LT21 a type of aluminum alloy used for the irradiation channel of the first heavy water research reactor (HWRR) in China. Studying the mechanical property of irradiated LT21 aluminum under actual service conditions is essential for evaluating its application property. In this paper, tensile specimens of irradiated LT21 were manufactured from the decommissioned irradiation channel of an HWRR; then, tensile tests were carried out, and then the fracture surfaces were observed. The effect of neutron irradiation on tensile behavior and the failure mechanism was analyzed by comparing the result of irradiated and unirradiated LT21 specimens. The results show that, with the thermal neutron flux increasing to 2.38 × 1022 n/cm2, the YS gradually increased from the initial 158 MPa to 251 MPa, the UTS increased from 262 MPa to 321 MPa, and the elongation decreased from 28.8% to about 14.3%; the brittle fracture of the LT21 specimen appeared after irradiation, and the proportion of brittle fracture increased as the neutron fluence increased; the nanophase structures, with a size of less than 50 nm, were precipitated in the LT21 aluminum alloy after neutron irradiation. Transmutation Si is presumed to be the main cause of the radiation effect mechanism of LT21. [ABSTRACT FROM AUTHOR]

• 9 chemical contents and 3 irradiation conditions were used as input factors. • The probability density distribution of Δ RT NDT was used to evaluated the model performance. • The GBDT model has the best performance, its prediction is close to that of ASTM E900-15. • FNF, T and the content of Cu, Ni, C are the most important 5 factors for irradiation embrittlement. A reliable irradiation embrittlement model of reactor pressure vessel (RPV) is critical to the safe operation and life extension of nuclear power plants (NPP). In this study, 474 datasets from NUREG/CR-6551 and 6 machine learning (ML) methods were adopted to accurately predict the irradiation embrittlement behavior (Δ RT NDT) of RPV with comprehensive input factors involving irradiation conditions and metal composition. The GBDT model has the best prediction performance. The calculated result by GBDT model is close to those of JEAC-4201 and ASTM E900-15. Cu content is the most sensitive factor for Δ RT NDT , followed by neutron fluence. This work demonstrates a successful application of ML in promoting NPP safety and RPV materials design. [ABSTRACT FROM AUTHOR]

The behavior of solute atoms in an undersaturated Fe-3.3 at.%Ni model alloy upon heavy and light particle irradiations was investigated by Atom Probe Tomography. Whereas first irradiations, performed using 27 MeV Fe ions at 400 °C, highlight significant Ni enrichment on point defect clusters, solute-rich features detected after 2.8 MeV H + ion (400 °C) and 1 MeV electron (320 °C) irradiations are only associated with pre-existent microstructural defects. Nanoindentation tests show no hardening in light particle irradiated samples, strongly suggesting that no dislocation loop formed. These observations put forward the importance of point defect clusters resulting from displacement cascades in Ni clusters' formation. Image, graphical abstract [ABSTRACT FROM AUTHOR]

In situ irradiation in transmission electron microscope following pre-irradiation was performed on Fe-0.6Ni alloy to investigate the growth of dislocation loops under irradiation. The observations showed two types of loop growth behaviour. One type was almost linear growth with irradiation dose, possibly caused by loop absorbing freely migrating defects. The other was abrupt growth with rapid increase in diameter. It was found that nanometre-sized loop might migrate one-dimensionally, following which the large loop could absorb the small loop. This process can result in the abrupt growth of loop and broadening of loop size distribution. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Neutron irradiation following thermal ageing experiments were performed using Fe-Cu, Fe-Cu-Ni, Fe-Cu-Ni-Mn, and Fe-Cu-Si alloys to investigate the effects of Ni, Mn, and Si on the formation of Cu-rich clusters and their chemical composition. Atom probe tomography showed that Ni and Mn increased the number density of Cu-rich clusters. This can be caused by that Ni and Mn reduce the formation energy of Cu nuclei, thus enhancing the Cu nucleation rate. Mn may also enhance the heterogeneous nucleation of Cu because of its strong interaction with self-interstitial atoms. In addition, Mn can accelerate solute diffusion during thermal ageing. A high Ni alloying content enhanced the Mn concentration in the clusters as well as the Ni concentration, which is believed to be caused by the thermodynamic relationship between Ni and Mn. In Fe-Cu-Si alloys, the Si concentration in the clusters was very low and was comparable to the Si alloying content. This indicates that Si atoms hardly cluster with Cu. [ABSTRACT FROM AUTHOR]

