Reactor pressure vessel (RPV) is the critical un-changeable component of the reactor during its service lifetime, which prevents the radioactive leak of the nuclear power plant core. The irradiation test (about 10 × 10 19 cm − 2 , E > 1 MeV) in research reactor of the pressure vessel material was carried out, and the charpy impact test has been carried out before and after the neutron irradiation. Analysis of the impact energy and the fracture morphology has been done to estimate the embrittlement due to neutron irradiation. It shows that the main effects of neutron irradiation to fracture are the crack initiation and stable expansion process. And there also are a small amount of intergranular fracture in the unstable crack expansion after neutron irradiated which aware us pay more attention to the increasing intergranular fracture behavior of higher neutron fluence level after 60a nuclear power plant operation. [ABSTRACT FROM AUTHOR]

F82H is the Japanese reference reduced-activation ferritic-martensitic (RAFM) steel for fusion blanket applications. The harsh environment of a fusion reactor, such as neutron irradiation and He/H damage, can result in significant degradation of F82H fracture toughness. Therefore, understanding the fracture toughness behavior of F82H in the fusion environment is critical to ensure the long-term safe operation of the fusion reactor. In this paper, we summarize seven irradiation campaigns of the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory (ORNL) covering five variants of F82H steels, including F82H IEA, F82H Mod3, F82H doped with 1.4% natural Ni, F82H doped with 1.4% 58Ni, and F82H doped with 1.4% 60Ni. The irradiation temperatures covered the range from 220 °C to 530 °C and the neutron irradiation dose spanned 4 dpa to 70 dpa. The effects of neutron irradiation temperature, dose, materials composition, Ni doping, and He production on F82H fracture toughness are discussed. Our results showed that irradiation embrittlement monotonically decreased with increasing irradiation temperature until 400 °C for F82H IEA and F82H Mod3. F82H Mod3 showed better fracture toughness than F82H IEA both before and after neutron irradiation. We determined that 1.4% Ni alloying can be applied to F82H for simulating He effect in a fission reactor without jeopardizing the fracture toughness of the material. However, more studies are needed to understand the effect of high dose (>20 dpa) and He production on F82H fracture toughness. [ABSTRACT FROM AUTHOR]