Search

An investigation of the effect of strain rate on the dynamic compressive behavior of glass/polytetrafluoroethylene (PTFE) composite is presented. Experimental studies were carried out on two dimensional (2D), satin weave (SW) and three dimensional (3D) woven glass/PTFE composites using split Hopkinson pressure bar (SHPB) apparatus. Commercial grades of glass/PTFE fabrics were autoclaved to prepare the composite laminates and circular specimens were cut out using a high‐pressure water jet. High strain rate studies confirmed the rate‐dependent behavior of all the woven composite systems under consideration. The highest rates of loading were attained by 3D woven specimens for identical incident energies. The highest peak stress attained by 3D woven specimens was 501 MPa, which was trailed by 2D woven specimens with 482 MPa stress. The advantage of satin weave was not reflected in the small specimens as the peak stress attained for identical loading was limited to 405 MPa. Similarly, the highest strain and toughness were recorded for 3D woven composites. However, the SW pattern unlocked a new possibility of controlling the primary damage axis. Furthermore, an analytical method is presented based on variable rate power law to predict the dynamic compressive stress of glass/PTFE. [ABSTRACT FROM AUTHOR]

In this study, experimental investigations on Kevlar fiber reinforced polypropylene (PP) woven composites under high strain rate compression loading are discussed. Kevlar/PP composite laminates with 8 and 24 layers are fabricated using vacuum assisted compression molding technique. Maleic anhydride grafted-PP (MAg-PP) is added to PP to improve the interfacial property between Kevlar fiber and PP resin. The through-thickness properties at high strain rates from 1370 to 6066 s −1 are obtained using split Hopkinson pressure bar (SHPB) setup. The behavior of PP resin is found to be different than the commonly used thermoset resins, such as epoxy. Dynamic stress–strain relations are drawn to reveal the mechanical properties at high strain rates and these relations appear to be rate sensitive. As a result, the peak stress increased by three times, toughness increased by almost ten times and strain at peak stress increased by as much as two times with an increase in the strain rate. The final failure of the specimens is examined by scanning electron microscopy (SEM) to explore the possible failure mechanisms such as, delamination, fiber failure and shear fracture. [ABSTRACT FROM AUTHOR]

• Vacuum compression moulded Basalt-Polyeteherimide (PEI) composites manufacturing. • Optimization of Basalt-PEI composite manufacturing moulding parameters. • Basalt-PEI composite under quasi-static and dynamic high strain rate loading. • Elastic recovery of Basalt-PEI composite can help in reflecting the blast wave. High temperature blast and ballistic resistant light weight fibre reinforced plastic composites are very much in demand. Accordingly, the present investigation is focused on the quasi-static and high strain rate behaviour of Basalt/Polyetherimide (PEI) composite. Nine different types of composite samples were fabricated by compression moulding. The moulding pressures and temperatures were varied in the range of 15–25 bars and 325 °C−375 °C, respectively. Quasi-static testing was done at the rate of 3 mm/min to establish the optimum moulding parameters. High strain rate compression tests in the strain rate range of 900/s−3200/s were performed on the optimum moulded composite specimens. High strain rate testing revealed that 40 layered Basalt/PEI composite moulded at 25 bar pressure and 350 °C attained highest stress of 932 MPa whereas, the same was found to attain 446 MPa under quasi-static loading conditons. Thus, establishing the rate depedency of Basalt/PEI composite. Damage studies revealed that Basalt/PEI undergoes brittle damage, typically resulting in shear plane angle of 42°−45°. SEM micrographs revealed brittle fibre failure and matrix free fibre bundles, indicating the importance of process parameter optimiation. [ABSTRACT FROM AUTHOR]

The present study deals with the quasi-static and high strain rate characterization of Kevlar-129 based thermoplastic composites. Two different thermoplastic matrices, namely, Polypropylene (PP) and Polyetherimide (PEI) were used to manufacture composite laminates. Quasi-static compression tests were performed at strain rates of 0.041 s−1 and 0.045 s−1. High strain rate tests were performed using a split Hopkinson pressure bar apparatus within the strain rates ranging from 2548 s−1 to 4379 s−1. Stress-strain relations reveals the rate-sensitive behaviour of composites. Kevlar/PP (K-PP) showed higher peak stress under quasi-static loading as compared to the high strain rate test. Comparable peak stresses were revealed under quasi-static and high strain rate loading for Kevlar/PEI (K-PEI) composite. Also, high strain rate compression properties such as peak stress, peak strain and toughness of K-PP were 25%, 27% and 6% higher than that of the K-PEI composite. The failure mechanisms of both the composites were characterized through macroscopic and scanning electron microscopy. K-PP failed majorly due to matrix crush and fibre failure while K-PEI failed due to shear cracking. Damage study reveals that a single fibre based composite system can be tailored to act as an energy-absorbing or dissipating material system by varying the thermoplastic matrix materials. • Static and dynamic compressive properties of Kevlar reinforced high-performance polymers. • Kevlar/Polypropylene outperforms over Kevlar/Polyetherimide under both the quasi-static and high strain rate loads. • The quasi-static strength of Kevlar/Polypropylene is 25% higher than its high strain rate strength. • Polypropylene matrix results in ductile failure, while the Polyetherimide matrix results in brittle failure. [ABSTRACT FROM AUTHOR]