Search

The precipitation behavior of α phase in a β-quenched Ti-55511 alloy during high-temperature compression is investigated. The influences of deformation parameters on the flow characteristics, microstructural evolution, as well as the precipitation behavior of α phase, are discussed. Results show that the flow stress features and the dominant softening mechanism are sensitive to the deformation parameters. At low strain rates or high deformation temperatures, the main softening mechanism is dynamic recovery. But, the dynamic recrystallization becomes the dominant softening mechanism at high strain rates or low temperatures. At low strain rates, the continuous strengthening, induced by the pinning effect of α precipitates, happens at the late period of deformation. Distribution of α precipitates is not greatly affected by deformation parameters. In the region near β grain boundary, α precipitates are densely distributed with few orientations. While in the central region of β grain, the α precipitates are distributed a bit more sparsely with several scattering orientations. In addition, with increasing deformation temperature, the content, aspect ratio and size of α phases decrease. However, with increasing strain rate, the content, aspect ratio and size first increase and then decrease. Furthermore, the peak value of aspect ratio appears at 0.01 s−1. • Precipitation behavior of α phase in a β-quenched Ti-55511 alloy during hot compression is studied. • At low strain rates or high deformation temperatures, the main softening mechanism is dynamic recovery. • Dynamic recrystallization is the dominant softening mechanism at high strain rates or low temperatures. • α precipitates are distributed a bit more sparsely with several scattering orientations within β grains. • With increasing deformation temperature, the content, aspect ratio and size of α phases decrease. [ABSTRACT FROM AUTHOR]

Hot compression features of Ti-55511 alloy are investigated by high-temperature compression tests in α+β region. It is found that the flow stress and softening mechanisms are obviously influenced by deformation conditions. The true stress decreases with the reduced strain rate or the raised temperature. The spheroidization of α phase and dynamic recrystallization (DRX) of β phase easily occur at low temperatures such as 973, 1003 and 1033 K, while the dynamic recovery (DRV) of β phase mainly occurs at high temperatures such as 1063 K because of the transformation from α phase to β phase at relatively high temperatures A dislocation density-based constitutive model, which is associated with DRV, work hardening mechanisms and the spheroidization of α phases, is established and validated to describe flow behavior. The correlation coefficient (R) and average absolute relative error (AARE) of the established model are 0.9924 and 6.8%, respectively. 3D power dissipation efficiency maps and processing maps are established to determine the appropriate processing window, i.e., too low temperatures (lower than 973 K) or too high strain rates (higher than 1 s−1) easily induce flow instability. Therefore, the medium temperature (1003–1063 K) and the low strain rate (0.001–0.1 s−1) are applicable for thermal compression of the studied titanium alloy. • Hot compression features of Ti-55511 alloy is investigated by high-temperature compression tests in α+β region. • DRX easily occurs at low temperatures, while DRV mainly occurs at high temperatures. • A accurate dislocation density-based constitutive model considering the spheroidization of α phases is established. • The optimal forming temperature and strain rate are 1003–1063 K and 0.001–0.1 s−1. [ABSTRACT FROM AUTHOR]