We performedin situobservation of one-dimensional (1D) migration of self-interstitial atom (SIA) clusters in iron under electron irradiation at 110–300 K using high-voltage electron microscopy. Most 1D migration was stepwise positional changes of SIA clusters at irregular time intervals at all temperatures. The frequency of 1D migration did not depend on the irradiation temperature. It was directly proportional to the damage rate, suggesting that 1D migration was induced by electron irradiation. In contrast, the 1D migration distance depended on the temperature: distribution of the distance ranged over 100 nm above 250 K, decreased steeply between 250 and 150 K and was less than 20 nm below 150 K. The distance was independent of the damage rate at all temperatures. Next, we examined fluctuation in the interaction energy between an SIA cluster and vacancies of random distribution at concentrations 10−4–10−2, using molecular statics simulations. The fluctuation was found to trap SIA clusters of 4 nm diameter at vacancy concentrations higher than 10−3. We proposed that 1D migration was interrupted by impurity atoms at temperatures higher than 250 K, and by vacancies accumulated at high concentration under electron irradiation at low temperatures where vacancies are not thermally mobile. [ABSTRACT FROM AUTHOR]

Vacancy depth profiles installed by rapid thermal annealing can be monitored either by Pt diffusion or through vacancy-assisted oxygen precipitation. The features of these profiles clearly show that the vacancy species manifested in these experiments is a 'slow vacancy', Vs. The evolution of Vs depth profiles is controlled by an exchange with another (mobile) kind of vacancy that is likely to be a 'Watkins vacancy', Vw, first observed at cryogenic temperatures. At low T the conversion of Vs into Vw is slow and practically irreversible. At higher T the two species coexist in an equilibrium ratio and diffuse as one entity with an averaged diffusivity. This model provides a good fit to the RTA-installed depth profiles of Vs. The total vacancy community includes, beside Vs and Vw, also a fast vacancy Vf that is responsible for the vacancy contribution into self-diffusion at high T. In RTA experiments, the Vf species seems to be completely annihilated by self-interstitials which leaves only two other vacancy species, Vs and Vw. [ABSTRACT FROM AUTHOR]