We have studied the microstructure of the growth surface of the 4H-SiC grown by the m-face solution growth. Atomic Force Microscopy (AFM) revealed the micro-striped morphology with the asperity of several nm in the band-like morphology region. The cross-sectional Transmission Electron Microscopy (XTEM) showed that the growth surface consisted of a bunch of nanofacets and vicinal surface. This peculiar morphology is totally different from that of conventional spiral growth on c-face, which can be closely related with the growth mechanism of the m-face solution growth.

Dislocation structures at the seed/grown-crystal interface in PVT-grown 4H-SiC crystals are investigated. The dislocation density is found to show a sharp increase at the interface and its main contribution is probably ascribable to TEDs which stem from BPDs generating at the interface through the structural transformation. Intense TEM observations reveal an intriguing in-plane distribution structure of the interface BPDs; the BPDs form a two-dimensional dislocation network comprising of {-1100} partial dislocations associated with expanded areas of stacking faults at the nodes of the network.

We investigated the effect of the solution flow on crystalline morphology in the off-axis 4H-SiC solution growth. In particular, we focused on the relation between the Si solution flow and step flow directions. In step parallel flow in which the solution drifted transversely to the step flow direction of the off-axis substrate, it was possible to attain a better surface morphology than in the flow in which the solution drifted toward the other direction. Furthermore, it was found that the surface morphology was found to be improved as the solution flow velocity increased. These improvements in the morphological stability are presumed to be caused by aligning the solute concentration fluctuation along the steps.

A long-term growth of high-quality 4H-SiC single crystals by a top-seeded solution growth method using a Si–Cr-based melt was investigated. A new growth technique called “solution growth on concave surface” (SGCS) was developed to help prevent solvent inclusions. The concave shape of the growth surface was achieved by controlling the meniscus height, which enhances the step provision from the periphery to the center. In contrast, under the growth surface, the solution flows from the center to the periphery through convection by inductive heating. The opposite directions of the step flow and solution flow during solution growth create a smooth surface without solvent inclusions. SGCS was used to successfully grow a 1-in. diameter 4H-SiC crystal with a thickness of 30 mm, which is the thickest reported for a solution growth technique, and 1.7-in. diameter high-quality wafers without solvent inclusions were obtained. Schottky barrier diodes were fabricated on 4H-SiC substrates grown by SGCS, which demonstrat...

The off-axis solution growth of 4H-SiC was studied focusing on the morphological instabilities by using conventional TSSG technique. The morphology depends strongly on the crystalline polarity, and that on Si surface can be characterized by wandering while that on C surface is characterized by strong step-bunching. By raising the temperature gradient, step bunching on Si surface is considerably suppressed which can be consistent to the constitutional super cooling scheme. However, C surface exhibits strong step bunching as the temperature gradient increase. These behaviors can be explained by the difference in Ehrlich-Schwoebel barrier and diffusion behavior of adatoms.

We performed top-seeded solution growth of 4H-SiC for obtaining longer length crystal. Si-Cr and Si-Ti melts were used as solvents. Meniscus formation technique was applied to the present study. Special attention was paid to improve the process stability during long-term growth. One of major technological problems in the solution growth is that the precipitation of polycrystalline SiC which hiders the stable single crystal growth. Another problem is the fluctuation of supersaturation at the growth interface during the growth. Through the optimization of growth process conditions, we have successfully grown 4H-SiC single crystals up to 14 mm long with three-inch-diameter, and evaluated their crystalline quality.

In this study, we have investigated the rate-limiting process of 4H-SiC solution growth using Si-Cr based melt, and have tried high-speed growth. It is revealed that the rate-limiting process of SiC growth under our experimental condition is interface kinetics, which can be controlled by such factors as temperature and supersaturation of carbon. By enhancing the interface kinetics, SiC crystal has been grown at a high rate of 2 mm/h. The FWHM values of X-ray rocking curves and threading dislocation density of the grown crystals are almost the same as those of seed crystal. Possibility of high-speed and high-quality growth of 4H-SiC has been indicated.

