A novel diaminodiphenylmethane (DDM) modified ammonium polyphosphate (APP) flame retardant, DDP, was successfully synthesized via ion-exchange reaction. DDP was introduced into epoxy resins (EPs) to reduce flammability. A comparable level of DDP exerts better flame-retardant and smoke suppression efficiencies in EP than APP. An EP blend containing 15 wt% DDP displays a limiting oxygen index (LOI) value of 37.1% and a UL 94 V-0 rating, and further exhibits a 32.3% reduction in total heat release and a 48.0% reduction in total smoke production compared with pure EP. The presence of DDP greatly facilitates char formation during combustion, and the char mass from thermal decomposition of an EP blend is 37.8% smaller than that of an EP blend containing 15 wt% DDP at 800 °C. The incorporation of DDP into EP blends has a smaller impact on the glass transition temperature and tensile strength than those of a comparable level of APP. This reflects the better compatibility of DDP with the EP matrix compared with that for APP. [ABSTRACT FROM AUTHOR]

• A phosphaphenanthrene/benzimidazolone-containing flame retardant (POBDBI) was synthesized successfully. • POBDBI imparted excellent flame retardancy and smoke suppression to EP. • POBDBI exerted flame-retardant effect both in condensed phase and gaseous phase. A novel flame retardant POBDBI was generated by the reaction of p-dibenzaldehyde, 5-amino-2-benzimidazolinone and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), and employed to epoxy resin. The structure of POBDBI was measured by FT-IR and NMR tests. Then flame-retardant EP was fabricated by using POBDBI as a flame-retardant. The thermal stability, flame-retardant performance and fire behavior were investigated by a serious of comprehensive instruments. Combustion tests show the flame-retardant performance of composite materials has been significantly improved. For example, the EP/POBDBI-1.0 with the phosphorus content of 1.0% accorded a V-0 rating and its limiting oxygen index (LOI) value increased to 36.5%. Besides, total smoke production (TSP), peak heat release rate (PHRR) and total heat release (THR) of EP/POBDBI-1.0 dropped significantly, and the corresponding values were decreased by 48.4%, 48.9% and 8.7%, respectively. At the same time, the composition, morphology of chars and gaseous products of POBDBI were studied by X-ray photoelectron spectroscopy (XPS), FT-IR, scanning electron microscope (SEM) and Py-GC/MS. These results presented that POBDBI could not only exerted free radical capture effect, but also enhanced the density of char residue. [ABSTRACT FROM AUTHOR]