Search

MnO2 and CeO2 were doped to improve the corrosion resistance of CSZ (calcia-stabilized zirconia), and we studied the phase formation, mechanical properties, and corrosion resistance by molten mold flux. The volume fraction of the monoclinic phase gradually decreased as the amount of MnO2 doping increased. The splitting phenomenon of the t(101) peak was observed in 2Mn_CSZ, and in 4Mn_CSZ, it was completely split, forming a cubic phase. The relative density increased and the monoclinic phase decreased as the doping amount increased, leading to an increase in Vickers hardness and flexural strength. However, in 3Mn_CSZ and 4Mn_CSZ, where cubic phase formation occurred, the tetragonal phase decreased, leading to a reduction in these properties. MnO2-doped CSZ exhibited a larger fraction of the monoclinic phase compared to the original CSZ after the corrosion test, indicating worsened corrosion resistance. These results are attributed to the predominant presence of Mn3+ and Mn2+ forms, rather than the Mn4+ form, which has a smaller basicity difference with SiO2, and due to the low melting point. The monoclinic phase fraction decreased as the doping amount of CeO2 increased in CeO2-doped CSZ, but the rate of decrease was lower compared to MnO2-doped CSZ. The monoclinic phase decreased as the doping amount increased, but the Vickers hardness and flexural strength showed a decreasing trend due to the low relative density. The destabilization behavior of Ca in SEM-EDS images before and after corrosion was difficult to identify due to the presence of Ca in the slag, and the destabilization behavior of Ce due to slag after corrosion was not observed. In the XRD data of the specimen surface after the corrosion test, the fraction of the monoclinic phase increased compared to before the test but showed a lower monoclinic phase fraction compared to CSZ. It is believed that CeO2 has superior corrosion resistance compared to CaO because Ce predominantly exists in the form of Ce4+, which has a smaller difference in basicity within the zirconia lattice. [ABSTRACT FROM AUTHOR]

The effects of CaO content and post-heat treatment were investigated on the phase stability and mechanical and thermal properties of Ca-PSZ. ZrO2 specimens with 5–10 mol% CaO were sintered, and post-heat treatment was performed at 1200 °C for 100 h. Subsequently, to test and analyze the crystal structure and the microstructure, the mechanical and thermal properties of the specimens were evaluated. All specimens were partially stabilized by 5–10 mol% CaO (5CSZ–10CSZ) in a mixed monoclinic and tetragonal phase; however, peaks of the secondary phase of CaZrO3 were observed in 10CSZ. The ratio of the monoclinic phase decreased from 62.50% (5CSZ) to 21.02% (10CSZ) as the CaO content increased. Additionally, the monoclinic phase ratio decreased from 59.38% (5CSZ) to 19.57% (9CSZ) after the post-heat treatment; an increase to 24.84% was observed for 10CSZ. An increase in Vickers hardness from 676.02 to 1256.25 HV and flexural strength from 437.7 to 842.7 MPa was observed with increasing CaO content. The post-heat treatment resulted in further increases in these values as the CaO content increased from 5CSZ to 9CSZ; however, the Vickers hardness and flexural strength of 10CSZ decreased by approximately 8% and 9%, respectively. The thermal expansion coefficient exhibited the same tendency as the mechanical properties. This coefficient increased from 8.229 × 10−6 to 9.448 × 10−6 K−1 with increasing CaO content and was enhanced after the post-heat treatment in 5CSZ to 9CSZ; however, the thermal expansion coefficient of 10CSZ decreased by approximately 4% after the post-heat treatment. The mechanically and thermally stable tetragonal phase increased, and the monoclinic phase decreased as the doped Ca replaced the Zr sites, as was confirmed by the X-ray diffraction (XRD) analysis. The post-heat treatment and the increased Ca addition further facilitated the replacement of Zr sites by Ca. However, at high Ca concentrations of 10CSZ, an equilibrium phase of CaZrO3 was formed as a secondary phase at the post-heat treatment temperature, resulting in low performance. [ABSTRACT FROM AUTHOR]