Search

Melamine–formaldehyde resin-coated bamboo fiber (MFBF) and ammonium polyphosphate (MFAPP) were prepared, and then flame-retardant polypropylene (PP)/bamboo fiber composites based on MFBF/MFAPP were obtained by melt blending. The water resistance, flame retardant, and thermal properties of the composites were studied. The results show that MFBF and MFAPP have excellent water resistance with the water contact angles 130.85° and 119.78°, respectively. Compared with pure PP, the limit oxygen index (LOI) of the prepared composite increased from 18.5 to 25.5% with the UL-94V-0 rating. The peak heat release rate of the composite decreased from 1011.8 to 344.3 kW·m−2 and the total heat release decreased from 100.6 to 58.8 MJ·m−2. Meanwhile, the total smoke release decreased from 1453.3 to 922.0 m2·m−2. After soaking in 70 °C water for 36 h, the composite still reached the V-0 rating in UL-94 test, demonstrating a good water resistance. This work provides an effective method to improve the water resistance and flame retardancy of PP/bamboo fiber composites. Melamine–formaldehyde resin-coated bamboo fibers (MFBF) and ammonium polyphosphate (MFAPP) were prepared, then flame-retardant PP/BF composites were obtained based on MFBF/MFAPP. The results show that prepared composite exhibited excellent water resistance and flame-retardant properties. [ABSTRACT FROM AUTHOR]

The more efficient and hydrophobic modificated ammonium polyphosphate (M-APP) and charring agent (M-CA) were prepared based on sol–gel method, and they were used in the preparation of water-resistant and flame-retardant polypropylene (PP) composites. The results showed that the contact angles of M-APP and M-CA were 135.11° and 137.89°, respectively. The flame-retardant and thermal properties of the PP composites were also studied. The results showed that the flame retardancy of PP loaded with 30 mass% intumescent flame retardant (M-APP/M-CA = 3:1) was significantly increased. The limiting oxygen index (LOI) reached 36.8% and passed UL-94 V-0. The peak heat release rate and total heat release of the PP composite decreased from 1011.77 to 134.43 kW·m−2 and 100.58 to 6.86 MJ·m−2, respectively. The peak smoke production rate and total smoke release decreased from 0.13 to 0.0056 m2·s−1 and 1453.09 to 74.82 m2·m−2. The PP composite with M-APP/M-CA = 3:1 also exhibited excellent water resistance, and it could still reach UL-94 V-0 after soaking in 70 ℃ water for 168 h. [ABSTRACT FROM AUTHOR]

Fire alarm systems are essential for protecting lives and properties from fire hazards. However, most of the existing fire alarm nanopapers rely on the resistance reduction after heating, which requires direct contact with the flame. In this study, we present a novel fire alarm nanopaper (CMPA) based on heat-triggered shape recovery. The CMPA is composed of hydroxypropyl methyl cellulose (HPMC) as the matrix and 2D nanomaterials M(OH)(OCH 3) as fillers. When the temperature of CMPA exceeded the glass transition, the thrice-folded CMPA-1.0 flattened in 30s and connected to the alarm circuit based on its conductive surface. According to the results, the CMPA-1.0 with a thickness of about 0.2 mm had an efficient electromagnetic shielding of 42.1 dB. Moreover, the CMPA-1.0 self-extinguished rapidly after being ignited with its original shape preserved. The peak heat release rate of CMPA-1.0 was 108.9 W/g, which was 61.9 % lower than that of HPMC. Furthermore, the thermal conductivity of CMPA-1.0 reached to 0.317 W m−1 K−1, which was 40.8 % higher than that of HPMC, reducing the heat accumulation effectively. This work shows that CMPA is an ideal material for sensitive and safe early fire alarm, and the strategy based on heat-triggered shape recovery is promising in fire alarm application. [ABSTRACT FROM AUTHOR]

Phosphorylated celluloses (PCFs) were obtained via reaction of microcrystalline cellulose with phosphorous acid in molten urea. Fourier transform infrared spectroscopy and scanning electron microscopy were used to observe the chemical structure and microstate of the PCFs. A flame retardant glutaraldehyde cross‐linked poly (vinyl alcohol)/PCF aerogel was fabricated using a melt cross‐link and freeze‐dried method. The results of thermogravimetric analysis confirmed that the thermal stability of the poly(vinyl alcohol) (PVA) aerogels incorporating PCF is more outstanding. The peak of heat release rate (PHRR) and the total heat release (THR) values of the PCA/PCF10 aerogel deceased obviously by 33.8 and 64%, respectively, compared to the corresponding values for the pure PVA aerogel; these changes confirm that the PCA/PCF aerogel had better flame‐retardant properties than the pure PVA aerogel. Moreover, the fire performance index and fire growth index indicate that the introduction of PCF would diminish the occurrence of fire. [ABSTRACT FROM AUTHOR]