Search

Coatings contribute to about 10% of the overall cost of paper production of which, the binder is the highest cost component in the formulation. In addition to costs, the binders that are currently being used are synthesized from fossil fuel feedstock raising concerns towards the sustainability of paper coatings. Furthermore, papers coated with waxes, polyolefins and other synthetic materials are difficult to recycle or compost. These challenges inherent with synthetic binders can be addressed by using renewable, plant based binders. This research focused on an abundant and underutilized source of hemicellulose based binders (DG gum) that can be extracted from distiller's dried grains. The extracted binder was compared with polyvinyl alcohol (PVA) in a coating formulation consisting of 10:1 CaCO 3 to binder formulation coated on light weight paper. Cobb test, dry and wet tensile tests, optical properties (brightness, color, opacity), water vapor transmission rate (WVTR) analysis were performed to compare the hemicellulose based binder with PVA. The results indicate water absorptivity reduction by 25% for both DG gum and PVA coatings from the base paper value. Dry tensile index was lower with higher coating weights for both coatings with similar performance. The performance on WVTR analysis for both coatings was also comparable. No significant differences in optical properties after coating were observed from that of the base paper. These results suggest that hemicellulose based binder extracted from distiller's grains has the potential to replace synthetic binders in paper coating formulations. [ABSTRACT FROM AUTHOR]

Xylan is a highly abundant plant-based biopolymer. Original xylans in plants are in an amorphous state, but deacetylated and low-branched xylan can form a crystalline structure with water molecules. The utilizations of xylan have been limited to bulk applications either with inconsistency and uncertainty or with extensive chemical derivatization due to the insufficient studies on its crystallization. The applications of xylan could be greatly broadened in advanced green materials if xylan crystals are effectively utilized. In this paper, we show a completely green production of nano-sized xylan crystals and propose their application in forming Pickering emulsions. The branches of xylan were regulated during the separation step to controllably induce the formation of xylan hydrate crystals. Xylan hydrate nanocrystals (XNCs) with a uniform size were successfully produced solely by a mild ultrasonic treatment. XNCs can be adsorbed onto oil–water interfaces at a high density to form highly stable Pickering emulsions. The emulsifying properties of XNCs were comparable to some synthetic emulsifiers and better than some other common biopolymer nanocrystals, demonstrating that XNCs have great potential in industrial emulsification. [ABSTRACT FROM AUTHOR]

Hemicellulose is an important component of the plant cell wall which vary in structure and composition between plant species. The research of hemicellulose structures is primarily focused on fast-growing plants during xylogenesis, with slow-growing and rare trees receiving the least attention. Here, hemicellulose structure of the rare species Castanopsis hystrix during xylogenesis was analyzed. Acetyl methyl glucuronide xylan was the most common type of hemicellulose in C. hystrix , with a unique tetrasaccharide structure at the reducing end. Hemicellulose type, structure, molecular weight, thermal stability, biosynthesis and acetyl substitution content and pattern remained stable during the xylogenesis in C. hystrix , which could be attributed to its slow growth. The stable polymer type, low side chain modification and high acetyl substitution of hemicellulose throughout the stems are among the reasons for the hardness and corrosion resistance properties of C. hystrix wood. Genetic modification can be used to improve these properties. • C. hystrix hemicellulose is an acetyl glucuronylxylan with a tetrasaccharide reducing end. • C. hystrix hemicellulose has high acetyl substitution and low branching. • The structure of C. hystrix hemicellulose is relatively stable during xylogenesis. • The apical part of C. hystrix stalk has undergone sufficient secondary thickening. • Biosynthesis of C. hystrix hemicellulose is stable throughout the stalk. [ABSTRACT FROM AUTHOR]

In this study, hemicellulose was isolated from the apical, middle and basal segments of C. lanceolata stem to investigate the dynamic change of its structure during xylogenesis. Results showed that the C. lanceolata hemicellulose is mainly consisted of O -acetylgalactoglucomannan (GGM) which backbone is alternately linked by β- d -mannopyranosyl (Man p) and β- d -glucopyranosyl (Glc p) via (1 → 4)-glycosidic bond, while the side chains are α- d -galactopyranosyl (Gal p) and acetyl. In addition, 4- O -methylglucuronoarabinoxylan (GAX) is another dominant structure of C. lanceolata hemicellulose which contains a linear backbone of (1 → 4)-β- d -xylopyranosyl (Xyl p) and side chains of 4- O -Me-α- d -glucuronic acid (MeGlc p A) and α-L-arabinofuranose (Ara f). The thickness of the cell wall, the ratio of GGM/GAX and the molecular weight of hemicellulose were increased as the extension of growth time. The degree of glycosyl substitutions of xylan and mannan was decreased from 10.34 % (apical) to 8.38 % (basal) and from 15.63 % (apical) to 10.49 % (basal), respectively. However, the total degree of acetylation was enhanced from 0.28 (apical) to 0.37 (basal). Transcriptome analysis showed that genes (CSLA9 , IRX9H1 , IRX10L , IRX15L , GMGT1 , TBL19 , TBL25 , GUX2 , GUX3 , GXM1 , F8H1 and F8H2) related to hemicellulose biosynthesis are mainly expressed in mature part. This study is of great significance for genetic breeding and high-value utilization of C. lanceolata. The structures of C. lanceolata hemicellulose and its changing trend during xylogenesis. [Display omitted] • The hemicellulose in C. lanceolata is mainly composed of GGM and GAX. • The constructures of GGM and GAX were interpreted. • GGM was main component at the all stages of development. • GGM increased while GAX decreased during xylogenesis. • The hemicellulose biosynthesis in C. lanceolata is mainly concentrated in mature stem. [ABSTRACT FROM AUTHOR]