4H-SiC single crystal with 3-inch diameter was grown by top seeded solution growth (TSSG) technique. We used a new convection control member called “Immersion Guide (IG)” which causes the high and homogenous fluid flow in the solution. As a result, we achieved relatively high growth rate and morphological stability

We report the results of the systematic investigation into correlations between energetics and hexagonal stacking configurations for carbon, silicon, SiC, BN, AlN, GaN, and InN polytypes with sp3-bonded networks. The atomistic geometry, energetics, and electronic structure for these compounds with up to the periodic stacking length of L = 8 have been carefully calculated based on the density functional theory within the generalized gradient approximation (GGA). Using the Axial Next-Nearest-Neighbor Ising model extracted from the GGA calculations, we have also studied the energetics for more than 6 million kinds of nonequivalent stacking polytypes with up to L = 30, whose configurations have been deduced by the efficient polytype generation algorithm [E. Estevez-Rams and J. Martinez-Mojicar, Acta Crystallogr., Sect. A: Found. Crystallogr. 64, 529 (2008)], and illustrated some trends of structural and energetic properties for these compounds.

Crystallinity of 4H-SiC bulk crystal obtained by solution growth technique was characterized mainly by KOH etching of the off-ground and serially ground specimen. Marked reduction of basal plane dislocation, threading edge and screw dislocations during the growth of on-axis crystal was confirmed. Cross-sectional TEM observation revealed the rapid reduction behavior of threading dislocations microscopically. AFM observation of as-grown morphology showed that screw dislocation dipoles is related to the reduction of threading screw dislocations and single domain formation, which is essential for establishing the high crystallinity.

We have grown high-quality long cylindrical (12 mm thick) 4H-SiC bulk crystals by the meniscus formation technique, which was first applied for the solution growth of bulk SiC. It enabled long-term growth by suppressing parasitic reactions such as polycrystal precipitation around the seed crystal. In addition, we could control the growth angle from −22° to 61° by adjusting the meniscus height. The thickness of the grown cylindrical crystals was 12 mm, which is the largest reported until now, and corresponded to a growth rate of 0.6 mm/h. Smooth morphology growth was maintained on the (000-1) C-face. In cross-sectional transmission optical microscopy images, few solvent inclusions and voids were observed. XRD measurements revealed that the FWHM values of the grown crystals were almost the same as those of the seed crystal.

We attempted the traveling solvent method (TSM) growth of SiC on 6H-SiC(0001) substrates using Si and Si-M (M=Ti, Cr and Dy) solvents at growth temperatures of 1500-1800°C. It was confirmed that 4H-SiC polytype was extremely stabilized in the highly carbon dissolved liquid phase. 4H-SiC growth on 6H-SiC, i.e. hetropolytype epitaxial growth, was observed only from Si-Dy solvent. The Dy content above 60at% was necessary to obtain 100% 4H-SiC polytype.

We performed liquid phase epitaxial growth of SiC layers on on-axis 4H-SiC substrates using Si solvent. It was found that the polytype controllability of the epilayer significantly depends on the growth process conditions. By optimizing them, polytype mixing in the epilayers can be completely suppressed. It is shown that the density of basal plane dislocations in the epilayers is much less than in the substrates due to on-axis growth. SIMS analysis showed that the concentrations of trace impurity elements (B,Al,Ti,V,Cr,Fe,Ni,P) in the epilayers are under lower detection limit. The only impurity is nitrogen resulting in an n-type layer. Carrier concentrations Nd-Na ranging from high 1016 to low 1017cm-3 are achievable.

LPE (liquid phase epitaxy) growth of low nitrogen unintentionally doped SiC epitaxial layer on on-axis 4H-SiC substrate using nitrogen getter Si based solution was investigated to realize basal plane dislocation (BPD) free epitaxial layer. A significant reduction in BPD was demonstrated.

