Search

Abstract: The microstructures and mechanical properties of Mg–5.3Zn–0.2Ca–0.5Ce (wt%) alloy fabricated by semi-continuous casting were investigated. The as-cast alloy consists of α-Mg, Ca2Mg6Zn3 and T′1 phase with orthorhombic structure (a=0.57nm, b=0.75nm and c=1.00nm). T′1 phase mainly distributes at the triple conjunctions while the Ca2Mg6Zn3 at the grain boundaries. The as-cast alloy exhibits high strength retention due to the stable Ca2Mg6Zn3 and T′1 phase at the grain boundaries. [Copyright &y& Elsevier]

Abstract: A large Mg-4.50Zn-1.13Ca (wt%) alloy ingot 350mm in diameter and 1730mm long was successfully fabricated by semi-continuous casting. The microstructures and mechanical properties of the as-cast and as-extruded alloys were investigated. The as-cast alloy exhibits uniform chemical composition and microstructure from the centre to the surface of the ingot and mainly consists of α-Mg and Ca2Mg6Zn3. The coarse grains and network-like second phases that are distributed at the grain boundaries result in poor mechanical properties for the as-cast alloy. The mechanical properties of the as-extruded alloys are significantly enhanced. The high yield strengths of the as-extruded alloys mainly result from the fine DRXed grain and the stronger basal texture. [Copyright &y& Elsevier]

Abstract: Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy ingot with diameter of 280mm and length of 2940mm was successfully fabricated by semi-continuous casting. The microstructure and mechanical properties of the large ingot at different locations were investigated. The concentration of the RE and Zn elements distributed almost homogeneously through the whole alloy ingot. The average grain size decreased from the center to the surface of the alloy ingot, while the strength and ductility were improved gradually. The main eutectic compounds located at the grain boundaries were (Mg,Zn)3(Gd,Y) phase, adjacent to these eutectic compounds the 14H-type long period stacking ordered (LPSO) phase formed. Furthermore, some block-shaped Mg24(Gd,Y)5 phase and isolated Zr cores can be recognized in the interior of the grains. [Copyright &y& Elsevier]

Abstract: In this research, the as-cast and as-homogenized Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy were subjected to the hot rolling with the same processing parameters. The microstructure and mechanical properties of the two kinds of as-rolled sheets were investigated. The sheet rolled from the as-cast alloy was mainly composed of recrystallized α-Mg grains surrounded by Mg3(Gd,Y) eutectic compounds. While the sheet rolled from the as-homogenized alloy was composed of large deformed grains with long-period stacking ordered (LPSO) phase inside and fewer recrystallized α-Mg grains, and exhibited higher strength due to the deformed grains with stronger basal texture and larger volume fraction of long-period stacking ordered (LPSO) phase. [Copyright &y& Elsevier]

Abstract: Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy sheets containing long period stacking ordered (LPSO) phase were prepared by hot rolling at 400°C with total reduction of 96%. Microstructure evolution of the sheets during hot rolling was investigated, and its influence on mechanical properties was discussed. Twinning occurred during the early stage of hot rolling, and disappeared after total reduction higher than 89%. Average grain size was gradually refined, microstructure became much more homogeneous and volume fraction of LPSO phase decreased with increasing rolling reduction. Furthermore, the type of LPSO phases far from and near the block shaped phases were identified to be different. Basal texture was obtained during rolling process, but the intensity declined with the further rolling, which is mainly due to the dynamic recrystallization and the addition of RE elements. The as-rolled sheet with 96% reduction shows excellent mechanical properties: yield strength of 318MPa, ultimate tensile strength of 403MPa and elongation to failure of 13.7% at ambient temperature along the rolling direction. [Copyright &y& Elsevier]