• Statistical model was used to study effects of hemi structures on material property. • High Xylan/Arabinan ratio is favorable to the material property of hemicelluloses. • High Mw and low lignin is favorable to the material property of hemicelluloses. Using originally isolated xylan-type hemicelluloses for material application suffers from poor mechanical properties including low tensile strength and brittleness. The subsequent chemical modifications of hemicelluloses are facing the problems of high costs and toxic chemicals. Consequently, this study tried to investigate the factors affecting the film-forming properties of the originally isolated xylan-hemicelluloses and promoting their material properties from the extraction step. Two different extraction methods, a one-step alkali or alkaline peroxide solution method and a two-step alkali extraction-delignification method were used to extract the hemicellulose with different chemical structures from sugarcane bagasse. For the two-step alkali extraction-delignification method, hemicelluloses were first extracted by alkali solution and then delignified by dioxane/water, hydrogen peroxide solution or sodium hypochlorite solution. The lignin contents of all the extracted hemicelluloses ranged from 1.6%–9.5%, of which the lowest value was obtained through delignification by sodium hypochlorite. The number average molecular weight ranged from 8200 to 26800, while the xylan/arabinan ratio ranged from 5.0 to 9.1. The hemicelluloses were characterized and processed into films. Tensile strength of films could be considerably improved up to ˜52% when using sodium hypochlorite solution as the delignification agents and the lignin content was greatly reduced for the hemicellulose fraction. Statistical models were generated between film mechanical properties and hemicellulose structural characteristics. The models predicted that hemicellulose with higher molecular weight, more linear structure and lower lignin content would result in better mechanical properties. [ABSTRACT FROM AUTHOR]

• Hemicellulose in cassava is mainly composed of methylated glucuronic acid arabinoxylan. • Hemicellulose in cassava plant contains tetrasaccharide reducing end sequence. • The degree of hemicellulose acetylation increases with xylogenesis. • The molecular weight of cassava hemicellulose also increases during xylogenesis. • Hemicellulose biosynthesis in old cassava is mainly concentrated in upper stem. Cassava is one of the three major potato crops due to the high starch content in its tubers. Unlike most current studies on the utilization of cassava tubers, our research is mainly focused on the stem of cassava plant. Through nuclear magnetic resonance (NMR), fourier transform infrared spectrometer (FTIR) and other methods, we found that cassava stalk hemicellulose consists of β-1,4 glycosidic bond-linked xylan backbone with a tetrasaccharide reducing end and decorated with methylated glucuronic acid, acetyl groups and a high degree of arabinose substitutions. Hemicellulose content gradually increased from the upper to the lower parts of the stem. The apical part of cassava stalk contained more branched and heterogeneous glycans than the middle and basal parts, and the molecular weight of hemicellulose increased from top to bottom. Our findings will be helpful in understanding of structural variations of cassava hemicellulose during xylogenesis, as well as in better utilization of cassava plant waste in industry. [ABSTRACT FROM AUTHOR]

As one of the most abundant natural polymers in nature, polysaccharides have the potential to replace petroleum-based polymers that are difficult to degrade in paper coatings. Polysaccharide molecules have a large number of hydroxyl groups that can bind strongly with paper fibers through hydrogen bonds. Chemical modification can also effectively improve the mechanical, barrier, and hydrophobic properties of polysaccharide-based coating layers and thus can further improve the related properties of coated paper. Polysaccharides can also give paper additional functional properties by dispersing and adhering functional fillers, e.g., conductive particles, catalytic particles or antimicrobial chemicals, onto paper surface. Based on these, this paper reviews the application of natural polysaccharides, such as cellulose, hemicellulose, starch, chitosan, and sodium alginate, and their derivatives in paper coatings. This paper analyzes the improvements and influences of chemical structures and properties of polysaccharides on the mechanical, barrier, and hydrophobic properties of coated paper. This paper also summarizes the researches where polysaccharides are used as the adhesives to adhere inorganic or functional fillers onto paper surface to endow paper with great surface properties or special functions such as conductivity, catalytic, antibiotic, and fluorescence. [ABSTRACT FROM AUTHOR]