = 5 T) for H//c. The giant MCE and I-MCE can be applied to the rotational magnetocaloric effect (R-MCE) depending on the crystal orientations. NdAlGe exhibits rotational entropy change ∆Sc−a = −12.85 J kg−1 K at Tpeak = 7.5 K, H = 5 T. With comparison to conventional MCE materials, NdAlGe is suggested as promising candidate of R-MCE, which is a novel type of magnetic refrigeration system. [ABSTRACT FROM AUTHOR]

The giant magnetocaloric effect Gd5Si2Ge2 alloy was prepared with 99wt% low purity commercial Gd. Powder XRD and magnetic measurements showed that the Gd5Si2Ge2 alloy annealed at 1200°C for 1 h had a significant magnetic- crystallographic first order phase transition at about 270 K. The maximal magnetic entropy change is 17.55 J · kg-1 · K-1 under a magnetic field change of 0-5 T. The distinct increase of magnetic entropy change belongs to the first-order phase transition from the orthorhombic Gd5Si4-type to the monoclinic Gd5Si2Ge2-type after high temperature heat-treatment. [ABSTRACT FROM AUTHOR]