The article explores the photoluminescence properties of UV, near-UV and blue excited BaWO 4 : Eu3+ red phosphors. The optical band gap narrowing is observed after adding Eu3+ ions. The excitation spectra exhibit a broad peak centred at 255 nm and several narrow peaks of Eu3+ ions at 362, 382, 395, 415 and 465 nm. The three peaks located at 255 (UV), 395 (near-UV) and 465 nm (blue) are the most intense and suitable for the excitation of the sample. The spectral profile of the emission spectra irradiated at 255, 395 and 465 nm are identical. The brightest emission is realized at 18 mol% doping of Eu3+ ions at 255 and 465 nm excitations. However, the optimum concentration is 16 mol% at 395 nm excitation. The phosphors emit highly pure red lights with color purity 98.192%, 97.794% and 98.693% for the optimised concentration under UV, near-UV and blue excitations of 255, 395 and 465 nm, respectively. The quantum efficiency of BaWO 4 : 16 mol% Eu3+ phosphor is calculated as∼48.234% at 395 nm excitation. The emission intensity parameters are calculated in view of the Judd-Ofelt theory. The spectroscopic parameters like radiative transition probability, radiative lifetime, branching ratio and stimulated emission cross-section are further evaluated from the three emission spectra recorded at 255, 395 and 465 nm excitations. The derived results advocate the use of synthesized material as a red phosphor in white-LED, laser and display devices. [ABSTRACT FROM AUTHOR]

Charge transfer band (CTB) transition significantly improves the photoluminescence properties of phosphor materials due to its higher absorption efficiency than the characteristic excitations of rare-earth ions. La 2 Zr 2 O 7 (LZO): Pr3+ phosphors with varying doping concentrations of Pr3+ were synthesized through the hydrothermal method. The formation of the pure pyrochlore phase was confirmed from powder X-ray diffraction (XRD). The structural analysis was performed from Rietveld refinement of the XRD data. Field emission electron microscope (FESM) equipped with EDX spectroscopy was used to study the surface morphology and elemental compositions. X-ray photoelectron spectroscopy (XPS) analysis of the optimized sample provides the bonding state of the compositions. Under 257 nm CTB excitation, the photoluminescence emission spectra (PL) exhibit all the characteristic emission peaks of Pr3+ ion. The transitions involved in the excitation and emission process have been shown in the energy level diagram of Pr3+ ions. The Concentration quenching effect was explained from Bless relation and Dexter energy transfer theory between activator ions. Decay curves of the prepared phosphors show bi-exponential behavior. The up-conversion emission spectra were recorded under 980 nm laser excitation. The optical transition in the UV–Vis range was investigated based on the diffuse reflectance spectra, and the results match well with the excitation spectra. The photometric study informs the color and the quality of the emitted light. The outcomes produce a new synthesis method to prepare La 2 Zr 2 O 7 :Pr3+ nano phosphor that can be an excellent candidate for solid-state lighting and UV/NIR to the visible converter in solar cell applications. [Display omitted] [ABSTRACT FROM AUTHOR]