Search

This work studied the influence of hydrogel’s physical properties (geometry and hierarchical roughness) on the in vitro sorption/release profiles of molecules. To achieve this goal, chitosan (CS) solutions were cast in 3D-printed (3DP) molds presenting intricate shapes (cubic and half-spherical with/without macro surface roughness) and further immersed in alkaline solutions of NaOH and NaCl. The resulting physically crosslinked hydrogels were mechanically stable in aqueous environments and successfully presented the shapes and geometries imparted by the 3DP molds. Sorption and release profiles were evaluated using methyl orange (MO) and paracetamol (PMOL) as model molecules, respectively. Results revealed that distinct MO sorption/PMOL release profiles were obtained according to the sample’s shape and presence/absence of hierarchical roughness. MO sorption capacity of CS samples presented both dependencies of hierarchical surface and geometry parameters. Hence, cubic samples without a hierarchical surface presented the highest (up to 1.2 × greater) dye removal capacity. Moreover, PMOL release measurements were more dependent on the surface area of hydrogels, where semi-spherical samples with hierarchical roughness presented the fastest (~1.13 × faster) drug delivery profiles. This work demonstrates that indirect 3DP (via fused filament fabrication (FFF) technology) could be a simple strategy to obtain hydrogels with distinct sorption/release profiles.

Atherosclerosis is one of the leading causes of death worldwide. Although this subject arouses much interest, there are limitations associated with the biomechanical investigation done in atherosclerotic tissues, namely the unstandardized tests for the mechanical characterization of these tissues and the inherent non-consensual results obtained. The variability of tests and typologies of samples hampers direct comparisons between results and hinders the complete understanding of the pathologic process involved in atherosclerosis development and progression. Therefore, a consensual and definitive evaluation of the mechanical properties of healthy and atherosclerotic blood vessels would allow the production of physical biomodels that could be used for surgeons’ training and personalized surgical planning. Additive manufacturing (AM), commonly known as 3D printing, has attracted significant attention due to the potential to fabricate biomodels rapidly. However, the existing literature regarding 3D-printed atherosclerotic vascular models is still very limited. Consequently, this review intends to present the atherosclerosis disease and the consequences of this pathology, discuss the mechanical characterization of atherosclerotic vessels/plaques, and introduce AM as a potential strategy to increase the understanding of atherosclerosis treatment and pathophysiology.

One of the leading causes of death is cardiovascular disease, and the most common cardiovascular disease is coronary artery disease. Percutaneous coronary intervention and vascular stents have emerged as a solution to treat coronary artery disease. Nowadays, several types of vascular stents share the same purpose: to reduce the percentage of restenosis, thrombosis, and neointimal hyperplasia and supply mechanical support to the blood vessels. Despite the numerous efforts to create an ideal stent, there is no coronary stent that simultaneously presents the appropriate cellular compatibility and mechanical properties to avoid stent collapse and failure. One of the emerging approaches to solve these problems is improving the mechanical performance of polymeric bioresorbable stents produced through additive manufacturing. Although there have been numerous studies in this field, normalized control parameters for 3D-printed polymeric vascular stents fabrication are absent. The present paper aims to present an overview of the current types of stents and the main polymeric materials used to fabricate the bioresorbable vascular stents. Furthermore, a detailed description of the printing parameters’ influence on the mechanical performance and degradation profile of polymeric bioresorbable stents is presented.

The use of additive manufacturing technologies for biomedical applications must begin with the knowledge of the material to be used, by envisaging a very specific application rather than a more general aim. In this work, the preliminary study was focused on considering the cartilaginous tissue. This biological tissue exhibits different characteristics, such as thickness and mechanical properties, depending on its specific function in the body. Due to the lack of vascularization, cartilage is a supporting connective tissue with limited capacity for recovery and regeneration. For this reason, any approach, whether to repair/regenerate or as a total replacement, needs to fulfill the adequate mechanical and chemical properties of the surrounding native cartilage to be successful. This work aims to explore the possibility of using new polymers for cartilage total replacement approaches with polymeric materials processed with the specific 3D printing technique of fused filament fabrication (FFF). The materials studied were Nylon® 12 (PA12), already described for this purpose, and LAY-FOMM® 60 (FOMM). FOMM has not been described in the literature for biomedical purposes. Therefore, the chemical, thermal, swelling capacity, and mechanical properties of the filaments were thoroughly characterized to better understand the structure–properties–application relationships of this new polymer. In addition, as the FFF technology is temperature based, the properties were also evaluated in the printed specimens. Due to the envisaged application, the specimens were also characterized in the wet state. When comparing the obtained results with the properties of native cartilage, it was possible to conclude that: (i) PA12 exhibits low swelling capacity, while FOMM, in its dry and wet forms, has a higher swelling capacity, closer to that of native cartilage; (ii) the mechanical properties of the polymeric materials, especially PA12, are higher than those of native cartilage; and (iii) from the mechanical properties evaluated by ultra-micro hardness tests, the values for FOMM indicate that this material could be a good alternative for cartilage replacement in older patients. This preliminary study, essentially devoted to expanding the frontiers of the current state of the art of new polymeric materials, provides valuable indications for future work targeting the envisaged applications.