Gypsum-based composites were prepared via a slurry casting process using construction gypsum as the binding material and poplar fibers as reinforcing material. The effects of different fiber content and curing time on the mechanical properties, water resistance, and flame retardancy of these composites were investigated, and the influence mechanism was characterized by infrared spectroscopy, scanning electron microscopy, and X-ray diffractometry. The results showed that the best composite mechanical strength was achieved with 10% poplar fiber- content, and the absolute dry flexural and compressive strengths reached 3.59 and 8.06 MPa, respectively. Compared with pure gypsum, the flexural strength and compressive strength increased by 10% and 19%, respectively. The inclusion of fibers somewhat prevented the migration of free water within the composites and enhanced their water resistance. At 10% fiber content, the composite's 24 h water absorption rate was 34.3%, 8% lower than that of pure gypsum, with a softening coefficient of 0.55. However, fiber content increases the porosity of gypsum-based composites. When heated, this increased porosity accelerates' heat conduction within the matrix, raising the peak and total exothermic rates, thereby weakening the composites' inherently flame-retardant properties. Poplar-fiber-reinforced gypsum-based composites offered superior performance in commercial applications, compared to pure gypsum board, providing a sustainable and green alternative for ceilings, partitions, and other applications, while broadening the prospects for gypsum-based composites in the engineering field. [ABSTRACT FROM AUTHOR]

Biodegradable composites were prepared from polylactic acid (PLA) and bamboo charcoal (BC) by melt blending and hot pressing. The effects of BC addition on the mechanical properties, water absorption, DMA, TGA, DSC, and CONE of BC/PLA composites were investigated. The microscopic morphology of the composites was analyzed by SEM. The results showed that for BC addition of 40 wt%, the mechanical strength, thermal properties, and flame retardant properties of the composites were improved compared with those of PLA, with a 2.24 % increase in flexural strength and a 1535 % increase (500 °C) in TG mass retention rate. The crystallinity increased by 129.66 %, the peak loss factor decreased by 31.15 %, the time required for combustion was delayed by 168 s, the peak heat release rate decreased by 29.40 %, the carbon residue rate detected by cone calorimetry increased by 48.50 %, and the peak mass loss rate decreased by 48.82 %. The addition of BC enhanced the crystallization capacity of PLA, and improved the thermal properties and flame retardant properties of the prepared composites. The results showed that materials prepared with a BC content of 40 wt% exhibited the best overall performance. • Bamboo charcoal/polylactic acid biodegradable composites were prepared by melt blending and hot pressing. • The effects of the amount of added BC on properties of composites and their mechanisms were determined. • BC/PLA composites obtained high water resistance, thermal properties, thermal stability, and flame retardant properties. • The application field of Bamboo charcoal has been expanded. [ABSTRACT FROM AUTHOR]