Search

The self-focusing characteristic of 355 nm, 3.3 ns pulses propagating through phosphate glass samples is found to significantly change during repeated exposure. The results indicate this change is related to the formation of color centers in the material as well as the generation of a transient defect population during exposure to the laser pulses. A model is used to fit the experimental data and obtain an estimated range of values for the modified linear and nonlinear indices of refraction.

The light emission produced near the surface of fused silica following laser-induced breakdown on the exit surface was spatially and spectrally resolved. This signal is in part generated by ejected particles while traveling outside the hot ionized region. The thermal emission produced by the particles can be separated from the plasma emission near the surface and its spectral characteristics provide information on the temperature of the particles after ejection from the surface. Assuming the emission is thermal in origin, data suggest an initial average temperature on the order of at least 0.5 eV.

The transient changes in the optical properties of bulk DKDP material arising from its exposure to high temperatures and pressures associated with localized laser energy deposition are investigated. Two methods for initiation of laser-induced breakdown are used, intrinsic, involving relatively large energy deposition brought about by focusing of the laser beam to high intensities, and extrinsic, arising from more localized deposition due to the presence of pre-existing absorbing damage initiating defects. Each method leads to a very different volume of material being affected, which provides for different material thermal relaxation times to help better understand the processes involved.

Laser-induced damage at near operational laser excitation conditions can limit the performance of potassium dihydrogen phosphate (KH(2)PO(4), or KDP) and its deuterated analog (DKDP) which are currently the only nonlinear optical materials suitable for use in large-aperture laser systems. This process has been attributed to pre-existing damage precursors that were incorporated or formed during growth that have not yet been identified. In this work, we present a novel experimental approach to probe the electronic structure of the damage precursors. The results are modeled assuming a multi-level electronic structure that includes a bottleneck for 532 nm excitation. This model reproduces our experimental observations as well as other well-documented behaviors of laser damage in KDP crystals. Comparison of the electronic structure of known defects in KDP with this model allows for identification of a specific class that we postulate may be the constituent defects in the damage precursors. The experimental results also provide evidence regarding the physical parameters affecting the ability of individual damage precursors to initiate damage, such as their size and defect density; these parameters were found to vary significantly between KDP materials that exhibit different damage performance characteristics.

We report on the material response during the cooling phase in bulk fused silica following localized energy deposition via laser-induced breakdown.We use a time-resolved microscope system to acquire images of the region of energy deposition at delay times covering the entire timeline of events. In addition, this system is configured to perform pump-and-probe damage testing measurements to investigate the evolution of the transient absorption of the modified material. The main features of a damage site are established at approximately 30 ns after the pump pulse, i.e. cracks reach their final size within this time frame. The results reveal that the cracks and melted core exhibit a transient absorption up until about 300 ns and 200 micros delay times, respectively, and suggest that the melted region returns to solid phase at approximately 70 ms delay., ((c) 2010 Optical Society of America.)