The purpose of this paper is to investigate the impact behaviour and damage characterization of carbon fibre reinforced aluminium hybrid laminates (Al/CFRP) in comparison to classic carbon fibre reinforced polymer (CFRP) at low-velocity and low-energy impact. Impact damage characteristic with damage initiation and progression, internal failure modes and understanding of the role of the metal layers in the impact behaviour under low-energy were examined and discussed. The damage mechanism of the tested laminates is very complex. There is an internal degradation of the material, with the plastic deformation in case of fibre metal laminates. Characteristic matrix cracks (bending and shearing cracks) running at the fibre–matrix interface in composite layers are the first damage mode. The critical damage mode is delaminations observed between composite layers with different orientation as well as delaminations at the metal–composite interface in fibre metal laminates. For the tested materials, particularly carbon fibre reinforced composites, the absorbed impact energy is mainly connected with elastic response and damage of the laminate. In case of fibre metal laminates the absorbed energy is also connected with plastic deformation of the laminate, occurring especially in the metal layers. High impact resistance of fibre metal laminates indicates that metal (aluminium) layers may prevent delamination propagation and impactor penetration. [ABSTRACT FROM AUTHOR]

Abstract: This work presents a numerical analysis of damage of composite materials with polymeric matrix reinforced with carbon fibres subject to static tension. Verification of numerical analyses was conducted with experimental methods – strength tests and microstructural observations. The methodologies applied were: the material damage modelling methodology based on XFEM (eXtended Finite Element Method) and contact interactions in a fibre–matrix connection layer using the CZM method (Cohesive Zone Method – Surface-based Cohesive Behaviour). ABAQUS/Standard software was the applied numerical tool. Microstructural analysis and numerical simulations indicate the fact that initiation of composite material damage takes place at the interface as a result of cracking and loss of fibre/matrix connection. This results in weakening of the composite microstructure in this area through the initiation of a reinforcement cracking process, which leads to further structural degradation, consisting in propagation of matrix cracking and, as a result, complete damage of the composite structure. The presented research of carbon/epoxy composite damage confirmed the adequacy of the prepared numerical model. [Copyright &y& Elsevier]