Search

In this article an alternative high yield route for the synthesis of CoSb3-based unfilled skutterudites is presented. Using low-melting temperature salts of the constituents, melting and mixing the ...

Skutterudites are known to be efficient thermoelectric (TE) materials in the temperature range from 600 K to 900 K. Dimensionless figure of merit (ZT) for filled skutterudite TE materials have been reported as ca. 1 at 800 K. Novel nano- engineering approaches and filling of the skutterudites crystal can further improve the transport properties and ultimately the ZT. Although classified among the promising TE materials, research on their large-scale production via bottom up synthetic routes is rather limited. In this work, large quantity of cobalt antimonide (CoSb3) based skutterudites nanopowder (NP) was fabricated through a room temperature co-precipitation precursor method. Dried precipitates were process by thermo-chemical treatment steps including calcination (in air) and reduction (in hydrogen). CoSb3 NPs were then mixed with silver (Ag) nanoparticles at different weight percentages (1%, 5% and 10% by wt) to form nanocomposites. Skutterudite NP was then consolidated by Spark Plasma Sintering (SPS) technique to produce highly dense compacts while maintaining the nanostructure. Temperature dependent TE characteristics of SPS’d CoSb3 and Ag containing nanocomposite samples were evaluated for transport properties, including thermal conductivity, electrical conductivity and Seebeck coefficient over the temperature range of 300 - 900 K. Physicochemical, structural and microstructural evaluation results are presented in detail.

Depending on their application temperature thermoelectric (TE) materials are classified in three main categories; as low (up to 250°C), intermediate (up to 550°C) and high (above 600°C) temperature. Currently, Skutterudites (CoSb3) based materials have shown promising results in the intermediate temperature range (300-500°C). This family of material is highly suitable for automotive, marine transportation and industrial power generation applications to recover the waste heat from the exhaust and generate electricity. Conventional TE modules need p- and n-type semiconductor materials and for the skutterudite family, iron (Fe) has proven to be among the best candidates for the substitution of cobalt sites. Additionally, rare earths are introduced as rattlers in the crystal cages of the skutterudite to decrease the thermal conductivity, thus improving the figure of merit ZT of the TE material. For practical application for device fabrication, stability of these materials is of great importance. Compositional stability is being addressed as the material decomposes above certain temperature. Temperature dependent x-ray diffraction study was performed on Fe substituted, Yb-filled skutterudites, using Beam Line I711 at MAX LAB, to observe the crystal structure as a function of temperature. Diffraction patterns were collected from room temperature up to 500°C by utilizing Huber furnace. The results show success in filling process showing almost 80% reduction of the thermal conductivity from bulk. Additionally the thermal expansion coefficient value was within the average value for skutterudites which proves practical application of this powder for industrial applications.