Beech wood has a high frequency of defects such as red heartwood, reaction wood (tension wood). For the experimental measurements four logs without visible defects like red heartwood, which can noticeably affects the measurements' results were qualified. The drying medium temperature in the first phase of the process before the moisture content of the specimens fell below the FSP was maintained at 45 °C. Then, the temperature was gradually increased to the maximum value 65 °C. The results showed that different initial wood moisture content does not affect to final value of tension and normal wood. The colorimetric parameter L* was much higher for tension wood. After steaming, there were greater differences in the colorimetric parameters, respectively, a* and b*. After drying the difference of all colorimetric parameters between tension and normal wood was significantly less. The color changes were only noticed in the surface layers of specimens. Differences were small, and thus, the impact of the tension wood on the color changes was not confirmed. However, since the lightness of tension wood plays a key role for its visual detection, it may be adequate to only measure the lightness parameter (L*). [ABSTRACT FROM AUTHOR]

This study examined the changes in the properties of beech wood (Fagus sylvatica L.) after intense drying. Beech wood with false red heartwood was selected as the test specimen. The test samples had dimensions of 50 mm thickness, 180 mm width, and 350 mm length. The specimens were divided into two groups, false red heartwood and sapwood. These specimens were selected with different angles of the growth rings (radial and tangential). The results showed that samples with red heartwood, in comparison to samples with sapwood content, had a remarkable effect in covering. Observation of specimens with false red heartwood and sapwood before and after drying process revealed significant differences in color changes and measured values during the covering-slicing test, but not between samples with different growth ring angles. [ABSTRACT FROM AUTHOR]