Abstract: Zirconium-based ceramics and composites such as ZrC, ZrB2, ZrC–SiC, ZrB2–SiC–ZrC, and ZrB2–SiC–ZrC–ZrSi were synthesized in fine powder form via combustion synthesis (CS) using ZrSiO4, Mg, C, B, and NaCl as raw materials. Temperature distributions in the combustion wave were measured by thermocouples and used to estimate the combustion temperature and wave propagation velocity. The influence of the NaCl mole fraction on the combustion parameters, phase composition, and particle size of the composite powders was investigated. The experimental results revealed that the combustion temperature and particle size of the composites have a stable decreasing tendency with increase in the NaCl mole fraction in the starting mixture. It was found that near the combustion limit (1.5mol NaCl), the combustion temperature drops below 1500°C and the particle size reaches the nanometer scale. [Copyright &y& Elsevier]

In this study, we examined the effect of potassium perchlorate (KClO 4 ) and magnesium hydroxide (Mg(OH) 2 ) additives on the combustion behavior of a ZrO 2  + 2Mg mixture to produce a fine powder of zirconium metal. The results of thermodynamic analysis and experiments imply that nearly 0.04 mol of KClO 4 is needed to initiate a combustion reaction in the ZrO 2  + 2Mg system. As the amount of KClO 4 increases from 0.04 to 0.1 mol, the combustion temperature increases from 1250 to 1850 °C. This results in formation of fine zirconium powder with a typical particle size of less than 5 µm, and with 1.4–2.2 wt% residual oxygen. Subsequent reduction of particle size to 100–500 nm, and oxygen content to <1.0 wt% was achieved by adding Mg(OH) 2 . The as-prepared Zr powder was mixed with nitrocellulose and printed onto 10–100 µm thin-layers to study their burning stability. The wave propagation in a thin layer was on the order of 0.35–30 cm/s, which is suitable for applications requiring localized power generation. [ABSTRACT FROM AUTHOR]