The influence exerted by the conditions of the post-implantation annealing of silicon implanted with germanium ions on how luminescence centers are formed is studied. Measurements by the technique of the Rutherford backscattering of medium- and high-energy ions demonstrates that implantation with 1-MeV germanium ions at a dose of 1.5 × 1014 cm–2 does not lead to the amorphization of single-crystal silicon. It is found that subsequent high-temperature annealing of the implanted samples in a chlorine-containing atmosphere at a temperature of 1100°C for 0.5–1.5 h gives rise to so-called D1 and D2 dislocation-related luminescence lines with wavelengths of 1.54 and 1.42 μm. With increasing annealing duration, the intensity of the D1 line decreases and that of D2 remains constant, but the D1 line dominates in all the spectra. The possible factors responsible for a decrease in the intensity of the D1 line and, in particular, the diffusion of germanium atoms and the formation of a silicon–germanium solid solution are discussed. [ABSTRACT FROM AUTHOR]

The implantation of Czochralski-grown p-type silicon with 1-MeV germanium ions at a dose of 2.5 × 1014 cm–2 does not lead to the amorphization of single-crystal silicon. Under subsequent high-temperature annealing, electrically active acceptor centers are transformed. Their concentration and special distribution depend on the annealing temperature. The possible factors determining how these centers are formed are discussed. [ABSTRACT FROM AUTHOR]

Implantation of silicon ions with an energy of 100 keV at a dose of 1 × 1017 cm−2 into n-type floatzone Si does not lead to the formation of an amorphous layer. Subsequent annealing in a chlorine-containing atmosphere at 1100°C gives rise to dislocation-related luminescence. The intensity of the dominant D1 line peaked at a wavelength of ∼1.54 μm grows as the annealing time is increased from 15 to 60 min. [ABSTRACT FROM AUTHOR]