Search

A series of white light emitting Pr3+ activated SrWO 4 phosphors are synthesized by most facile solid state reaction routes. The structural properties are investigated by X-ray diffraction (XRD) spectroscopy, Field Emission Scanning Electron Microscopy (FESEM), Energy dispersive X-ray (EDX) spectroscopy, Fourier transform infrared (FTIR) spectroscopy and X-ray photoemission spectroscopy (XPS). The optical properties are elaborated in detail using UV–visible–NIR spectroscopy and Photoluminescence (PL) spectroscopy. Rietveld refinement of obtained XRD data is performed to investigate the crystal structure and crystallographic parameters. The photoluminescence measurements ensure that the developed phosphors emit bright white light under UV excitation of 242 nm and blue excitation of 448 nm. The maximum emission intensity is achieved at 3 mol% doping of Pr3+, followed by concentration quenching due to dipole-dipole interactions. The decay of electrons from the most populated 3P 0 state in all the samples follows the single exponential nature. The average decay time varies in the same manner as the emission intensity with Pr3+ concentration. The color purities of the lights emitted from all the materials under 242 nm and 448 nm excitations are low (close to 10%) and hence suitable for white light. A bright white LED is successfully fabricated by coating the optimised phosphor SrWO 4 : 3 mol% Pr3+ on a 460 nm blue LED chip. The interesting results recommend that the proposed material can be used in developing single phase white-LED. [ABSTRACT FROM AUTHOR]

An array of Eu3+ doped Ba 2 GdSbO 6 luminescent materials have been synthesized by the conventional solid-state (high temperature) reaction route. Surface morphology has been studied via Field Emission Scanning Electron Microscopy. The structural and optical behaviors have been studied using X-Ray Diffraction (XRD), FTIR, Raman spectroscopy, Diffuse reflectance spectroscopy, Photoluminescence excitation (PLE), and Photoluminescence emission (PL) spectra. FTIR and Raman's spectra provided the chemical functional group and different vibrational levels within the samples. The calculated optical band gap was 4.40 eV and 4.47eV for pure and optimized samples respectively. Photoluminescence emission curves have been recorded for 245 nm of excitation wavelength and the highest emission peak was focused at 595 nm corresponding to 5D 0 → 7F 1. Similarly, the Photoluminescence excitation curves were monitored at the emission wavelength of 595 nm and a broad charge transfer band (CTB) was observed from 230 to 285 nm. The emission spectra show the concentration quenching effect beyond the 2 mol% Eu3+ concentration. The corresponding transitions of Eu3+ were further utilized to obtain the Judd-Ofelt (J-O) transition intensity parameters Ω λ (λ = 2, 4) for each sample. Additionally, by studying decay kinetics, the average lifetime of the red emission of the samples has been evaluated, which was 4.622 ms. The photometric study also reveals the CIE coordinates, color purity and CCT values of the proposed phosphor material. Thus, the results obtained from these characterizations, suggest that the prepared sample may behave as a potential candidate in the case of UV-excited red light-emitting phosphor material for light-emitting diodes and field emission devices. • Ba 2 GdSbO 6 : Eu3+ phosphors have been synthesized by solid-state reaction method. • Rietveld refinement has been carried out for better crystal structure analysis. • Raman studies for this host Ba 2 GdSbO 6 have been carried out for the first time. • The phosphors show intense photoluminescence emission with very high color purity. • Judd-Ofelt analysis has been done to understand the spectroscopic behavior of the proposed phosphor material. [ABSTRACT FROM AUTHOR]