In order to achieve the goal of resource utilization of High-Ti vanadium titanomagnetite (High-Ti VTM), the high-temperature sintering characteristics of High-Ti VTM were investigated by micro-sintering experiments, while the effects of different ordinary iron ore dosage and basicity on the sintering process parameters and sinter quality were investigated by sintering pot experiments. The results showed that the TiO2 and SiO2 contents increased gradually with increasing dosage of High-Ti VTM, and the liquid phase fluidity index and binder phase strength increased gradually, while the assimilation temperature and intergranular consolidation strength showed a decreasing trend. With the increase of the dosage of ordinary iron ore, the vertical sintering speed was reduced, while the sinter yield and tumble index gradually increased. As the basicity of the sinter gradually increased, the sintering time and the pulverization degree of the sinter gradually increased and the sinter yield gradually decreased, while the vertical sintering speed and the tumble index both showed a trend of first increasing and then decreasing. The results of the study provide data to support the preparation of sinter with High-Ti VTM. [ABSTRACT FROM AUTHOR]

Vanadium titanomagnetite is an important mineral resource. It is a raw material for ironmaking, vanadium extraction, strategic metal titanium production, and titanium dioxide production. In this study, high chromium vanadium titanomagnetite (High-Cr VTM) and ordinary iron ore were used as raw materials for pelletizing. The effect of V2O5 on the preparation and properties of High-Cr VTM pellets was studied. The influence of V2O5 on the properties of the green pellets, the compressive strength of oxidized pellets, the reduction swelling index and reduction degree, softening-melting behavior, and the migration law of Fe, Ti, and Cr in the reduction process were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that with the increase in V2O5 content, the properties of the green pellets basically showed a trend of first decreasing and then increasing but all met the basic requirements of pelletizing. When the added amount of V2O5 in the pellet was 6%, the compressive strength of the oxidized pellet was the lowest at only 2565 N/pellet but it still met the quality requirements for pellets in blast furnace production. As the dosage of V2O5 increased, the reduction swelling index and reduction degree of the pellets showed a trend of first increasing and then decreasing. The addition of V2O5 can increase the softening initial temperature, softening final temperature, melting start temperature, and dripping temperature of the High-Cr VTM pellets, narrowing the softening interval, and expanding the melting dripping interval. The experimental results provided a data reference for revealing the influence of V2O5 on High-Cr VTM pellets during the blast furnace smelting process. [ABSTRACT FROM AUTHOR]