Reactor pressure vessel (RPV) is the critical un-changeable component of the reactor during its service lifetime, which prevents the radioactive leak of the nuclear power plant core. The irradiation test (about 10 × 10 19 cm − 2 , E > 1 MeV) in research reactor of the pressure vessel material was carried out, and the charpy impact test has been carried out before and after the neutron irradiation. Analysis of the impact energy and the fracture morphology has been done to estimate the embrittlement due to neutron irradiation. It shows that the main effects of neutron irradiation to fracture are the crack initiation and stable expansion process. And there also are a small amount of intergranular fracture in the unstable crack expansion after neutron irradiated which aware us pay more attention to the increasing intergranular fracture behavior of higher neutron fluence level after 60a nuclear power plant operation. [ABSTRACT FROM AUTHOR]

A multiscale modeling approach was applied to investigate the nucleation process of CRPs (copper rich precipitates, i.e., copper-vacancy clusters) in α-Fe containing 1 at.% Cu during irradiation. Monte-Carlo simulations were performed to investigate the nucleation process, with the rate theory equation analysis to evaluate the concentration of displacement defects, along with the molecular dynamics technique to know CRP thermal stabilities in advance. Our MC simulations showed that there is long incubation period at first, followed by a rapid growth of CRPs. The incubation period depends on irradiation conditions such as the damage rate and temperature. CRP’s composition during nucleation varies with time. The copper content of CRPs shows relatively rich at first, and then becomes poorer as the precipitate size increases. A widely-accepted model of CRP nucleation process is finally proposed. [ABSTRACT FROM AUTHOR]

To assess the combined effect of thermal aging and neutron irradiation on the cracking behavior of CF-8 cast austenitic stainless steel, crack growth rate (CGR) and fracture toughness J-R curve tests were carried out on compact-tension specimens in high-purity water with low dissolved oxygen. Both unaged and thermally aged specimens were irradiated at ∼320 °C to 0.08 dpa. Thermal aging at 400 °C for 10,000 h apparently had no effect on the corrosion fatigue and stress corrosion cracking behavior in the test environment. The cracking susceptibility of CF-8 was not elevated significantly by neutron irradiation at 0.08 dpa. Transgranular cleavage-like cracking was the main fracture mode during the CGR tests, and a brittle morphology of delta ferrite was often seen on the fracture surfaces at the end of CGR tests. The fracture toughness J-R curve tests showed that both thermal aging and neutron irradiation can induce significant embrittlement. The loss of fracture toughness due to neutron irradiation was more pronounced in the unaged than aged specimens. After neutron irradiation, the fracture toughness values of the unaged and aged specimens were reduced to a similar level. G-phase precipitates were observed in the aged and irradiated specimens with or without prior aging. The similar microstructural changes resulting from thermal aging and irradiation suggest a common microstructural mechanism of inducing embrittlement in CF-8. [ABSTRACT FROM AUTHOR]

The irradiation of high-energy particles always leads to the embrittlement of metallic materials. Here, we report an abnormal irradiation toughening phenomenon in a hierarchical structured ZrTi, which results from the irradiation-induced lattice relaxation that yields an enhanced ductility with a slight decrease of strength. Positron annihilation measurements reveal that the lattice relaxation dominantly originates from a recombination of irradiation-induced interstitials (i.e., Ti atoms) with preexisting dislocation-associated vacancies. This study provides an approach to suppress the irradiation-induced brittleness in metallic materials. [ABSTRACT FROM AUTHOR]

We discuss irradiation tests performed at the Budapest research reactor operating with 10 MW using a new irradiation rig. Some examples of the use of the irradiation rigs are presented: results of reactor pressure vessel cladding, 9% Cr steels (Euroferr), application of Master Curve to irradiated reactor pressure vessel steels, as well as irradiation tests of Ti-alloys and tungsten. [ABSTRACT FROM AUTHOR]

