To date, there have been no efficient semiconductor light emitters operating in the green and amber wavelengths. This study reports on the synthesis of InGaN nanowire photonic crystals, including dot-in-nanowires, nanotriangles, and nanorectangles with precisely controlled size, spacing, and morphology, and further demonstrates that bottom-up InGaN photonic crystals can exhibit highly efficient and stable emission. The formation of stable and scalable band edge modes in defect-free InGaN nanowire photonic crystals is directly measured by cathodoluminescence studies. The luminescence emission, in terms of both the peak position (λ ≈ 505 nm) and spectral linewidths (full-width-half-maximum ≈ 12 nm), remains virtually invariant in the temperature range of 5-300 K and under excitation densities of 29 W cm−2 to 17.5 kW cm−2. To the best of our knowledge, this is the first demonstration of the absence of Varshni and quantum-confined Stark effects in wurtzite InGaN light emitters-factors that contribute significantly to the efficiency droop and device instability under high-power operation. Such distinct emission properties of InGaN photonic crystals stem directly from the strong Purcell effect, due to efficient coupling of the spontaneous emission to the highly stable and scalable band-edge modes of InGaN photonic crystals, and are ideally suited for uncooled, high-efficiency light-emitting-diode operation. [ABSTRACT FROM AUTHOR]

We report on the demonstration of a new type of axial nanowire LED heterostructures, with the use of self-organized InGaN/AlGaN dot-in-a-wire core-shell nanowire arrays. The large bandgap AlGaN shell is spontaneously formed on the sidewall of the nanowire during the growth of AlGaN barrier of the quantum dot active region. As such, nonradiative surface recombination, that dominates the carrier dynamics of conventional axial nanowire LED structures, can be largely eliminated, leading to significantly increased carrier lifetime from ~0.3 ns to 4.5 ns. The luminescence emission is also enhanced by orders of magnitude. Moreover, the p-doped AlGaN barrier layers can function as distributed electron blocking layers (EBLs), which is found to be more effective in reducing electron overflow, compared to the conventional AlGaN EBL. The device displays strong white-light emission, with a color rendering index of ~95. An output power of >5 mW is measured for a 1 mm × 1 mm device, which is more than 500 times stronger than the conventional InGaN axial nanowire LEDs without AlGaN distributed EBLs. [ABSTRACT FROM AUTHOR]

InGaN/GaN disk-in-nanowire heterostructures on silicon substrates have emerged as important gain media for the realization of visible light sources. The nature of quantum confinement in the disks is largely unknown. From the unique nature of the measured temperature dependence of the radiative lifetime and direct transmission electron microscopy, it is evident that such self-organized islands (disks) behave as quantum dots. This is confirmed by the observation of single photon emission from a single disk-in-nanowire and the presence of a sharp minimum in the line width enhancement factor of edge emitting lasers having the InGaN disks as the gain media. [ABSTRACT FROM AUTHOR]