Search

An investigation of fluoroindate glass and fiber co-doped with Yb3+/Er3+ ions as a potential temperature sensor was assessed using the fluorescence intensity ratio (FIR) technique. Analysis of thermally coupled levels (TCLs—2H11/2 and 4S3/2), non-thermally coupled levels (non-TCLs—4F7/2 and 4F9/2), and their combination were examined. Additionally, the luminescent stability of the samples under constant NIR excitation using different density power at three different temperatures was carried out. The obtained values of absolute sensitivity (0.003 K−1—glass, 0.0019 K−1—glass fiber 2H11/2 → 4S3/2 transition) and relative sensitivity (2.05% K−1—glass, 1.64% K−1—glass fiber 4F7/2 → 4F9/2 transition), as well as high repeatability of the signal, indicate that this material could be used in temperature sensing applications. [ABSTRACT FROM AUTHOR]

The effect of BaF2, MgF2, and AlF3 on the structural and luminescent properties of gallo-germanate glass (BGG) doped with erbium ions was investigated. A detailed analysis of infrared and Raman spectra shows that the local environment of erbium ions in the glass was influenced mainly by [GeO]4 and [GeO]6 units. Moreover, the highest number of non-bridging oxygens was found in the network of the BGG glass modified by MgF2. The 27Al MAS NMR spectrum of BGG glass with AlF3 suggests the presence of aluminum in tetra-, penta-, and octahedral coordination geometry. Therefore, the probability of the 4I13/2→4I15/2 transition of Er3+ ions increases in the BGG + MgF2 glass system. On the other hand, the luminescence spectra showed that the fluoride modifiers lead to an enhancement in the emission of each analyzed transition when different excitation sources are employed (808 nm and 980 nm). The analysis of energy transfer mechanisms shows that the fluoride compounds promote the emission intensity in different channels. These results represent a strong base for designing glasses with unique luminescent properties. [ABSTRACT FROM AUTHOR]

This work reports on the fabrication and analysis of near-infrared and mid-infrared luminescence spectra and their decays in fluoroindate glasses co-doped with Yb3+/Ho3+. The attention has been paid to the analysis of the Yb3+→ Ho3+ energy transfer processed ions in fluoroindate glasses pumped by 976 nm laser diode. The most effective sensitization for 2 μm luminescence has been obtained in glass co-doped with 0.8YbF3/1.6HoF3. Further study in the mid-infrared spectral range (2.85 μm) showed that the maximum emission intensity has been obtained in fluoroindate glass co-doped with 0.1YbF3/1.4HoF3. The obtained efficiency of Yb3+→ Ho3+ energy transfer was calculated to be up to 61% (0.8YbF3/1.6HoF3), which confirms the possibility of obtaining an efficient glass or glass fiber infrared source for a MID-infrared (MID-IR) sensing application. [ABSTRACT FROM AUTHOR]

Fluoroindate glasses co-doped with Pr3+/Er3+ ions were synthesized and their near-infrared luminescence properties have been examined under selective excitation wavelengths. For the Pr3+/Er3+ co-doped glass samples several radiative and nonradiative relaxation channels and their mechanisms are proposed under direct excitation of Pr3+ and/or Er3+. The energy transfer processes between Pr3+ and Er3+ ions in fluoroindate glasses were identified. In particular, broadband near-infrared luminescence (FWHM = 278 nm) associated to the 1G4 → 3H5 (Pr3+), 1D2 → 1G4 (Pr3+) and 4I13/2 → 4I15/2 (Er3+) transitions of rare earth ions in fluoroindate glass is successfully observed under direct excitation at 483 nm. Near-infrared luminescence spectra and their decays for glass samples co-doped with Pr3+/Er3+ are compared to the experimental results obtained for fluoroindate glasses singly doped with rare earth ions. [ABSTRACT FROM AUTHOR]

The ErF3-doped oxyfluoride phospho-tellurite glasses in the (40-x) TeO2-10P2O5-45 (BaF2-ZnF2) -5Na2O-xErF3 system (where x = 0.25, 0.50, 0.75, 1.00, and 1.25 mol%) have been prepared by the conventional melt-quenching method. The effect of erbium trifluoride addition on thermal, structure, and spectroscopic properties of oxyfluoride phospho-tellurite precursor glass was studied by differential scanning calorimetry (DSC), Fourier-transform infrared (FTIR), and Raman spectroscopy as well as emission measurements, respectively. The DSC curves were used to investigate characteristic temperatures and thermal stability of the precursor glass doped with varying content of ErF3. FTIR and Raman spectra were introduced to characterize the evolution of structure and phonon energy of the glasses. It was found that the addition of ErF3 up to 1.25 mol% into the chemical composition of phospho-tellurite precursor glass enhanced 2.7 µm emission and upconversion. By controlled heat-treatment process of the host glass doped with the highest content of erbium trifluoride (1.25 mol%), transparent erbium-doped phospho-tellurite glass-ceramic (GC) was obtained. X-ray diffraction analysis confirmed the presence of BaF2 nanocrystals with the average 16 nm diameter in a glass matrix. Moreover, MIR, NIR, and UC emissions of the glass-ceramic were discussed in detail and compared to the spectroscopic properties of the glass doped with 1.25 mol% of ErF3 (the base glass). [ABSTRACT FROM AUTHOR]

The near-infrared emission properties in low-phonon (805 cm−1) gallo-germanate glasses and their glass fibers co-doped with Yb3+/Ho3+ and Yb3+/Tm3+/Ho3+ have been investigated. Emission bands centered at about 2 μm correspond to 3F 4 → 3H 6 (Tm3+) and/or 5I 7 → 5I 8 (Ho3+) transitions. The spectral widths of emission lines are relatively large and their values for glass samples co-doped with 0.7Yb 2 O 3 /0.15Ho 2 O 3 and 0.5Yb 2 O 3 /0.4Tm 2 O 3 /0.05Ho 2 O 3 are close to 159 nm and 343 nm, respectively. Gallo-germanate glasses characterized by broadband emission at 2 μm have been used for fabrication of glass fibers. The effects of fibers length on their near-infrared luminescent properties have been also analyzed in details. [ABSTRACT FROM AUTHOR]

• Pr3+/Er3+ co-doped glass based on InF 3 have been studied • Emission spectra of Pr3+/Er3+ were measured under different excitation wavelengths • Energy transfer process from Pr3+ to Er3+ occurs • Pr3+/Er3+ co-doped glass based on InF 3 are promising for white light emission Pr3+/Er3+ co-doped glasses based on InF 3 were synthesized and then studied for white light emission. The emission spectra consist of several bands corresponding to characteristic 4f-4f electronic transitions of Pr3+ and Er3+ ions. The relative intensities of emission bands depend on the selective excitation wavelengths. The energy transfer process from Pr3+ to Er3+ ions was confirmed by the excitation and emission spectra measurements. From emission spectra, the CIE chromaticity coordinates, the correlated color temperature (CCT) and the color purity (CP) were determined. The results indicate that Pr3+/Er3+ co-doped glasses based on InF 3 are excellent fluoride candidate to achieve warm white light emission. Graphical Abstract [Display omitted]. [ABSTRACT FROM AUTHOR]