Search

Abstract: Au/Ni-foam electrodes with three dimensional network structures are prepared by simple spontaneous deposition of nano-sized Au particles onto nickel foam surface in an aqueous solution of AuCl3. Their morphology and catalytic performance for NaBH4 electrooxidation and H2O2 electroreduction in NaOH solution are investigated. Au particles with diameters smaller than 100nm are uniformly deposited on the whole surface of all skeletons of the nickel foam substrate. The onset potential for NaBH4 electrooxidation and H2O2 electroreduction is about −1.2V and −0.1V, respectively. A direct liquid feed alkaline NaBH4–H2O2 fuel cell is constructed using Au/Ni-foam electrode as both the anode and the cathode. The effects of the concentration of NaBH4 and H2O2 and operation temperature on the fuel cell performance are investigated. The fuel cell exhibits an open circuit voltage of about 1.07V and a peak power density of 75mWcm−2 at a current density of 150mAcm−2 and a cell voltage of 0.5V operating on 0.2moldm−3 NaBH4 and 0.5moldm−3 H2O2 at 40°C. [Copyright &y& Elsevier]

Nanoporous palladium supported on the carbon coated titanium carbide (C@TiC) nanowire arrays (Pd NP/C@TiC) are successfully prepared by a facile chemical vapor deposition of three-dimensional (3D) C@TiC substrate, followed by electrochemical codeposition of Pd–Ni and removal of Ni via dealloying. The structure and morphology of the obtained Pd NP/C@TiC electrodes are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). Cyclic voltammetry (CV), linear sweep voltammetry (LSV), chronoamperometry (CA) and electrochemical impedance spectroscopy (EIS) are used to examine the catalytic performances of the electrodes for H 2 O 2 electroreduction in H 2 SO 4 solution. The Pd NP/C@TiC electrode exhibits a largely effective specific surface area owing to its open nanoporous structure allowing the full utilization of Pd surface active sites. At the potential of 0.2 V in 2.0 mol L −1 H 2 O 2 and 2 mol L −1 H 2 SO 4 solutions, the reduction current density reaches 3.47 A mg −1 , which is significantly higher than the catalytic activity of H 2 O 2 electroreduction achieved previously with precious metals as catalysts. [ABSTRACT FROM AUTHOR]

A novel three-dimensional carbon- and binder-free nickel nanowire arrays (Ni NAs) electrode is successfully fabricated by a facile galvanostatic electrodeposition method using polycarbonate membrane as the template. The Ni NAs electrode achieves a oxidation current density (divided by the electroactive surface areas of Ni) of 25.1 mA cm −2 in 4 mol L −1 KOH and 0.9 mol L −1 H 2 O 2 at 0.2 V (vs. Ag/AgCl) accompanied with a desirable stability, which is significantly higher than the catalytic activity of H 2 O 2 electro-oxidation achieved previously with precious metals as catalysts. The impressive electrocatalytic performance is largely attributed to the superior 3D open structure and high electronic conductivity, which ensures the high utilization of Ni surfaces and makes the electrode have higher electrochemical activity. The apparent activation energy of H 2 O 2 electro-oxidation on the Ni NAs catalyst is 13.59 kJ mol −1 . A direct peroxide–peroxide fuel cell using the Ni NAs as anode exhibits a peak power density of 48.7 mW cm −2 at 20 °C. The electrode displays a great promise as the anode of direct peroxide–peroxide fuel cell due to its low cost, high activity and stability. [ABSTRACT FROM AUTHOR]

A novel three-dimensional (3D) porous nickel-cobalt (Ni-Co) film on nickel foam is successfully prepared and further used as an efficient anode for direct urea-hydrogen peroxide fuel cell (DUHPFC). By varying the cobalt/nickel mole ratios into 0%, 20%, 50%, 80% and 100%, the optimized Ni-Co/Ni foam anode with a ratio of 80% is obtained in terms of the best cell performance among five anodes. Effects of the KOH and urea concentrations, the flow rate and operation temperature on the fuel cell performance are investigated. Results show DUHPFC with the 3D Ni-Co/Ni foam anode exhibits a higher performance than those reported direct urea fuel cells. The cell gives an open circuit voltage of 0.83 V and a peak power density as high as 17.4 and 31.5 mW cm −2 at 20 °C and 70 °C, respectively, when operating on 7.0 mol L −1 KOH and 0.5 mol L −1 urea as the fuel at a flow rate of 15 mL min −1 . Besides, when the human urine is directly fed as the fuel, direct urine-hydrogen peroxide fuel cell reaches a maximum power density of 7.5 mW cm −2 with an open circuit voltage of 0.80 V at 20 °C, showing a good application prospect in wastewater treatment. [ABSTRACT FROM AUTHOR]

Abstract: The open circuit potentials (OCPs) of H2O2 at Pt, Pd, Au, and glassy carbon electrodes are measured in H2SO4 and NaOH electrolyte solutions. Effects of concentration of H+, OH− and H2O2 as well as temperature on the OCP of H2O2 are investigated. The OCP of H2O2 is much lower than its theoretical reduction potential in both acidic and basic medium. The OCP is actually a mixed potential of H2O2 electroreduction and electrooxidation simultaneously occurring at electrode surfaces and it is more close to the equilibrium potential of H2O2 electrooxidation rather than electroreduction. The OCP of H2O2 is around 0.77–0.80V at [H+]=[H2O2]=1.0moldm−3 in H2SO4 solution and is about 0–0.06V at [OH−]=[H2O2]=1.0moldm−3 in NaOH at 298K on Pt, Pd, Au and GC electrodes. The OCP of H2O2 is independent of H2O2 concentration within the range of 0.01 to 1.0moldm−3. It increases approximately linearly with the logarithm of H+ concentration from 0.02 to 2.0moldm−3, decreases with the logarithm of OH− concentration from 0.01 to 1.0moldm−3 and decreases with increase of temperature from 278K to 333K. The linear equations were presented and discussed. [Copyright &y& Elsevier]