We have successfully grown 3C-SiC(111) single crystals 10mm x 10mm in dimension on 6H-SiC(0001) substrate by the solution growth method using cold crucible technique. The growth rate of 60μm/hr was achieved. The use of Si-Ti-C ternary solution as well as the electromagnetic stirring are responsible for the relatively high growth rate in solution method. The threading dislocation density is low and the etch pit density amounts to 105-106 /cm2 at the lowest region. Polytype of the grown layer has changed from 3C to 6H with an increase in the dip depth of substrate. A mathematical model was applied to get better understanding of what happened in the crucible.

Top seeded solution growth of SiC on on-axis 6H-SiC was performed using Si solvent at growth temperature as high as 1645-1870°C. It was found that different polytypes of SiC layers were grown on 6H-SiC depending on gas species during growth. The growth under He atmosphere produced 6H-SiC homoepitaxial layers. On the other hand, the growth under N2-He atmosphere led to 3C-SiC epitaxial layers. It was obvious that the nitrogen dissolved in solvent strongly favoured the 3C-SiC polytype formation on 6H-SiC. We also conducted characterization of 3C-SiC layers grown on 6H-SiC (0001)Si by TEM, molten KOH etching and precise XRD measurement.

Solution growth on off-axis 4H-SiC sublimation substrate as a buffer layer for the subsequent CVD epitaxial growth was investigated. Dislocation conversion and propagation from the substrate to the CVD epitaxial layer through the solution grown buffer layer was inspected by molten KOH etch pit observation. Effective dislocation conversion from BPD to TED as an effect of the buffer layer insertion with no drastic change in the total EPD was confirmed.

We carried out the characterization of the crystallinity of the solution growth self-standing silicon carbide (SiC) crystals, which were grown from Si-C-Ti ternary solution with Accelerated Crucible Rotation Technique (ACRT). The self-standing crystal exhibited homogeneous green color without cracks and inclusions. The crystallinity of the self-standing crystal was characterized by various precise XRD diffraction measurements, such as の-scan rocking curve measurement, X-ray topography and reciprocal lattice mapping. The Full Width at Half Maximum (FWHM) of the の-scan rocking curves was about 20 arcsec. The X-ray topography showed a large area with a homogeneous orientation. The reciprocal lattice mapping exhibited a sharp single peak indicating the excellent crystallinity. Finally we confirmed rather high crystallinity of the self-standing crystals by etch pits measurement using molten KOH etching.

We performed solution growth of SiC single crystals from Si-Ti-C ternary solution using the accelerated crucible rotation technique (ACRT). It was confirmed that the growth rate exceeding 200 μm/hr was achievable by several ACRT conditions. This high growth rate might be due to the enhancement of the carbon transport from the graphite crucible to the growth interface using the ACRT. Moreover, the incorporation of inclusions of the Si-Ti solvent in the grown crystal was significantly suppressed by using the ACRT. It was thought that the intensive convection near the growth interface resulted in not only the marked increase of SiC growth rate but also the superior homogeneity in the surface morphology. It was concluded that faster stable growth can be accomplished in the SiC solution growth using the ACRT.

We carried out the growth of single crystalline silicon carbide (SiC) from Si-C-X (X= Co, Fe) ternary solutions. These ternary solutions are expected to show large carbon solubility compared with Si solvent (self-flux) by means of CALPHAD (CALculation of PHAse Diagrams) method. We investigated the growth rate and the polytype of the grown crystal from the ternary solutions. Then we found that the growth rate from the ternary solutions is much larger than that from the self-flux. The growth rate from Si-C-Co (Si-C-Fe) system was about 6mm/hr (12mm/hr) while that from the self-flux was only 2mm/hr. The grown crystal from the ternary solutions is classified into 6H that takes over the seed polytype.