Oxide dispersion strengthened (ODS) steels are being developing for application as advanced fast reactor cladding and fusion blanket materials, in order to allow increased operation temperature. Oxidation testing of ODS steel was conducted under a controlled dry air atmosphere to evaluate the high temperature oxidation behavior. This showed that 9Cr-ODS martensitic steels and 12Cr-ODS ferritic steels have superior high temperature oxidation resistance compared to 11 mass% Cr PNC-FMS and 17 mass% Cr ferritic stainless steel. This high temperature resistance is attributed to earlier formation of the protective α-Cr2O3 on the outer surface of ODS steels. [Copyright &y& Elsevier]

Abstract: Oxide dispersion strengthened (ODS) ferritic steels, which are the most promising candidate materials for advanced fast reactor fuel elements, have exceptional creep strength at 973K. The superior creep property of 9Cr-ODS ferritic steels is ascribed to the formation of a nonequilibrium phase, designated as the residual ferrite. The yield strength of the residual ferrite itself has been determined to be as high as 1360MPa at room temperature from nanoindentation measurements. The creep strength is also enhanced by minimizing the number of packet boundaries induced by the martensitic phase transformation. The creep strain occurs at a lower stress than that necessary for the deformation of the intragrain regions, which are strengthened by an interaction between nanosize oxide particles and dislocations; this occurs by sliding at weaker regions such as at the grain boundaries and packet boundaries. It is found that 9Cr-ODS ferritic steels behave as fiber composite materials comprising the harder residual ferrite and the softer tempered martensite. [Copyright &y& Elsevier]

Abstract: Friction stir welding was applied to the wrapper tube materials, 11Cr-ferritic/martensitic steel, designed for fast reactors and defect-free welds were successfully produced. The mechanical and microstructural properties of the friction stir welded steel were subsequently investigated. The hardness values of the stir zone were approximately 550Hv (5.4GPa) with minimal dependence on the rotational speed, even though they were much higher than those of the base material. However, tensile strengths and elongations of the stir zones were high at 298K, compared to those of the base material. The excellent tensile properties are attributable to the fine grain formation during friction stir welding. [Copyright &y& Elsevier]