To enhance the friction and wear performance of cemented carbide, textured microholes were machined on micro Electron Discharge Machining (EDM) on the tool rake face, and Calcium Fluoride (CaF2) powders were burnished into the microholes. The friction and wear characteristics of the microhole-textured tool filled with CaF2 were investigated using sliding friction tests and dry cutting tests. Results exhibited that the working temperature could affect the tribological performance of the microhole-textured tool filled with CaF2 due to the temperature-sensitive nature of CaF2. There is no obvious lubrication effect for the textured tool filled with CaF2 at room temperature, while it was shown to be more effective in improving tribological property at a cutting speed of higher than 100 m/min with a corresponding to cutting temperature of 450 °C. The possible mechanisms for the microhole-textured tool filled with CaF2 were discussed and established. [ABSTRACT FROM AUTHOR]

PTFE coatings were deposited on the Si 3 N 4 /TiC ceramic substrate by using spray technology. The surface and cross-section micrographs, adhesive force of coatings with substrate, surface roughness and micro-hardness of the coated ceramics were examined. The friction and wear behaviors of ceramic samples with and without coatings were investigated through carrying out dry sliding friction tests against WC/Co ball. The test results indicated that the coated ceramics exhibited rougher surface and lower micro-hardness, and the PTFE coatings can significantly reduce the surface friction and adhesive wear of ceramics. The friction performance of PTFE-coated sample was affected by applied load due to the lower surface hardness and shear strength of coatings, and the main wear failure mechanisms were abrasion wear, coating delamination and flaking. It can be considered that deposition of PTFE coatings is a promising approach to improve the friction and wear behavior of ceramic substrate. [ABSTRACT FROM AUTHOR]