Search

In this study, the investigation of the oil painting on canvas I Tesori del Mare made by Plinio Nomellini in 1901 is presented. The aim of the research was threefold: the examination of the state of conservation in view of the restoration treatment, together with the identification of the causes of degradation and the study of the artistic technique. During the years, the artwork underwent several cleaning and fixing interventions, resulting in a patchy appearance of the surface. Nevertheless, the presence of consistent liftings persists, while the protective coating shows uneven chromatic alteration, both requiring further analysis. Multispectral imaging allowed for better visualization of the figuration's structure and the restored areas. The combined use of Raman spectroscopy, Fourier Transform Infrared spectroscopy in the Attenuated Total Reflection mode (FT-IR ATR), and Scanning Electron Microscopy coupled with an Energy Dispersive Spectroscopy (SEM/EDS) enabled better understanding of the stratigraphy through the identification of some pigments, the binder, and the aged varnish layer on the top. SEM/EDS highlighted the presence of zinc in both the ground layer and the paint layers. Furthermore, FT-IR ATR spectroscopy showed peaks related to metal soaps such as zinc stearate, which are known to cause severe delamination of the paint layers, explaining the recurring lifting issues. Eventually, the varnish layer was found to be acrylic resin, presumably mixed with varnishes applied in past restoration treatments. [ABSTRACT FROM AUTHOR]

Organic remains preserved on eight copper alloy artifacts of the Byzantine Collection of the Benaki Museum with an Egyptian provenance were investigated, implementing a multi-analytical approach combining microscopy-FTIR and GC/MS. The transmission spectra of powder samples provided important information on the vessels regarding inorganic and organic components. In the latter case, subsequent extractions with a range of solvents allowed discrimination of components with different polarities and provided data on the suitability of the solvents for the acquisition of more informative spectra. GC/MS was implemented for the detailed characterization of the compounds present in the samples because of the complex nature of the residues preserved. A wide range of fatty acid oxidation products was identified, including a series of α, ω-dicarboxylic acids typical of such remains. In addition, vicinal dihydroxy-docosanoic and dihydroxy-eicosanoic acid, oxidation products of erucic and gondoic acid, respectively, were detected. Both are found in abundance in oils from plants belonging to the Brassicaceae family and imply their multiple uses in medieval Egypt. [ABSTRACT FROM AUTHOR]

Abstract: The formation of metal soaps (metal complexes of saturated fatty acids) is a serious problem affecting the appearance and structural integrity of many oil paintings. Tailored model systems for aged oil paint and time‐dependent attenuated total reflection Fourier transform infrared (ATR‐FTIR) spectroscopy were used to study the diffusion of palmitic acid and subsequent metal soap crystallization. The simultaneous presence of free saturated fatty acids and polymer‐bound metal carboxylates leads to rapid metal soap crystallization, following a complex mechanism that involves both acid and metal diffusion. Solvent flow, water, and pigments all enhance metal soap crystallization in the model systems. These results contribute to the development of paint cleaning strategies, a better understanding of oil paint degradation, and highlight the potential of time‐dependent ATR‐FTIR spectroscopy for studying dynamic processes in polymer films. [ABSTRACT FROM AUTHOR]

The degradation process involving the formation of metal soaps in drying oils is a well-known problem due to cations from pigments reacting with free fatty acids from the oil. The aggregation of these carboxylates in semi-crystalline structures can lead to eruptions through the paint layers and ‘blooming’ on the surface. In this work, the metal soaps formation in presence of natural resins has been assessed and studied by means of Fourier transform infrared spectroscopy with experiments concerning the ageing of drying oil and different natural resins (shellac, dammar and colophony) in the presence of common historic pigments (smalt, ochre, umber, azurite, lead white, zinc white and titanium white). Mixtures of resins and pigments have been exposed to photo-ageing in solar box up to 1000 h, thermal ageing at 50 °C up to 1100 h and 6 month of room conditions exposure as reference. The decrease in the intensity of the carbonyl band in the spectra, as well as the contemporary increase of the metal carboxylates (in the range from 1500 to 1650 cm −1 ) absorption bands, were used as the main indicators of metal soap formation. It has been observed that some pigments, particularly zinc white and smalt, present a ‘catalytic’ effect favouring the simultaneous formation of associated oxalates. The formation of oxalates and different degradation products from natural resins in the presence of pigments is particularly important, as it deeply affects the removability of varnishes and, more generally, the cleaning processes. Moreover, it permanently modifies the interface between painting and varnish layers as well as the aesthetic aspects of the painted surfaces. The influence of natural resins reactivity with pigments and their role in the oxalate formation is an issue still unexplored. [ABSTRACT FROM AUTHOR]

The interaction of pigments and binding media may result in the production of metal soaps on the surface of paintings which modifies their visible appearance and state of conservation. To characterise more fully the metal soaps found on paintings, several historically accurate oil and egg yolk tempera paint reconstructions made with different pigments and naturally aged for 10 years were submitted to attenuated total reflectance Fourier transform infrared (ATR FTIR) microspectroscopic analyses. Standard metal palmitates were synthesised and their ATR spectra recorded in order to help the identification of metal soaps. Among the different lead-based pigments, red lead and litharge seemed to produce a larger amount of carboxylates compared with lead white, Naples yellow and lead tin yellow paints. Oil and egg tempera litharge and red lead paints appeared to be degraded into lead carbonate, a phenomenon which has been observed for the first time. The formation of metal soaps was confirmed on both oil and egg tempera paints based on zinc, manganese and copper and in particular on azurite paints. ATR mapping analyses showed how the areas where copper carboxylates were present coincided with those in which azurite was converted into malachite. Furthermore, the key role played by manganese in the production of metals soaps on burnt and raw sienna and burnt and raw umber paints has been observed for the first time. The formation of copper, lead, manganese, cadmium and zinc metal soaps was also identified on egg tempera paint reconstructions even though, in this case, the overlapping of the spectral region of the amide II band with that of metal carboxylates made their identification difficult. [Figure not available: see fulltext.] [ABSTRACT FROM AUTHOR]

Paintings and painted objects are quite susceptible to degradation, as paint layers are usually composed of complex mixtures of materials that can participate in chemical degradation processes. The identification of the constituent materials in paint (including binders, pigments, and fillers) and the degradation products within paint layers is of particular importance to ensuring the conservation of paintings, by providing important information both about their material history as well as their state of conservation. Metal fatty acid salts (metal soaps) are degradation products that can form in situ from interactions between inorganic pigments and free fatty acids in oil-based binding media, and can cause significant condition issues in paintings. Fourier transform infrared (FTIR) spectroscopy is one of the leading analytical techniques for the study of metal soaps. In this article, the materials analysis of several cross-sections from paintings and painted objects from works in Canadian collections is presented. Recent results on the use of external reflection FTIR (R-FTIR) spectroscopy to identify and map the distribution of paint components and metal soap degradation products is presented. In particular, zinc, lead, calcium, and copper fatty acid salts were all readily identified in paint cross-sections by R-FTIR spectroscopy, along with several pigments and the oil binding medium. The results shown here are among the first detailed examinations of these metal soaps in paint cross-sections using R-FTIR spectroscopy. The use of highly polished samples in which specular reflection is dominant allowed for spectral transformations to be applied to generate transmission/absorption-like spectra which facilitated identification of these species. The distribution of these species across the cross-sections was mapped by integrating characteristic absorption features in the R-FTIR spectra. Attenuated total internal reflection (ATR) FTIR spectroscopy was also performed on several samples, which provided additional compositional details at the interface of paint layers and degradation products. [ABSTRACT FROM AUTHOR]