Reactor internals are subjected to three principal operation effects: neutron and gamma irradiation, static and dynamic mechanical stresses and coolant chemistry. In this study, we investigate the effect of these mechanisms on WWER 440 reactor vessel internals and present lifetime analysis, in order to extend the operational lifetime of reactor vessel internals. [ABSTRACT FROM AUTHOR]

Abstract: The effects of intergranular P segregation and hardening on the ductile-to-brittle transition temperature (DBTT) in several neutron-irradiated reactor pressure vessel steels with different bulk contents of P and Cu have been investigated using a scanning Auger microbe, a local electrode atom probe and positron annihilation spectroscopy. Increasing the neutron fluence at 563K promotes intergranular P segregation, particularly in steels with high levels of P. The content of P (<570ppm) more significantly affects irradiation-hardening than that of Cu (<0.17wt.%) due to distinct formation of P-rich precipitates arising from the stabilization of vacancies. Analyzing the correlations between P segregation, hardening, fraction of intergranular fracture and DBTT, it is found neutron irradiation mitigates the embrittling effect of segregated P, and therefore the hardening more strongly affects the DBTT shift than the P segregation, with the exception of highly P-doped steel irradiated to high neutron fluence. [Copyright &y& Elsevier]

Abstract: Irradiation embrittlement is a limiting condition for the long-term safety of a nuclear reactor pressure vessel (RPV). The first PWR in Korea is approaching its initial licensing life of 30 years. In order to operate the reactor for another 10 years and more, it should be demonstrated that the irradiation embrittlement of the reactor will be adequately managed by ensuring that the fracture toughness properties are above a certain level of the required safety margin. The RPV was designed by an old construction code and its beltline circumferential welds have suffered from an irradiation shift problem like other Linde 80 welds. The master curve method is considered as the most promising tool to characterize irradiated structural steels by using a fracture mechanics basis. In order to implement the master curve method for the assessment of an irradiation embrittlement of old power reactors for a continued long-term operation, three practical issues were emphasized in this investigation, which are the specimen geometry effects on the master curve results, the specimen reconstitution techniques in an old existing surveillance program, and the index temperatures of an irradiation embrittlement when compared with the conventional Charpy data. [Copyright &y& Elsevier]

Most of reactor vessel internals (RVIs) have been constructed by austenitic stainless steels (ASSs) to support and protect core from high temperature coolant and radiation particles. However, if they are operated in the harsh environment for a long time, ASS materials may undergo significant changes in micro-structural features, macroscopic deformation and strengths due to age-related degradation mechanisms (ARDMs). In this study, user subroutines were developed based on material constitutive models of recently revised technical reports to reflect irradiation embrittlement, irradiation enhanced creep and void swelling behaviors. Benchmark analyses for a simple rod and detailed numerical analyses for a RVI sub-components assembly with welds were conducted via coupling the subroutines. With regard to the latter analyses, not only typical normal operating sequences but also three fuel cycles associated with specific core loading patterns were taken into account with a constant initial weld residual stress distribution. Adequacy of the subroutines was verified through analytical solutions generated from temperature and radiation damage dependent equations. Complex neutron dose, temperature and pressure profiles of the assembly were successfully determined from thermal and mechanical finite element analyses. Structural integrity assessment in terms of the ductility, embrittlement and irradiation assisted stress corrosion cracking susceptibility ratio after 40-years of operation led to acceptable in spite of the ARDMs. Contributions of factors and interaction effects were further quantified and discussed via design of experiment approach. • Five subroutines were developed to reflect irradiation induced degradations. • Uniform operating, fuel cycle loads and weld residual stress were incorporated. • The contribution of irradiation creep was the most influential to loss of ductility. • Stress relief reduced irradiation assisted stress corrosion cracking susceptibility. [ABSTRACT FROM AUTHOR]

Abstract: The correlation between recent PAS results and the outcomes from mechanical testing of RPV model alloys are presented, here significant changes due to different chemical composition and different irradiation levels are observed. The influence of alloying elements to the microstructure degradation process following irradiation was identified by analysis of the mean-lifetime parameter, since an interesting interdependency of this parameter with hardness was observed. [Copyright &y& Elsevier]